A kind of magnetic jet polishing fluid and preparation method thereof

A technology of magnetic jet and polishing fluid, which is applied in the direction of polishing compositions containing abrasives, etc., and can solve the problems that the polishing fluid is difficult to meet

Active Publication Date: 2021-07-06
CHANGCHUN INST OF OPTICS FINE MECHANICS & PHYSICS CHINESE ACAD OF SCI
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The polishing liquid used in the existing magnetic jet polishing technology is mostly based on the conventional magnetorheological polishing liquid, but due to the particularity of the magnetic jet processing process, it requires that the polishing liquid not only have good rheological properties, but also under high pressure And under high-speed impact, it has good rust resistance and suspension stability, while conventional magnetorheological polishing fluid is difficult to meet the above requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of magnetic jet polishing fluid and preparation method thereof
  • A kind of magnetic jet polishing fluid and preparation method thereof
  • A kind of magnetic jet polishing fluid and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] The present invention also provides a method for preparing the magnetic jet polishing fluid described in the above technical solution, comprising the following steps:

[0046] Mix soft magnetic powder, non-magnetic polishing powder, thickener, dispersant, antirust agent, extreme pressure wear agent, pH regulator and defoamer in water to obtain a magnetic jet polishing fluid.

[0047] In the preparation method provided by the present invention, the soft magnetic powder, non-magnetic polishing powder, thickener, dispersant, antirust agent, extreme pressure wear-resistant agent, pH regulator and defoamer are mixed uniformly in water, that is The magnetic jet polishing fluid provided by the invention can be obtained. Wherein, the concrete process of described mixing preferably comprises:

[0048] a) adding thickener, dispersant, antirust agent, extreme pressure wear agent, pH regulator, and defoamer into water and mixing in order to obtain a composite carrier liquid;

[0...

Embodiment 1

[0065] 1) Composition design

[0066] The specific components and content of the magnetic jet polishing liquid provided in this embodiment are as shown in Table 1:

[0067] Table 1 Embodiment 1 Composition information table of magnetic jet polishing fluid

[0068]

[0069] 2) The preparation of the magnetic jet polishing fluid, the specific steps are as follows:

[0070] Step 1. Weigh 480g of deionized water, add 4g of sodium carboxymethyl cellulose to it, stir for 5 hours with a disperser, set the speed of the stirrer at 800r / min, and control the temperature at 70°C.

[0071] Step 2. Add 16g of sodium polymethacrylate to the solution obtained in step 1, and stir for 2 hours with a stirrer, the speed of the stirrer is set at 500r / min, and the temperature is controlled at 22°C.

[0072]Step 3. Add 10 g of anti-phosphate ester into the solution obtained in step 2, and stir for 1.5 hours with a stirrer, the speed of the stirrer is set at 500 r / min, and the temperature is con...

Embodiment 2

[0078] 1) Composition design

[0079] The specific components and content of the magnetic jet polishing liquid provided in this embodiment are as shown in Table 2:

[0080] Table 2 The composition information table of embodiment 2 magnetic jet polishing liquid

[0081]

[0082] 2) The preparation of the magnetic jet polishing fluid, the specific steps are as follows:

[0083] Step 1. Weigh 450g of deionized water, add 5g of sodium carboxymethyl cellulose to it, stir for 5 hours with a disperser, set the speed of the stirrer at 1000r / min, and control the temperature at 80°C.

[0084] Step 2. Add 20 g of polycarboxylate into the solution obtained in Step 1, and stir for 1 hour with a stirrer. The speed of the stirrer is set at 500 r / min, and the temperature is controlled at 25° C.

[0085] Step 3. Add 10 g of organic phosphate into the solution obtained in Step 2, and stir for 1 hour with a stirrer, the speed of the stirrer is set at 500 r / min, and the temperature is contro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of optics and metal precision processing and manufacture, and in particular relates to a magnetic jet polishing fluid and a preparation method thereof. The magnetic jet polishing fluid provided by the invention comprises: soft magnetic powder 50-75wt%; non-magnetic polishing powder 0.2-5wt%; thickener 0.1-0.3wt%; dispersant 0.5-1wt%; rust inhibitor 0.3-0.5wt% %; extreme pressure wear agent 0.2~0.3wt%; pH regulator 0.2~0.3wt%; defoamer 0.01~0.05wt%; solvent is water; One or more of sodium polyvinylpyrrolidone carboxylate; rust inhibitors include one or more of inorganic phosphates, organic phosphates, carboxylates and phosphoric acid esters; extreme pressure wear agents include borates and / or borates. The magnetic jet polishing fluid provided by the invention has good rust resistance and suspension stability under the conditions of high pressure and high speed impact.

Description

technical field [0001] The invention belongs to the field of optics and metal precision processing and manufacture, and in particular relates to a magnetic jet polishing fluid and a preparation method thereof. Background technique [0002] As early as the 1990s, the Belarus Institute of Heat and Mass Transfer used magnetorheological fluid and added polishing particles to realize the polishing of optical components, and optimized and promoted this method, and proposed magnetorheological polishing technology. This technology has been successfully applied in the field of ultra-precision machining. Magnetic jet polishing technology is a new processing method based on magnetorheological polishing technology. Its main advantage is that it can achieve ultra-precision machining of complex structures, especially complex cavities, and has high material removal efficiency and polishing quality. This technology is different from water jets. Its polishing process does not require ultra-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09G1/02
CPCC09G1/02
Inventor 白杨王旭李龙响王孝坤薛栋林张学军
Owner CHANGCHUN INST OF OPTICS FINE MECHANICS & PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com