Two-dimensional nano low-surface-treatment graphene anticorrosive primer and preparation method thereof

A low surface treatment, two-dimensional nanotechnology, applied in the field of anti-corrosion paint, can solve the problems of anti-corrosion effect and poor shielding, and achieve the effect of improving anti-corrosion performance

Inactive Publication Date: 2020-02-28
SUZHOU JIREN HIGH TECH MATERIAL CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the anti-corrosion paints on the market are generally made of epoxy system plus anti-rust pigments, which have problems such as anti-corrosion effect and poor shielding performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of graphene anticorrosion primer of two-dimensional nano low surface treatment, in mass percentage, this graphene anticorrosion primer is made of following raw materials:

[0033] Epoxy resin, 32wt%;

[0034] Xylene, 5wt%;

[0035] Isobutanol, 2wt%;

[0036] Polyamide wax, 0.3wt%;

[0037] Pigment and filler, 25wt%;

[0038] Zinc phosphate, 5wt%;

[0039] Silicone polymer, 0.1 wt%;

[0040] Two-dimensional nano-graphene, 16wt%;

[0041] Curing agent, 14.6wt%.

[0042] Further, in terms of mass percentage, the curing agent is made of the following raw materials:

[0043] Xylene, 20wt%;

[0044] Isobutanol, 16wt%;

[0045] Phenalkamine, 17wt%;

[0046] Propylene glycol monomethyl ether, 3wt%;

[0047] Epoxy resin, 6wt%;

[0048] Modified polyamide, 38 wt%.

[0049] Further, the curing agent is prepared through the following steps:

[0050] The first step: Put the designed amount of xylene, isobutanol, phenalk ammonia, propylene glycol monomethyl ether...

Embodiment 2

[0058] A kind of graphene anticorrosion primer of two-dimensional nano low surface treatment, in mass percentage, this graphene anticorrosion primer is made of following raw materials:

[0059] Epoxy resin, 38wt%;

[0060] Xylene, 8wt%;

[0061] Isobutanol, 1wt%;

[0062] Polyamide wax, 0.5wt%;

[0063] Pigments and fillers, 23wt%;

[0064] Zinc phosphate, 6wt%;

[0065] Silicone polymer, 0.4 wt%;

[0066] Two-dimensional nano-graphene, 11wt%;

[0067] Curing agent, 12.1 wt%.

[0068] Further, in terms of mass percentage, the curing agent is made of the following raw materials:

[0069] Xylene, 15wt%;

[0070] Isobutanol, 20wt%;

[0071] Phenalkamine, 16.5wt%;

[0072] Propylene glycol monomethyl ether, 4wt%;

[0073] Epoxy resin, 8wt%;

[0074] Modified polyamide, 36.5 wt%.

[0075] Further, the curing agent is prepared through the following steps:

[0076] The first step: Put the designed amount of xylene, isobutanol, phenalk ammonia, propylene glycol monomethy...

Embodiment 3

[0084] A kind of graphene anticorrosion primer of two-dimensional nano low surface treatment, in mass percentage, this graphene anticorrosion primer is made of following raw materials:

[0085] Epoxy resin, 30wt%;

[0086] Xylene, 6wt%;

[0087] Isobutanol, 1wt%;

[0088] Polyamide wax, 0.5wt%;

[0089] Pigments and fillers, 22.3wt%;

[0090] Zinc phosphate, 8wt%;

[0091] Silicone polymer, 0.5 wt%;

[0092] Two-dimensional nano-graphene, 16.7wt%;

[0093] Curing agent, 15wt%.

[0094] Further, in terms of mass percentage, the curing agent is made of the following raw materials:

[0095] Xylene, 10wt%;

[0096] Isobutanol, 25wt%;

[0097] Phenalkamine, 20wt%;

[0098] Propylene glycol monomethyl ether, 6wt%;

[0099] Epoxy resin, 5wt%;

[0100] Modified polyamide, 34 wt%.

[0101] Further, the curing agent is prepared through the following steps:

[0102] The first step: Put the designed amount of xylene, isobutanol, phenalk ammonia, propylene glycol monomethyl e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a two-dimensional nano low-surface-treatment graphene anticorrosive primer and a preparation method thereof. The two-dimensional nano low-surface-treatment graphene anticorrosive primer is prepared from, by mass, 30-40wt% of epoxy resin, 5-8wt% of xylene; 1-3wt% of isobutanol; 0.3-1% of polyamide wax; 22.3-27.5wt% of a pigment and filler; 5-8wt% of zinc phosphate; 0.1-0.5wt% of an organosilicon polymer; 10-30wt% of two-dimensional nano graphene; and 12-15wt% of a curing agent. Different from a preparation formula and a preparation method adopting an epoxy system and ananti-rust pigment in the conventional technology, the graphene anticorrosion primer prepared by the invention possesses the anti-corrosion performance improved by 1-2 times compared with that of a conventional anti-corrosion paint.

Description

technical field [0001] The invention relates to the field of anti-corrosion paint, in particular to a two-dimensional nanometer low surface treatment graphene anti-corrosion primer and a preparation method thereof. Background technique [0002] At present, the anti-corrosion paints on the market are generally made of epoxy system plus anti-rust pigments, which have problems such as anti-corrosion effect and poor shielding performance. In fact, it is necessary to develop a two-dimensional nanometer low surface treatment graphene anticorrosion primer and a preparation method thereof to solve the above problems. Contents of the invention [0003] Aiming at the deficiencies in the prior art, the object of the present invention is to provide a two-dimensional nanometer low-surface-treated graphene anti-corrosion primer and a preparation method thereof, which has excellent anti-corrosion properties. [0004] In order to achieve the above-mentioned purpose and other advantages a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D5/08C09D7/61C09D7/65C08G59/62C08G59/46
CPCC08G59/46C08G59/62C08K2003/328C08K2201/011C08L2205/03C09D5/082C09D163/00C09D7/61C09D7/65C08L77/00C08L83/04C08K13/02C08K3/32C08K3/042
Inventor 李连才徐泽孝
Owner SUZHOU JIREN HIGH TECH MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products