Modified nano high-strength polyethylene films

A technology of high-strength polyethylene and high-density polyethylene, applied in the field of modified nanometer high-strength polyethylene film, can solve the problems of insufficient strength and tearing, and achieve the effect of good strength enhancement and tight connection

Inactive Publication Date: 2020-01-07
HAN YIN SUZHOU ECO MATERIALS TECH CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a modified nano-high-strength polyethylene film to solve the problem that the strength of the existing modified nano-high-strength polyethylene film proposed in the above-mentioned background technology may be torn due to insufficient strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified nano high-strength polyethylene films
  • Modified nano high-strength polyethylene films

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only a part of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without creative work shall fall within the protection scope of the present invention.

[0025] See Figure 1-2 , The present invention provides a technical solution: a modified nano high-strength polyethylene film prepared by a combination of the following process modules. The process modules include an additive module 1, a slurry filtration module 2, a batching module 3, and a mixing module 4 , Kneading module 5, molding module 6, cooling module 7 and packaging and warehousing module 8. The output end of additive module 1 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
crystallization temperatureaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses modified nano high-strength polyethylene films which are prepared by combining the following process modules, wherein the process modules comprise an additive module, a pulp grinding and filtering module, a batching module, a mixing module, a kneading module, a molding module, a cooling module and a packaging and warehousing module; the output end of the additive module isthe pulp grinding and filtering module; the pulp grinding and filtering module can receive materials from the interior of the additive module; the strength adhesive module is added in the production process of the polyethylene films; therefore, under the action of the strength adhesive module, the high-density polyethylene module and the low-density polyethylene module can be better mixed and interacted; the inner core operation is carried out after the mixing process, so that the produced polyethylene films can be connected with each other more tightly, the phenomenon of gaps is avoided, andthe strength can be better enhanced by using the strength adhesive module.

Description

Technical field [0001] The invention belongs to the technical field related to polyethylene film production, and specifically relates to a modified nano high-strength polyethylene film. Background technique [0002] Polyethylene is a thermoplastic resin made by polymerization of ethylene. In industry, it also includes copolymers of ethylene and a small amount of α-olefin. Polyethylene is odorless, non-toxic, feels like wax, has excellent low temperature resistance (minimum use temperature can reach -100 to -70°C), has good chemical stability, and can withstand most acids and alkalis (not resistant to oxidizing properties) Of acid). It is insoluble in general solvents at room temperature, has low water absorption and excellent electrical insulation. The performance of polyethylene depends on its polymerization method. High-density polyethylene is produced by Ziegler-Natta polymerization under medium pressure organic compound catalysis. Under this condition, the polymerized pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08K5/134C08K5/526C08J5/18B29D7/01
CPCC08J5/18B29D7/01C08J2323/06C08J2423/08C08K5/1345C08K5/526
Inventor 胡建明高宗旺
Owner HAN YIN SUZHOU ECO MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products