Aramid fiber coating liquid, preparation method thereof, diaphragm based on aramid fiber coating liquid and application
A coating liquid, aramid fiber technology, applied in the direction of electrical components, circuits, battery pack components, etc., can solve the problem of time-consuming and power consumption
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0035] Example 1
[0036] A preparation method of aramid coating liquid includes the following steps:
[0037] 1) Mix ceramic particles (alumina) and dimethylacetamide (DMAc) and stir for 30 minutes. Sand mill with a rod-pin nano sand mill for 20 minutes to obtain the first mixture, wherein the speed of the sand mill is 900r / min, and the ratio of ceramic particles to dimethylacetamide is 15:70 in parts by mass; In the test, the particle size of the ceramic particles in the first mixture is D50: 0.3 μm and D90: 1 μm.
[0038] 2) Under a nitrogen atmosphere, stir the first mixture with m-phenylenediamine for 20 minutes, after stirring, the temperature is cooled to 0°C through a chilled water bath, and then isophthaloyl chloride is added and stirred for 20 minutes (the process temperature is 0°C ), remove the water bath, and then raise the temperature to 80°C at a rate of 6°C / min. Add calcium hydroxide and stir for 30min (the process temperature is 80°C) to obtain the second mixture. ...
Example Embodiment
[0040] Example 2
[0041] A preparation method of aramid coating liquid includes the following steps:
[0042] 1) Mix ceramic particles (silica) and dimethylacetamide (DMAc) and stir for 30 minutes. Sand mill with a rod-pin nano sand mill for 20 minutes to obtain the first mixture, wherein the speed of the sand mill is 900r / min, and the ratio of ceramic particles to dimethylacetamide is 17:75 in parts by mass; According to the test, the particle size of the ceramic particles in the first mixture is D50: 0.5 μm and D90: 1.2 μm.
[0043] 2) Under a nitrogen atmosphere, stir the first mixture and m-phenylenediamine for 20 minutes, after stirring, cool down to 2°C in a chilled water bath, add isophthaloyl chloride, and stir for 20 minutes (the process temperature is 2°C) ), remove the water bath, and then raise the temperature to 80°C at a rate of 7°C / min. Add calcium hydroxide and stir for 30min (the process temperature is 80°C) to obtain the second mixture, in which, in parts by mass...
Example Embodiment
[0045] Example 3
[0046] A preparation method of aramid coating liquid includes the following steps:
[0047] 1) Mix ceramic particles (barium titanate) and dimethylacetamide (DMAc) and stir for 30 minutes. Sand grind with a rod-pin nano sand mill for 20 minutes to obtain the first mixture, wherein the speed of the sand mill is 900r / min, and the ratio of ceramic particles to dimethylacetamide is 20:80 in parts by mass; According to the test, the particle size of the ceramic particles in the first mixture is D50: 0.6 μm and D90: 1.3 μm.
[0048] 2) Under a nitrogen atmosphere, stir the first mixture with m-phenylenediamine for 20 minutes, after stirring, the temperature is cooled to 5°C through a chilled water bath, and then isophthaloyl chloride is added and stirred for 20 minutes (the process temperature is 5°C) ), remove the water bath, and then raise the temperature to 80°C at a rate of 8°C / min. Add calcium hydroxide and stir for 30min (the process temperature is 80°C) to obtai...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap