Method for preventing buckling and deviation in continuous annealing furnace of strip steel with thickness not greater than 0.5mm

A technology of continuous annealing furnace and continuous annealing furnace, which is used in furnaces, furnace types, heat treatment furnaces and other directions to achieve the effect of increasing machine-hour output, improving corporate reputation and economic benefits, and facilitating adjustment

Active Publication Date: 2021-11-23
新余钢铁股份有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Thin-gauge (thickness not greater than 0.5mm) cold-rolled steel strip bending and deviation in continuous annealing furnace is a problem. At present, there is no relevant prevention of thin-gauge steel strip thickness not greater than 0.5mm in continuous annealing furnace. Report on the technical solution of the deviation control method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preventing buckling and deviation in continuous annealing furnace of strip steel with thickness not greater than 0.5mm
  • Method for preventing buckling and deviation in continuous annealing furnace of strip steel with thickness not greater than 0.5mm
  • Method for preventing buckling and deviation in continuous annealing furnace of strip steel with thickness not greater than 0.5mm

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Methods to prevent bending and deviation in the continuous annealing furnace of strip steel with a thickness not greater than 0.5mm:

[0051] The target steel type is XGMB (strip steel for deep drawing), the product specification thickness×width is 0.5×1250mm, according to the production plan, arrange 2 rolls of transition material in advance, the steel type is DC01, and the product specification thickness×width is 0.6×1000mm. Since it is a transition from narrow front to wide rear and the width difference is ≥100mm, use crescent scissors to punch out the transition area at the rear half of the crescent at the weld to avoid stress concentration in the transition area and increase the risk of buckling.

[0052] Heating temperature control: The plate temperature in the heating section and the soaking section is gradually increased from 780°C to 820°C required by the target strip during the production of the 2-coil preceding transition material DC01 and remains in a stable ...

Embodiment 2

[0061] Methods to prevent bending and deviation in the continuous annealing furnace of strip steel with a thickness not greater than 0.5mm:

[0062] The target steel grade is DC03 (strip steel for deep drawing), and the product specification is 0.5×1000mm. According to the production plan, 3 rolls of transition material are arranged in advance. The steel grade is DC01, and the product specification is 0.45×1100mm.

[0063] Heating temperature control: The plate temperature in the heating section and soaking section is gradually increased from 780°C to 810°C required by the target strip during the production of 3 rolls of transition material DC01 and remains stable.

[0064] Tension control mode: After the target strip enters the furnace, it is changed from the secondary value tension mode control to the manual tension mode control. The tension is gradually revised to +19.06% of the secondary value. Before the head of the target strip is about to pass through the 1# aging secti...

Embodiment 3

[0072] Methods to prevent bending and deviation in the continuous annealing furnace of strip steel with a thickness not greater than 0.5mm:

[0073] The target steel type is XGMB (strip steel for deep drawing), the product specification is 0.4×1000mm, according to the production plan, arrange 2 rolls of transition material in advance, the steel type is DC01, and the product specification is 0.4×1000mm.

[0074] Heating temperature control: The plate temperature in the heating section and the soaking section is gradually increased from 780°C to 815°C required by the target strip during the production of the 2-coil preceding transition material DC01 and remains in a stable state.

[0075] Tension control mode: After the target strip enters the furnace, it is changed from the secondary value tension mode control to the manual tension mode control. The tension is gradually modified to +15% of the secondary value. Before the head of the target strip is about to pass through the 1# ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The method provided by the present invention to prevent bending and deviation in the continuous annealing furnace of strip steel with a thickness not greater than 0.5mm, the tension of the heating section and the soaking section is controlled at 6.48-8.64N / mm 2 ;The temperature is controlled at 770-830°C; the tension of the strip steel in the cold zone of the continuous annealing furnace is controlled at 6.21-8.464N / mm 2 ; The plate temperature in the final cooling section is controlled at 170-180°C. Compared with the prior art, the present invention prevents thin-gauge strip steel with a thickness not greater than 0.5 mm from being continuously annealed by increasing the tension in the hot zone, reducing the tension in the cold zone, reducing the plate temperature in the hot zone, and increasing the plate temperature in the final cooling section. In order to improve the one-time hit rate of the product and ensure the smooth flow of production.

Description

technical field [0001] The invention belongs to the technical field of continuous annealing, and relates to a method for preventing cold-rolled strip steel from bending and deviation in a continuous annealing furnace, in particular to a method for preventing bending and deviation in a steel strip with a thickness not greater than 0.5 mm. Background technique [0002] The continuous annealing furnace is usually divided into 8 different areas, which are preheating section (JPF), heating section (RTF), soaking section (SF), slow cooling section (SCS), rapid cooling section (RCS), 1# aging section Section (1#OA), 2# aging section (2#OA), final cooling section (FCS), the strip tension in each area is adjusted by the tensiometer roller set between the areas. During the high-speed continuous annealing process of cold-rolled strip steel, affected by factors such as strip steel shape, furnace tension, transition between front and rear varieties and specifications, temperature, etc., ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D9/573C21D9/56C21D1/26C21D11/00
CPCC21D1/26C21D9/564C21D9/573C21D11/00C21D11/005
Inventor 钟海清范超黄丽芳谢芳罗庆华易新平王金云陈渊邱明罗辉郭赞杨
Owner 新余钢铁股份有限公司