QuEChERS solid-phase extraction device, preparation method of QuEChERS solid-phase extraction device and solid-phase extraction method

An extraction device and extraction technology are applied in separation methods, chemical instruments and methods, solid adsorbent liquid separation, etc., which can solve the problems of high pre-treatment labor cost, complicated operation process, difficult automatic operation and batch processing, etc., to achieve Improve the detection sensitivity and recovery rate, simplify the operation process, and avoid the effect of instrument contamination

Inactive Publication Date: 2019-10-11
SHENZHEN BIOCOMMA TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although QuEChERS is a very effective sample pretreatment technology, the operation process is very complicated, especially multiple discontinuous operation steps such as s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • QuEChERS solid-phase extraction device, preparation method of QuEChERS solid-phase extraction device and solid-phase extraction method
  • QuEChERS solid-phase extraction device, preparation method of QuEChERS solid-phase extraction device and solid-phase extraction method
  • QuEChERS solid-phase extraction device, preparation method of QuEChERS solid-phase extraction device and solid-phase extraction method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0061] Example 1:

[0062] New and improved QuEChERS solid phase extraction column containing graphitized carbon solid adsorbent (referred to as SQ1 column)

[0063] (1) SQ1 column preparation (press image 3 Structural assembly shown):

[0064] The solid adsorbent (150mg PSA and 15mg graphitized carbon mixture) and 1.5g water absorbing material (diatomite) filler are packed into a 3mL column tube. A piece of porous polypropylene is provided in the upper, middle and lower positions of the column cavity. The sieve plate separates the column tube into two upper and lower packing chambers. The lower chamber of the column tube is made of adsorbent material, and the upper chamber is made of water-absorbing material. The SQ1 column is obtained according to a specific ratio.

[0065] (2) The application of SQ1 column in the detection of 12 kinds of carbamates such as oxamethoxin in honey:

[0066] It is used for sample pre-treatment and purification for the detection of 12 carbamates such as ...

Example Embodiment

[0075] Example 2:

[0076] New and improved QuEChERS solid phase extraction column containing PSA porous modified adsorbent (denoted as SQ2 column)

[0077] (1) Preparation of PSA porous modified adsorbent:

[0078] Thermoplastic polymer resin: UHMWPE, molecular weight is about 3.5 million, particle size is 80-120 mesh.

[0079] Solid adsorbent: PSA, particle size is 60μm, pore size is

[0080] 1) Add 70% UHMWPE and 30% PSA into the container in sequence, and mix them evenly to obtain spare raw materials;

[0081] 2) Adopt an aluminum mold with several holes with a diameter of 9.1mm and a height of 5.2mm. The spare raw materials are evenly added to the holes and compressed and shaken flat;

[0082] 3) After sintering at 165°C for 25 minutes and then cooling to obtain PSA porous modified adsorbent material.

[0083] (2) Preparation of SQ2 column (according to Figure 4 Structural assembly shown):

[0084] Load the modified PSA solid adsorbent material and 1.5 g of water-absorbing material (...

Example Embodiment

[0094] Example 3:

[0095] New and improved QuEChERS solid phase extraction column containing PEP porous modified adsorbent (denoted as SQ3 column)

[0096] (1) Preparation of PEP porous modified adsorbent:

[0097] Thermoplastic polymer resin: UHMWPE, molecular weight is about 2.8 million, particle size is 70-100 mesh.

[0098] Solid adsorbent: PEP, the particle size is 70μm, the pore size is

[0099] 1) Add 75% of UHMWPE and 25% of PEP to the container in sequence, and mix well to obtain spare raw materials;

[0100] 2) Adopt an aluminum mold with several holes with a diameter of 9.1mm and a height of 5.2mm. The spare raw materials are evenly added to the holes and compressed and shaken flat;

[0101] 3) Sintering at 180°C for 25 minutes and then cooling to obtain PEP porous modified adsorbent material.

[0102] (2) Preparation of Q3 column (press Figure 4 Structural assembly shown):

[0103] The modified PEP adsorbent material and 1.0g of water-absorbing material (diatomite accounted f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a QuEChERS solid-phase extraction device, a preparation method of the QuEChERS solid-phase extraction device and a solid-phase extraction method. The QuEChERS solid-phase extraction device comprises a carrier device, a water absorption material and an adsorbent material, wherein the water absorption material and the adsorbent material are successively placed in the carrierdevice up and down, the water absorption material is selected from one or more of kieselguhr and super absorbent resin, and the adsorbent material is selected from one or more of silica gel substrates, non-silica gel substrates, polymer substrates and porous modified adsorbents. According to the QuEChERS solid-phase extraction device, the operation process is simplified, high throughput and automation of sample pretreatment are more easily achieved, endogenous and exogenous substrate interfering substances in a complex sample can also be effectively removed, and instrument pollution is effectively avoided; the detection sensitivity and recovery rate of a target are greatly improved, and the device can be widely applied to the field of pretreatment of samples of biology, medicine, environments, food, commodity inspection, forensic science and the like.

Description

technical field [0001] The invention relates to the field of sample pretreatment, in particular to a QuEChERS solid-phase extraction device, a preparation method thereof and a solid-phase extraction method. Background technique [0002] QuEChERS is the abbreviation of Quick (fast), Easy (simple), Cheap (cheap), Effective (effective), Rugged (reliable / durable) and Safe (safe). A sample pretreatment method formed by the combination of dispersive solid phase extraction and purification phases. [0003] As early as 2003, it was first published by Michelangelo Anastassiades, Steven Lehotay, etc. After that, Steven Lehotay wrote the US Department of Agriculture General Standard AOAC. The national standard GB 23200.113 has been passed. QuEChERS technology has become a global standard sample pretreatment method for the detection of pesticide residues in fruits and vegetables because of its advantages of convenience, high efficiency, less solvent usage, less pollution, and low pric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D15/10B01D15/42
CPCB01D15/10B01D15/426
Inventor 梁慧明陈高明张娟卢鹏飞余飞胡玉梅
Owner SHENZHEN BIOCOMMA TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap