Preparation method of lyocell fiber antibacterial blended fabric

A technology of blended fabrics and antibacterial fabrics, applied in chemical instruments and methods, lamination devices, lamination auxiliary operations, etc., can solve the problems of poor elasticity, poor thermal insulation, poor elasticity and thermal insulation, etc. Simple preparation process and good antibacterial effect of lyocell fiber

Inactive Publication Date: 2020-04-17
JIANGYIN XIANGFEI APPAREL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the elasticity and heat retention of cotton fiber blended yarns currently on the market are not good. Therefore, the fabric after weaving has the disadvantages of poor heat retention and poor elasticity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A preparation method of lyocell fiber antibacterial blended fabric, comprising the following steps:

[0017] a surface layer manufacturing: the surface layer is made of lyocell fiber antibacterial fabric, and the lyocell fiber antibacterial fabric is formed by interweaving warp and weft threads, and the warp is a blended yarn of lyocell fiber and cotton fiber, The weft thread is a blended yarn of wool fiber and cotton fiber;

[0018] b middle layer manufacturing: wool fiber and cotton fiber are first blended in the first fabric layer and the third fabric layer, and then blended with lyocell fiber to be woven into cloth, and the second fabric layer is manufactured by spinning cotton fiber Forming, the first fabric layer, the second fabric layer and the third fabric layer are bonded together by dispensing glue or stitching;

[0019] c Inner layer manufacturing: first mix lyocell fiber, wool fiber and cotton fiber evenly, and then go through cleaning-carding-drawing-rovin...

Embodiment 2

[0023] A preparation method of lyocell fiber antibacterial blended fabric, comprising the following steps:

[0024] a surface layer manufacturing: the surface layer is made of lyocell fiber antibacterial fabric, and the lyocell fiber antibacterial fabric is formed by interweaving warp and weft threads, and the warp is a blended yarn of lyocell fiber and cotton fiber, The weft thread is a blended yarn of wool fiber and cotton fiber;

[0025] b middle layer manufacturing: wool fiber and cotton fiber are first blended in the first fabric layer and the third fabric layer, and then blended with lyocell fiber to be woven into cloth, and the second fabric layer is manufactured by spinning cotton fiber Forming, the first fabric layer, the second fabric layer and the third fabric layer are bonded together by dispensing glue or stitching;

[0026] c Inner layer manufacturing: first mix lyocell fiber, wool fiber and cotton fiber evenly, and then go through cleaning-carding-drawing-rovin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention particularly relates to a preparation method of a lyocell fiber antibacterial blended fabric. The method comprises: surface layer preparing, wherein the surface layer is made of a lyocell fiber antibacterial fabric, the lyocell fiber antibacterial fabric is formed by interweaving warp threads and weft threads, the warp thread is blended yarns of lyocell fibers and cotton fibers, andthe weft thread is blended yarns of wool fibers and cotton fibers; middle layer preparing, wherein wool fibers and cotton fibers in a first fabric layer and a third fabric layer are blended firstly and then blended with lyocell fibers to be woven into a cloth, a second fabric layer is formed by spinning cotton fibers, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a glue dispensing or needle and thread sewing mode; inner layer preparing; and integral sewing. According to the invention, the preparation method of the lyocell fiber antibacterial blended fabric is provided, the prepared fabric has good lyocell fiber antibacterial function, and the preparation technological process is simple and easy to operate.

Description

technical field [0001] The invention belongs to the technical field of fabrics, and in particular relates to a preparation method of a lyocell fiber antibacterial blended fabric. Background technique [0002] As people's awareness of environmental protection and health care continues to increase, more and more people begin to pay attention to natural fibers. Cotton fibers, as the most commonly used natural fibers, are widely used in the production of various textiles. At present, there are endless yarns on the market, with different material structures, which are widely used in weaving, rope making, thread making and other fields of life. Xinjiang cotton fiber is very famous in the textile industry because of its softness and length, and is known as the best among cottons. It has the advantages of less yarn defects, uniform and smooth dryness, and high dyeability. Yet the elasticity and warmth retention property of the cotton fiber blended yarn on the market are not good at...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B9/02B32B5/06B32B7/12B32B9/04B32B37/10B32B37/12B32B38/00
CPCB32B5/024B32B5/06B32B5/26B32B7/12B32B9/047B32B37/10B32B37/12B32B38/00B32B2038/008B32B2250/03B32B2250/20B32B2262/062B32B2262/08B32B2307/7145
Inventor 周建
Owner JIANGYIN XIANGFEI APPAREL