A lithium hexafluorozirconate and carbon co-coated lithium iron phosphate composite material, its preparation method and application

A carbon co-coating technology of lithium iron phosphate and lithium hexafluorozirconate, applied in structural parts, electrical components, battery electrodes, etc. The effect of good cycle performance and low temperature performance, high pole piece compaction density, and high first-turn capacity

Active Publication Date: 2022-05-03
BTR (TIANJIN) NANO MATERIAL MFG CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this coating method only solves the problem of poor electrochemical performance of the material itself, but does not effectively solve the problems of low first efficiency, poor low temperature performance, and low first cycle capacity in the charging and discharging process of the battery.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A lithium hexafluorozirconate and carbon co-coated lithium iron phosphate composite material, its preparation method and application
  • A lithium hexafluorozirconate and carbon co-coated lithium iron phosphate composite material, its preparation method and application
  • A lithium hexafluorozirconate and carbon co-coated lithium iron phosphate composite material, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] Lithium carbonate, anhydrous ferric phosphate, glucose and lithium hexafluorozirconate are put into the grinding tank in sequence according to the molar ratio Li:Fe:C:Zr=1.05:1:1:0.001, and deionized water is added to the slurry The solid content of the material is 25%, and the precursor slurry is fully ground to a particle size of 100nm to realize activation.

[0075]The resulting slurry was spray-dried in a spray dryer, and the inlet temperature and outlet temperature were set to 310°C and 120°C respectively; 4 fluid nozzles were used for spraying, flow meters were installed on the two inlet pipes, and flow meters were installed on the two inlet pipes. A peristaltic pump is installed on the pipe and fed from the same bucket of slurry. The intake volume of one of the intake pipes is 30NL / min, and the feed volume of the corresponding feed pipe is 5ml / min, which is used to prepare small particle size particles; the intake volume of the other intake pipe is 90NL / min; The...

Embodiment 2

[0080] Lithium hydroxide, ferric phosphate dihydrate, polyvinyl alcohol and lithium hexafluorozirconate are put into the grinding tank in sequence according to the molar ratio of Li:Fe:C:Zr=1.01:1:1.4:0.1, and pure water is added to The solid content of the slurry is 15%, and the precursor slurry is fully ground to a particle size of 300nm to realize activation.

[0081] The resulting slurry was spray-dried in a spray dryer, and the inlet temperature and outlet temperature were set to 280°C and 120°C respectively; 8 fluid nozzles were used for spraying, flow meters were installed on 4 inlet pipes, and flow meters were installed on 4 inlet pipes. A peristaltic pump is installed on the pipe and fed from the same bucket of slurry. The intake volume of one of the intake pipes is 10NL / min, and the feed volume of the corresponding feed pipe is 5ml / min, which is used to prepare small particle size particles; the intake volume of the other three intake pipes is 60NL / min. min; the fee...

Embodiment 3

[0084] Lithium acetate, ammonium ferric phosphate dihydrate, phytic acid and lithium hexafluorozirconate are put into the grinding tank in sequence according to the molar ratio of Li:Fe:C:Zr=1.03:1:1.4:0.005, and pure water is added to The solid content of the slurry is 40%, and the precursor slurry is fully ground to a particle size of 400 nm.

[0085] The resulting slurry was spray-dried in a spray dryer, and the inlet temperature and outlet temperature were set to 300°C and 120°C respectively; 6 fluid nozzles were used for spraying, flow meters were installed on 3 inlet pipes, and flowmeters were installed on 3 inlet pipes. A peristaltic pump is installed on the pipe and fed from the same bucket of slurry. The intake volume of one of the intake pipes is 10NL / min, and the feed volume of the corresponding feed pipe is 2ml / min, which is used to prepare small particle size particles; the intake volume of the other two intake pipes is 70NL / min. min; the feeding volume of the co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a lithium hexafluorozirconate and carbon co-coated lithium iron phosphate composite material, its preparation method and application. The composite material includes: a core of lithium iron phosphate, and a cladding layer coated on the surface of the core, the cladding layer is composed of lithium hexafluorozirconate and pyrolytic carbon, and the composite material includes at least two Composite particles in different particle size ranges. The method of the present invention includes: 1) slurrying and activating lithium source, phosphorus iron source, carbon source and lithium hexafluorozirconate; 2) utilizing a spray dryer to produce spheres with at least two particle size ranges; (3) sintering , to obtain a composite material of lithium hexafluorozirconate and carbon co-coated lithium iron phosphate. The method of the invention can significantly improve the compacted density of the material, and the full battery made of the composite material as the positive electrode active material has excellent first cycle capacity, cycle performance and low temperature performance.

Description

technical field [0001] The invention relates to the field of positive electrode materials for lithium ion batteries, and relates to a lithium hexafluorozirconate and carbon co-coated lithium iron phosphate composite material, its preparation method and application, and in particular to a hexafluorozirconate with high compaction density and good electrochemical performance. Lithium fluorozirconate and carbon co-coated lithium iron phosphate composite material, its preparation method and use as lithium ion cathode material. Background technique [0002] As a commercialized positive electrode material, lithium iron phosphate material has always had the problems of low electronic conductivity and low ion migration rate. The lithium iron phosphate power battery has always needed further optimization due to its low actual energy density. [0003] At present, carbon coating has become the main means to improve the electrochemical performance of lithium iron phosphate cathode mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/58H01M4/62H01M4/136H01M10/0525
CPCH01M4/366H01M4/5825H01M4/62H01M4/136H01M10/0525Y02E60/10
Inventor 杨帆王张健杨顺毅吴小珍杨才德
Owner BTR (TIANJIN) NANO MATERIAL MFG CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com