Chemically-excited sulfur-fixing ash-based foam light soil

A technology of foam light soil and sulfur-fixed ash, which is applied in the field of building materials, can solve the problems of restricting the large-scale utilization of sulfur-fixed ash, low chemical activity, and poor workability, so as to promote utilization and development, and improve strength. Low, reduce the effect of damage

Active Publication Date: 2020-05-08
SHANDONG UNIV +1
View PDF8 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the emission of solid waste sulfur-fixed ash produced by circulating fluidized bed combustion technology is much higher than that of fly ash produced by pulverized coal boilers, and the untreated sulfur-fixed ash has rough particles, loose and porous surface, and low chemical activity. , high sulfur and high calcium and other physical and chemical properties, applied to cement-based materials will cause poor workability and later expansion problems, which restricts the large-scale utilization of sulfur-fixed ash

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] In some embodiments, the preparation method of the sulfur-fixed ash-based foam lightweight soil includes the following steps:

[0039] (1) Weigh the sulfur-fixed ash, fly ash, cement and foam raw materials of a certain mass portion;

[0040] (2) Stir the sulfur-fixed ash, fly ash, and cement at a speed of 1300 to 1500 rpm for 3 to 5 minutes in step (1);

[0041] (3) Add water to the pre-stirred dry material in step (2), and stir at a speed of 1300-1500 rpm for 3-5 minutes;

[0042] (4) Add the weighed activator into the mixed slurry obtained in step (3), and stir at a speed of 1300-1500 rpm for 3-5 minutes.

[0043] (5) Dilute the weighed foaming agent to 40 to 50 times and foam it by high-pressure air method to obtain foam, then add the foam to the mixed slurry obtained in step (4), and stir at a speed of 600 to 800rpm 2~3min.

[0044] (6) Adjust the density of the mixed slurry to 550-650g / L and test the flow value until the flow value reaches 18±1cm.

[0045] (7) ...

Embodiment 1

[0052] A preparation method of sulfur-fixed ash slag-based foam light soil, comprising the following steps:

[0053] (1) Weigh 116 parts of sulfur-fixing ash, 39 parts of fly ash, 260 parts of cement, 0.5 part of activator, 186 parts of water and 0.7 part of blowing agent;

[0054] (2) Stir the sulfur-fixed ash, fly ash, and cement for 3 minutes at a speed of 1400 rpm in step (1);

[0055] (3) Add water to the pre-stirred dry material in step (2), and stir for 3 minutes at a speed of 1400 rpm;

[0056] (4) activator is added in the cement slurry that step (3) stirs, stir 3min with the rotating speed of 1400rpm;

[0057] (5) After the blowing agent is diluted to 40 times, the foam is obtained by high-pressure air foaming. Then, the foam is added to the mixed slurry obtained in step (3), and stirred at a speed of 700rpm for 2min.

[0058] (6) Adjust the density of the mixed slurry to 600g / L and test the flow value until the flow value reaches 18±1cm.

[0059] (7) Pour the gai...

Embodiment 2

[0062] A preparation method of sulfur-fixed ash slag-based foam light soil, comprising the following steps:

[0063] (1) Weigh 101 parts of sulfur-fixing ash, 34 parts of fly ash, 275 parts of cement, 191 parts of water, 0.5 part of activator and 0.7 part of blowing agent;

[0064] (2) Stir the sulfur-fixed ash, fly ash, and cement for 3 minutes at a speed of 1400 rpm in step (1);

[0065] (3) Add water to the pre-stirred dry material in step (2), and stir for 3 minutes at a speed of 1400 rpm;

[0066] (4) activator is added in the cement slurry that step (3) stirs, stir 3min with the rotating speed of 1400rpm;

[0067] (5) After the blowing agent is diluted to 40 times, the foam is obtained by high-pressure air foaming. Then, the foam is added to the mixed slurry obtained in step (3), and stirred at a speed of 700rpm for 2min.

[0068] (6) Adjust the density of the mixed slurry to 600g / L and test the flow value until the flow value reaches 18±1cm.

[0069] (7) Pour the gai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to chemically-excited sulfur-fixing ash-based foam light soil which is prepared from the following raw materials in parts by mass: 88-165 parts of sulfur-fixing ash, 260-293 parts of cement, 29-55 parts of fly ash, 0.4-0.5 part of an excitant, 0.7-0.8 part of a foaming agent and 180-190 parts of water. According to the method, the solid waste sulfur-fixing ash of a thermal power plant is applied to the foamed light soil for the first time, a feasible method is provided for solving the stockpiling problem of the sulfur-fixing ash, and utilization and development of the clean energy technology of circulating fluidized bed combustion are promoted. The fly ash and the sulfur-fixing ash are mixed, so that the expansibility of the sulfur-fixing ash-based light soil can be reduced, the expansion stable period of the sulfur-fixing ash-based light soil is advanced, and the damage of the expansibility of the sulfur-fixing ash to the foamed light soil is reduced.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a chemically excited sulfur-fixing ash-based foam lightweight soil. Background technique [0002] The information disclosed in this background section is only intended to increase the understanding of the general background of the present invention, and is not necessarily to be regarded as an acknowledgment or any form of suggestion that the information constitutes the prior art already known to those skilled in the art. [0003] Foam light soil is a lightweight engineering material with a large number of closed pores obtained by adding the foam group obtained by foaming with a foaming agent into the cementitious material and curing it. It has the advantages of light weight, good integrity, adjustable strength and density, high fluidity, good heat insulation, sound insulation, waterproof performance, and self-support after solidification. The difference in settlemen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C04B38/10
CPCC04B28/02C04B38/10C04B2201/50C04B18/064C04B18/08C04B24/122
Inventor 蒋红光姚占勇薛志超侯智坚迟浩然姚凯胡艳秋梁明张吉哲
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap