Garden rockery beneficial to cultivation of green plants and processing method thereof

A technology of rockery and gardens, applied in the field of garden rockery and its processing, can solve problems affecting the environment, achieve beautification and purification of the environment, avoid adverse effects, and have strong environmental protection

Active Publication Date: 2020-07-17
NANJING FORESTRY UNIV +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, industrial waste blast furnace expansion slag and fly ash are produced in a large amount. If they are not used rationally, they will seriously affect the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Processing of rockery:

[0041] (1) Mold making: the mold includes an outer mold and an inner mold, and the mold is made according to the established rockery structure;

[0042] (2) Mixing materials: 60kg blast furnace expanded slag of 80 meshes, 30kg Class I fly ash, 20kg Portland cement, 13kg lignocellulose, 10kg asbestos wool, 3kg cement additive hydrolyzed polymaleic anhydride, 5kg binder Styrene-butadiene copolymer and 5kg lubricant talcum powder are added in the mixer, mixed for 10min at a rotating speed of 800r / min, and mixed evenly to obtain the rockery processing material;

[0043] (3) Pouring: import the above-mentioned materials into the mold, insert the vibrating rod into the mold, vibrate and tamp the material, and replenish the material until the material is tamped and flush with the mold opening;

[0044] (4) Demoulding: The material is cured and molded for 48 hours under natural conditions of 25°C, and the outer mold and the inner mold are separated to ...

Embodiment 2

[0047] The difference between embodiment 2 and embodiment 1 is the change of raw material consumption.

[0048] Processing of rockery:

[0049] (1) Mold making: the mold includes an outer mold and an inner mold, and the mold is made according to the established rockery structure;

[0050] (2) Mixing materials: 55kg blast furnace expanded slag of 80 meshes, 32kg Class I fly ash, 22kg Portland cement, 12kg lignocellulose, 10kg asbestos wool, 3kg cement admixture hydrolyzed polymaleic anhydride, 5kg binder Styrene-butadiene copolymer and 4kg lubricant talcum powder are added in the mixer, mixed for 10min at a rotating speed of 800r / min, and mixed evenly to obtain the rockery processing material;

[0051] (3) Pouring: import the above-mentioned materials into the mold, insert the vibrating rod into the mold, vibrate and tamp the material, and replenish the material until the material is tamped and flush with the mold opening;

[0052] (4) Demoulding: The material is cured and mo...

Embodiment 3

[0055] Taking Example 1 as a comparison, the cement admixture is set to replace the hydrolyzed polymaleic anhydride with an equivalent amount of polyaspartic acid in Example 3, and the rest of the processing operations are exactly the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a garden rockery beneficial to cultivation of green plants and a processing method of the garden rockery. The invention relates to the technical field of rockery processing. The garden rockery is prepared from the following raw materials in parts by weight: 30-80 parts of blast furnace expansion slag, 10-50 parts of fly ash, 10-50 parts of Portland cement, 5-20 parts of lignocellulose, 5-20 parts of asbestos wool, 1-10 parts of a cement additive, 1-10 parts of a binder, 1-10 parts of a lubricant and 100-200 parts of water. The garden rockery is prepared from the industrial waste blast furnace expanded slag and fly ash as main materials and auxiliary materials such as Portland cement, so that reasonable reutilization of the industrial waste blast furnace expanded slag and fly ash is achieved, and the prepared rockery is good in appearance quality, high in environmental protection property, excellent in compression resistance and beneficial to cultivation of largeand medium green plants on the rockery.

Description

Technical field: [0001] The invention relates to the technical field of rockery processing, in particular to a garden rockery beneficial to the cultivation of green plants and a processing method thereof. Background technique: [0002] Rockery is a mountain built with soil, stone and other materials for the purpose of landscaping in the garden. Rockery has various landscaping functions, such as forming the main landscape or terrain skeleton of the garden, dividing and organizing the garden space, arranging courtyards, revetments, slope protection, soil retaining, and setting up natural flower beds. It can also be combined with garden buildings, garden roads, sites and garden plants to form a changing landscape, so as to reduce the artificial atmosphere, add natural interest, and make the garden buildings blend into the landscape environment. Therefore, rockery has become one of the characteristics of Chinese natural landscape gardens. [0003] The development of modern gar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04A01G9/02
CPCA01G9/02C04B28/04C04B2111/00758C04B2201/50C04B18/141C04B18/08C04B18/26C04B14/40C04B24/2664C04B24/2611C04B14/042C04B24/165
Inventor 张青萍丁明静郑婕丁明亮