Preparation method and application of acid-resistant PSQ composite membrane

A composite membrane, acid-resistant technology, applied in chemical instruments and methods, membrane technology, semipermeable membrane separation, etc. Thermal stability, tunable surface properties, effect of membrane area reduction

Active Publication Date: 2020-07-03
CHANGZHOU UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the complexity of the film-forming mechanism of zeolite membranes, the difficulty in preparation, the high requirements on the carrier, and the need for expensive templates, it is difficult to expand its application
Moreover, although zeolite membranes (such as A-type zeolite and mordenite) show certain acid resistance properties, their acid resistance is only limited to weak acid conditions (such as acetic acid) in the current literature reports, and its performance will decrease as the concentration of weak acids increases. Decrease, and the overall performance fluctuates greatly in strong acid (such as nitric acid) system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of acid-resistant PSQ composite membrane
  • Preparation method and application of acid-resistant PSQ composite membrane
  • Preparation method and application of acid-resistant PSQ composite membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Dissolve 1,2-(triethoxysilyl)ethylene (BTESEthy) in an alcohol solvent with a mass fraction of 5wt%, add deionized water and 2wt% hydrochloric acid, and stir continuously for 30min in a water bath at 50°C , wherein the molar ratio of BTESM, water, and hydrochloric acid is 1:80:0.1.

[0026] (2) step (1) after acid catalyzed reaction, add ammoniacal liquor and carry out alkali catalyzed reaction, add the ammoniacal liquor that massfraction is 5wt% in molar ratio ammoniacal liquor: hydrochloric acid (the hydrochloric acid that is step (1)) is the ratio of 9:1, 50 ℃ Stir continuously in a water bath for 60 minutes to carry out alkali-catalyzed reaction, so that the particle size of the sol increases.

[0027] (3) add hydrochloric acid to carry out acid-catalyzed reaction after alkali catalysis, according to molar ratio hydrochloric acid: the ratio of ammoniacal liquor is 1.2:1 adding mass fraction is the hydrochloric acid of 2wt% to stop the alkali-catalyzed reaction o...

Embodiment 2

[0030] (1) Dissolve 1,2-bis(triethoxysilyl)methane (BTESM) in an alcohol solvent at 5 wt% by mass fraction, add deionized water and 2 wt% hydrochloric acid, and continuously stir in a water bath at 50°C 30min, wherein the molar ratio of BTESM, water and hydrochloric acid is 1:60:0.1.

[0031] (2) Add ammonia water with a mass fraction of 5wt% at a ratio of 10:1 to hydrochloric acid, and stir continuously in a water bath at 50°C for 60 minutes to carry out alkali-catalyzed reaction to increase the particle size of the sol.

[0032] (3) Molar ratio hydrochloric acid: ammoniacal liquor is the ratio of 1.5:1 to add the hydrochloric acid that the mass fraction is 2wt% to stop the alkali-catalyzed reaction of step (2), the reaction time is 45min, and reaction temperature is 45 ℃, generates stable under acidic environment BTESM Sol.

[0033] (4) Coating silica-zirconia sol on the ceramic support to form a transition layer, the transition layer is 0.5 wt% silica-zirconia sol. The tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method and an application of an acid-resistant PSQ composite membrane, and belongs to the technical field of membrane separation preparation. The preparation method comprises the following steps: (1) dissolving a PSQ precursor in an alcohol solvent, sequentially adding hydrochloric acid, ammonia water and hydrochloric acid, and carrying out an acid-base-acid alternate catalytic reaction to obtain PSQ sol; (2) coating a ceramic support body with a silicon dioxide-zirconium oxide sol to generate a transition layer; and (3) coating the surface of the transition layer with the PSQ sol to serve as a separation layer, and dipping-pulling to prepare the PSQ composite membrane with a supporting layer, the transition layer and a separation layer structure . ThePSQ composite membrane provided by the invention has good acid resistance, high flux and high selectivity, meets the current industrial requirements and expectations, and is widely applied to organicsolvent dehydration and organic solvent separation of an acidic system.

Description

technical field [0001] The invention belongs to the field of membrane separation preparation, in particular to a preparation method and application of an acid-resistant PSQ composite membrane. Background technique [0002] Anhydrous-grade organic solvents are essential in the fields of petrochemical, fine chemical, pharmaceutical and food industries, so it is particularly important to separate a small or trace amount of water from organic solvents to obtain anhydrous-grade organic solvents. Traditional organic solvent dehydration technologies such as extractive distillation, azeotropic distillation, and molecular sieve adsorption have disadvantages such as high energy consumption, complex process, high operating cost, and environmental pollution. Therefore, the above fields are facing the challenge of energy saving and emission reduction. Membrane separation technology has the advantages of high efficiency, low energy consumption, easy control, and small footprint, and it is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D67/00B01D69/12B01D61/36B01D61/02
CPCB01D67/0079B01D69/12B01D69/125B01D61/362B01D61/027B01D61/025
Inventor 徐荣刘倩钟璟任秀秀左士祥
Owner CHANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com