Preparation method of terylene light-shieding flame-retardant coated fabric

A flame retardant coating and fabric technology, which is applied in the field of polyester shading flame retardant coating fabric preparation, can solve the problems of non-compliance with users, unreasonable coating process control, etc., and achieve the effect of solving environmental protection problems

Inactive Publication Date: 2020-05-05
WUJIANG FUHUA WEAVING
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] (1) Due to the unreasonable treatment of the base fabric and the unreasonable control of the coating process, the shrinkage of the coated fabric is greater than 3% after a period of time at room temperature, and the product seam slippage is greater than 3mm, which does not meet the user's requirements
[0004] (2) Commonly used shading and flame-retardant coatings contain a variety of heavy metal ions and toxic substances exceeding the standard for formaldehyde

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The first coating agent PA emulsion includes the following formulations by mass:

[0034] Polyacrylate 100g;

[0035] Cross-linking agent 2g;

[0036] Toluene 6g;

[0037] White paint paste 20g.

[0038] The second coating agent PA emulsion includes the following formulations by mass:

[0039] Shading paint X3 100g;

[0040] Flame retardant XT 30g;

[0041] Cross-linking agent 2g;

[0042] Accelerator 0.5g;

[0043] Toluene 6g;

[0044] Ethyl acetate 6g;

[0045] The third coating agent PA emulsion includes the following formulations by mass:

[0046] Polyacrylate 100g;

[0047] Cross-linking agent 20g.

Embodiment 2

[0049] The first coating agent PA emulsion includes the following formulations by mass:

[0050] Polyacrylate 100g;

[0051] Cross-linking agent 2-3g;

[0052] Toluene 6-9g;

[0053] White paint slurry 20-30g.

[0054] The second coating agent PA emulsion includes the following formulations by mass:

[0055] Shading paint X3 100g;

[0056] Flame retardant XT 30g;

[0057] Cross-linking agent 2.5g;

[0058] Accelerator 1g;

[0059] Toluene 7.5g;

[0060] Ethyl acetate 7.5g;

[0061] The third coating agent PA emulsion includes the following formulations by mass:

[0062] Polyacrylate 100g;

[0063] Cross-linking agent 25g.

Embodiment 3

[0065] The first coating agent PA emulsion includes the following formulations by mass:

[0066] Polyacrylate 100g;

[0067] Cross-linking agent 3g;

[0068] Toluene 9g;

[0069] White paint paste 30g.

[0070] The second coating agent PA emulsion includes the following formulations by mass:

[0071] Shading paint X3 100g;

[0072] Flame retardant XT 30g;

[0073] Cross-linking agent 3g;

[0074] Accelerator 2g;

[0075] Toluene 9g;

[0076] Ethyl acetate 9g;

[0077] The third coating agent PA emulsion includes the following formulations by mass:

[0078] Polyacrylate 100g;

[0079] Cross-linking agent 30g.

[0080] Finally, the fabric enters the oven in a completely relaxed state for setting: the temperature is 165-175°C, and the speed is 38-42m / min.

[0081] Select the appropriate environmental protection rubber material, which does not contain any heavy metal ions and other toxic and harmful substances, and solves the environmental protection problem. The pre-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a terylene light-shielding flame-retardant coated fabric. The preparation method is carried out according to the following flow of: fabric pre-shrinking, fabric padding pretreatment agent drying, base coating drying, light-shielding layer coating drying and surface color coating drying, wherein in the fabric pre-shrinking process, a pre-shrinking setting speed is reduced to 20m / min from 40m / min, a pre-shrinking temperature is risen to 200 DEG C from 150 DEG C, and an effective width of 150cm of a base fabric before pre-shrinking is reduced to aneffective width of 146cm after pre-shrinking; an assistant water-soluble flame-retardant pretreatment agent is selected to carry out padding on the fabric, coating agents are compositely coated and scraped on the base fabric, the coating agents sequentially comprise three coating agents of a PA emulsion, a flame retardant and silver colloid, and finally, the fabric enters a drying oven in a completely relax state to be set. Proper environmental-friendly glue is selected, so that the problem of environmental protection is solved. The pre-shrinking setting speed and the pre-shrinking temperaturein the fabric pre-shrinking process are controlled, so that problems of size stability and seam slippage are solved, shrinkage control is smaller than 1%, and seam slippage is smaller than 2%.

Description

technical field [0001] The invention relates to a flame-retardant curtain fabric, in particular to a preparation method of a polyester light-shading flame-retardant coating fabric. Background technique [0002] Fabric finishing can not only endow textiles with aesthetic effects, but more importantly, special effects. Functional finishing technology can protect textiles from various adverse environmental influences, such as harsh climate, microorganisms or bacteria, high temperature, chemicals (such as acids, alkalis and organic solvents), and mechanical abrasion. At present, shading and flame-retardant coated fabrics are less produced in the market, and the production process has not yet been perfected. The main common problems are the following technical difficulties in the production process: [0003] (1) Due to the unreasonable treatment of the base fabric and the unreasonable control of the coating process, the shrinkage rate of the coated fabric is greater than 3% afte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D06N3/04D06C17/00
CPCD06N3/042D06N3/0061D06C17/00D06N2213/03D06N2209/067D06N2209/0853D06N2211/122
Inventor 李茂明梁伟
Owner WUJIANG FUHUA WEAVING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com