Nickel base alloy coating smooth sucker rod with high-toughness clamping section and machining method thereof

A technology for sucking polished rods and nickel-based alloys, which is applied to metal material coating processes, coatings, drill pipes, etc., and can solve the problems of limited improvement in the service life of polished rods and difficulty in effectively solving polished rod fractures.

Inactive Publication Date: 2020-05-22
BEIJING TECHNOLOGY AND BUSINESS UNIVERSITY
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing alloy-coated polished rods have been improved in many aspects, such as adjusting the composition of the NiCrBSi self-fluxing alloy coating, and using polished rod base materials with better toughness and fatigue resistance, but the improvement in the service life of polished rods Limited, it is still difficult to effectively solve the fracture of polished rods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel base alloy coating smooth sucker rod with high-toughness clamping section and machining method thereof
  • Nickel base alloy coating smooth sucker rod with high-toughness clamping section and machining method thereof
  • Nickel base alloy coating smooth sucker rod with high-toughness clamping section and machining method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] seefigure 1 and figure 2 According to the nickel-based alloy coated oil pumping rod with high toughness clamping section provided by the present invention, it comprises a base material 1 and an alloy coating positioned on the surface of the base material, the base material 1 is a long straight round rod, One end is an upset end 12, and the other end is an unupset end 11. Starting from the unupset end 11, the substrate 1 sequentially includes a first transition section 13, a clamping section 14, a second transition section 15 and a rod body 16 , the clamping section 14 of the substrate 1 is 1 to 3 meters long, and the first transition section 13 and the second transition section 15 are 0.1 to 0.5 meters long; the alloy coating includes a high-nickel tough composite coating 21 and a nickel-based self-fluxing alloy coating 22, the first transition section 13 and the clamping section 14 of the substrate 1 are prepared with the high-nickel tough composite coating 21, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a nickel base alloy coating smooth sucker rod with a high-toughness clamping section and a machining method thereof. The smooth sucker rod comprises a base material and an alloy coating located on the surface of the base material. The base material is a long and straight round rod, one end of the base material is an upset end, and the other end of the base material is a non-upset end. Starting from the non-upset end, the base material sequentially comprises a first transition section, the clamping section, a second transition section and a rod body. The alloy coating comprises a high-nickel high-toughness composite coating and a nickel base self-fluxing alloy coating. The surfaces of the first transition section, the clamping section and the second transition section of the base material are provided with texture patterns. Through the design of the base material of the smooth sucker rod, by introducing the millimeter-scale texture patterns into the surface of the clamping section of the base material and using the high-toughness nickel base alloy coating on the surface of the base material, the alloy coating smooth sucker rod with excellent toughness, wearresistance and corrosion resistance is provided, and the service life of the smooth sucker rod is remarkably prolonged.

Description

technical field [0001] The invention relates to petroleum equipment, in particular to a nickel-based alloy coated oil pumping polished rod. Background technique [0002] The oil pumping polished rod is one of the most critical components in oil field artificial lift production. Once the polished rod breaks, it will cause the oil well to stop production and carry out workover operations, resulting in huge economic losses. [0003] Wear, corrosion, and fracture are the three main causes of failure in polished rods. There have been many successful ways to solve wear and corrosion. For example, the nickel-based alloy coating spray-welded polished rod specified in the API 11B and SY / T 5029 standards has solved the wear and corrosion of the polished rod very well, and has become an oil field application. The widest range of polished rods. However, there is a big problem in the fracture of polished rods. Due to the superposition of severe bending alternating stress and tension al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E21B17/00E21B17/10C22C19/03C22C19/05C23C24/10
CPCC22C19/03C22C19/05C23C24/103E21B17/00E21B17/1085
Inventor 田斌冉志勇杜秋月张小青
Owner BEIJING TECHNOLOGY AND BUSINESS UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com