Fabricated element concrete special-purpose kitchen and bath waterproof agent

A prefabricated component and concrete technology, which is applied in the field of prefabricated concrete kitchen and bathroom waterproofing agent, can solve the problems of poor waterproof effect, single function, lack of water reduction, crack prevention, high impermeability and high pressure strength, etc., to achieve Strong waterproof effect, reduce temperature difference cracks, increase workability and compactness

Inactive Publication Date: 2019-11-01
湖南加美乐素新材料股份有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Traditionally used for prefabricated concrete special kitchen and bathroom waterproofing agent, mostly organic and inorganic, its waterproof effect is poor, and its function is single, and it does not have the functions of water reduction, crack prevention, high impermeability and high pressure resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A special kitchen and bathroom waterproofing agent for prefabricated component concrete. The raw materials in parts by weight include: 10 parts of modified silicon emulsion, 1 part of zirconium compound, 3 parts of organic silicon surfactant, 10 parts of water-soluble polyurethane resin emulsion, air-entrained 0.1 part of water reducing agent, 2 parts of water reducing agent, and 1 part of coagulation regulator.

[0030] The preparation method of the special kitchen and bathroom waterproofing agent for prefabricated component concrete, the specific steps are as follows:

[0031] (1) take each raw material according to parts by weight;

[0032] (2) Add the weighed organic silicon surfactant and water-soluble polyurethane resin emulsion into the reaction kettle, open the stirring equipment in the reaction kettle, and carry out preliminary stirring and emulsification to it, and the stirring and mixing time is 30-60min;

[0033] (3) Add the weighed modified silicon emulsio...

Embodiment 2

[0036] A special kitchen and bathroom waterproofing agent for prefabricated component concrete. The raw materials in parts by weight include: 11 parts of modified silicon emulsion, 1.25 parts of zirconium compound, 3.5 parts of organic silicon surfactant, 11 parts of water-soluble polyurethane resin emulsion, air-entrained 0.2 parts of water reducing agent, 2.5 parts of water reducing agent, and 1.5 parts of coagulation regulator.

[0037] The preparation method of the special kitchen and bathroom waterproofing agent for prefabricated component concrete, the specific steps are as follows:

[0038] (1) take each raw material according to parts by weight;

[0039] (2) Add the weighed organic silicon surfactant and water-soluble polyurethane resin emulsion into the reaction kettle, open the stirring equipment in the reaction kettle, and carry out preliminary stirring and emulsification to it, and the stirring and mixing time is 30-60min;

[0040] (3) Add the weighed modified sil...

Embodiment 3

[0043] A special kitchen and bathroom waterproofing agent for prefabricated component concrete. The raw materials in parts by weight include: 12 parts of modified silicon emulsion, 1.5 parts of zirconium compound, 4 parts of organic silicon surfactant, 12 parts of water-soluble polyurethane resin emulsion, air-entrained 0.3 parts of water reducing agent, 3 parts of water reducing agent, and 2 parts of coagulation regulator.

[0044] The preparation method of the special kitchen and bathroom waterproofing agent for prefabricated component concrete, the specific steps are as follows:

[0045] (1) take each raw material according to parts by weight;

[0046] (2) Add the weighed organic silicon surfactant and water-soluble polyurethane resin emulsion into the reaction kettle, open the stirring equipment in the reaction kettle, and carry out preliminary stirring and emulsification to it, and the stirring and mixing time is 30-60min;

[0047] (3) Add the weighed modified silicon em...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a fabricated element concrete special-purpose kitchen and bath waterproof agent. The fabricated element concrete special-purpose kitchen and bath waterproof agent comprises, byweight, 10 to 15 parts of modified silicon emulsion, 1 to 2 parts of a zirconium compound, 3 to 6 parts of a organic silicone surfactant, 10 to 15 parts of water-soluble polyurethane resin emulsion,0.1 to 0.4 part of an air entraining agent, 2 to 5 parts of a water reducer, and 1 to 4 parts of a thickening time control agent. According to a preparation method of the fabricated element concrete special-purpose kitchen and bath waterproof agent, organic compounds including the organic silicone surfactant and the water-soluble polyurethane resin emulsion are adopted, and are combined with the air entraining agent, the zirconium compound, the water reducer, and the thickening time control agent to prepare the composite waterproof agent. Compared with convention waterproof agent, the advantages of the composite waterproof agent are that: construction is simple; the composite waterproof agent is safe, and is friendly to the environment, possesses extremely excellent water resistance, is capable of reducing concrete water glue ratio, improving concrete workability and compactness, reducing concrete shrinkage rate further, filling concrete internal pores, and achieving impervious grade increasing, pressure resistance, and high strength.

Description

technical field [0001] The invention relates to the technical field of waterproofing agent preparation, in particular to a special kitchen and bathroom waterproofing agent for prefabricated component concrete. Background technique [0002] Concrete, referred to as "concrete" for short: refers to the collective name of engineering composite materials in which aggregates are cemented into a whole by cementitious materials. Generally speaking, the term concrete refers to the cement concrete obtained by using cement as the cementitious material, sand and stone as the aggregate; and water, which may contain admixtures and admixtures, mixed in a certain proportion, and stirred. Concrete, which is widely used in civil engineering, is one of the most important contemporary civil engineering materials. It is composed of cementitious materials, granular aggregates, also known as aggregates, water, and admixtures and admixtures added when necessary, prepared in a certain proportion, u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/42C04B103/65
CPCC04B40/0039C04B2103/65C04B24/42C04B24/282C04B2103/304C04B2103/302C04B2103/44C04B22/08
Inventor 王伟龙威
Owner 湖南加美乐素新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap