A kind of bifunctional chemical warfare agent degradation material and its preparation method

A chemical warfare agent and degradable material technology, which is applied in the field of dual-functional chemical warfare agent degradation materials and its preparation, can solve problems such as unpredictable chemical warfare agent types, and achieve the effect of great application value

Inactive Publication Date: 2021-07-30
BEIJING UNIV OF CHEM TECH +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Since the type of chemical warfare agent used cannot be predicted, it is a technical problem to be solved urgently by those skilled in the art to develop a kind of degradable material capable of degrading various chemical warfare agents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bifunctional chemical warfare agent degradation material and its preparation method
  • A kind of bifunctional chemical warfare agent degradation material and its preparation method
  • A kind of bifunctional chemical warfare agent degradation material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031](1) Dissolve 12g of aluminum chloride hexahydrate in 200mL of deionized water to obtain a 0.25mol / L aluminum chloride hexahydrate solution after dissolving;

[0032] (2) stirring the solution obtained in step (1) at 80°C;

[0033] (3) 4.5g sodium hydroxide is dissolved in the deionized water of 450mL, obtains the sodium hydroxide solution of 0.25mol / L;

[0034] (4) Slowly add the sodium hydroxide solution obtained in step (3) dropwise to the aluminum chloride hexahydrate solution obtained in step (1) to obtain Al 13 7+ solution;

[0035] (5) the Al obtained in step (4) 13 7+ The solution uses deionized water as a solvent, and is configured to obtain Al with a concentration of 6mmol / L 13 7+ solution, take 20mL of Al after configuration 13 7+ solution;

[0036] (6) H 5 PV 2 Mo 10 o 40 Dissolve in deionized water and configure to obtain H with a concentration of 6mmol / L 5 PV 2 Mo 10 o 40 solution, take 20mL of prepared H 5 PV 2 Mo 10 o 40 solution;

[...

Embodiment 2

[0040] (1) Dissolve 12g of aluminum chloride hexahydrate in a mixed solution of 200mL ethanol and tetrahydrofuran to obtain a 0.25mol / L aluminum chloride hexahydrate solution after dissolving;

[0041] (2) stirring the solution obtained in step (1) at 80°C;

[0042] (3) 4.5g sodium hydroxide is dissolved in the deionized water of 450mL, obtains the sodium hydroxide solution of 0.25mol / L;

[0043] (4) Slowly add the sodium hydroxide solution obtained in step (3) dropwise to the aluminum chloride hexahydrate solution obtained in step (1) to obtain Al 13 7+ solution;

[0044] (5) the Al obtained in step (4) 13 7+ The solution uses a mixed solution of ethanol and tetrahydrofuran as a solvent, and is configured to obtain Al with a concentration of 6mmol / L. 13 7+ solution, take 20mL of Al after configuration 13 7+ solution;

[0045] (6) H 3 PMo 12 o 40 Dissolve in a mixed solution of ethanol and tetrahydrofuran, and configure to obtain H with a concentration of 6mmol / L ...

Embodiment 3

[0049] (1) Dissolve 12g of aluminum chloride hexahydrate in 200mL of N,N-dimethylformamide, and obtain a 0.25mol / L aluminum chloride hexahydrate solution after dissolving;

[0050] (2) stirring the solution obtained in step (1) at 80°C;

[0051] (3) 4.5g sodium hydroxide is dissolved in the deionized water of 450mL, obtains the sodium hydroxide solution of 0.25mol / L;

[0052] (4) Slowly add the sodium hydroxide solution obtained in step (3) dropwise to the aluminum chloride hexahydrate solution obtained in step (1) to obtain Al 13 7+ solution;

[0053] (5) the Al obtained in step (4) 13 7+ The solution uses N,N-dimethylformamide as solvent, and configures Al with a concentration of 6mmol / L 13 7+ solution, take 20mL of Al after configuration 13 7+ solution;

[0054] (6) H 3 PW 12 o 40 Dissolved with N,N-dimethylformamide, and configured to obtain H with a concentration of 6mmol / L 3 PW 12 o 40 solution, take 20mL of prepared H 3 PW 12 o 40 solution;

[0055] (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bifunctional chemical warfare agent degradation material with a biomimetic enzyme structure and a preparation method thereof. The polyacid anions are obtained by reacting. The present invention mixes polyaluminate cationic cluster solution of equal volume and concentration with polyoxometalate solution, leaves the mixed solution for three days, filters and dries the product, and obtains the degraded material. The degradation material of the present invention can synergistically play the role of polyaluminate cation clusters and polyacids, realize the degradation of mustard gas and soman through two mechanisms of hydrolysis and oxidation, and can degrade mustard gas and soman into non-toxic products without Cause secondary harm; the degradable material of the present invention can still maintain good chemical warfare agent degradation performance after being recycled for four times.

Description

technical field [0001] The invention relates to the technical field of functional materials, in particular to a dual-functional chemical warfare agent degradation material capable of simultaneously degrading mustard gas and nerve chemical agents and a preparation method thereof. Background technique [0002] From the First World War to the occasional chemical weapons attacks today, chemical warfare agents have been developed and applied due to their strong toxicity and lethality. Although under the impetus of the Chemical Weapons Convention, countries have made great progress in the destruction of chemical weapons, and a large number of stockpiles or chemical weapons left over from history have been destroyed. However, compared with other weapons, chemical weapons have lower production costs and sustained lethality, making them an important choice for economically backward countries and terrorist forces when fighting wars or maintaining their own security. Therefore, it is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A62D3/35
CPCA62D3/35A62D2101/28
Inventor 周云山高奇张立娟钟玉绪王永安
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com