Preparation method of fluorine functional monomer modified soap-free emulsion polymer for polymer cement

A technology of soap-free emulsion and functional monomer, applied in the field of preparation of soap-free emulsion polymer modified with fluorine functional monomer for polymer cement, to achieve reliable reaction, mild reaction conditions, good heat transfer and temperature control

Inactive Publication Date: 2020-01-07
HUBEI UNIV OF TECH
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the coating products in the above patents are all better in single performance such as waterproof, binding ability, and anti-aging performance, and there is still room for further improvement in comprehensive performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of fluorine functional monomer modified soap-free emulsion polymer for polymer cement

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0047] A preparation method of a soap-free emulsion polymer modified with a fluorine functional monomer for polymer cement, which is mainly prepared from the following components:

[0048] 4-(ethyleneoxy)-1-butanol: 14 parts

[0049] Composition with a mass ratio of allyl alcohol to methacryl alcohol of 9:4: 13 parts

[0050] Sodium methacrylate: 0.7 parts

[0051] The composition of azobisisobutyronitrile and tert-butyl peroxy tert-butyl peroxyvalerate in a mass ratio of 5:3: 0.4 parts

[0052] Dicyclohexyl peroxydicarbonate: 3.4 parts

[0053] Butyl acrylate: 8 parts

[0054] Methacryloyloxyethyl hexahydrophthalate monoester: 227 parts

[0055] The composition of tris(2-hydroxyethyl)isocyanurate triacrylate and ethylene glycol dimethacrylate with a mass ratio of 1:1: 5.9 parts

[0056] Perfluorooctyl ethyl acrylate: 8 parts

[0057] Sodium methoxide: 6.6 parts

[0058] Sodium bicarbonate: 13 parts

[0059] The total mass parts is 1000, and the remainder is water.

...

example 2

[0065] A preparation method of a soap-free emulsion polymer modified with a fluorine functional monomer for polymer cement, which is mainly prepared from the following components:

[0066] Prenol: 10 parts

[0067] Composition with a mass ratio of allyl alcohol to methacryl alcohol of 9:4: 16 parts

[0068] Sodium methacrylate: 0.6 parts

[0069] Composition with azobisisobutyronitrile and tert-butyl peroxy tert-butyl peroxyvalerate at a mass ratio of 5:3: 0.6 parts

[0070] Composition with a mass ratio of diisopropyl peroxydicarbonate to dicyclohexyl peroxydicarbonate of 3:1: 4.2 parts

[0071] Composition with a mass ratio of hydroxypropyl acrylate to diethyl maleate of 2:3: 10 parts

[0072] Composition with a mass ratio of 2-propylheptyl acrylate to methacryloyloxyethyl phthalate monoester at a mass ratio of 5:2: 226 parts

[0073] The composition of tris(2-hydroxyethyl)isocyanurate triacrylate and ethylene glycol dimethacrylate with a mass ratio of 1:1: 3.8 parts

...

example 3

[0083] A preparation method of a soap-free emulsion polymer modified with a fluorine functional monomer for polymer cement, which is mainly prepared from the following components:

[0084] 4-(ethyleneoxy)-1-butanol: 12 parts

[0085] Propyl alcohol: 17 parts

[0086] Sodium methacrylate: 0.8 parts

[0087] Dibenzoyl peroxide: 0.7 parts

[0088] Composition with a mass ratio of diisopropyl peroxydicarbonate to dicyclohexyl peroxydicarbonate of 3:1: 3.5 parts

[0089] Butyl acrylate: 12 parts

[0090] Composition of 2-propylheptyl acrylate and methacryloyloxyethyl phthalic acid monoester with a mass ratio of 5:2: 230 parts

[0091] Ethylene glycol dimethacrylate: 4.5 parts

[0092] Perfluorooctyl ethyl acrylate: 6 parts

[0093] Sodium methoxide: 3.5 parts

[0094] Potassium carbonate: 10 parts

[0095] The total mass parts is 1000, and the remainder is water.

[0096] 1) Mix 200 parts of water, 12 parts of 4-(ethyleneoxy)-1-butanol, 0.8 parts of sodium methacrylate, 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a fluorine functional monomer modified soap-free emulsion polymer for polymer cement. Hydroxyl monomers and ester monomers are used as raw materials; asoap-free emulsion polymerization method is adopted, meanwhile, a pH regulator is used for controlling the pH value of the reaction environment to be 8 to 8.5; the soap-free hydroxyl hydrophilic monomers, soap-free ester-based hydrophobic monomers and an initiator a are subjected to reaction to synthesize a soap-free polymer; the soap-free polymer reacts with other raw materials to synthesize a polymer waterproof coating. The preparation method has the advantages of high polymerization speed, fewer reaction steps, small environmental pollution and mild reaction conditions, and the synthesizedproduct has quite good adhesion force, tensile elasticity and durability with a basal plane due to the proper pH value in the polymerization process.

Description

technical field [0001] The invention belongs to the technical field of building materials and relates to the field of waterproof materials, in particular to a preparation method of a soap-free emulsion polymer modified with a fluorine functional monomer for polymer cement. Background technique [0002] With the continuous improvement of social living conditions, people pay more and more attention to their quality of life, and their requirements for waterproof conditions are constantly increasing. In recent years, with the development of social science and technology, new waterproof products and their engineering application technologies have developed rapidly, and are developing from multi-layer to single-layer, from hot construction to cold construction. Faced with the continuous progress and renewal of science and technology, it is particularly important to master the construction preparation and quality issues of waterproofing projects, which is of great significance to t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F265/06C08F220/30C08F220/24C08F220/18C08F263/04C08F2/22C08F4/04C08F4/38C08F2/38C04B24/26C04B103/65
CPCC04B24/2688C04B2103/65C08F2/22C08F2/38C08F4/04C08F4/38C08F263/04C08F265/06C08F220/24
Inventor 柯凯刘飞宏姚恒
Owner HUBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap