A two-component flame-retardant ceramic tile beautifying agent and preparation method thereof

A flame-retardant, beautifying agent technology, applied in the field of beautifying agents, can solve the problems of easy scratching, rough surface, easy blackening of gaps, etc., and achieve smooth and smooth surface of the adhesive film, simple preparation method, and wide application range. Effect

Active Publication Date: 2022-03-11
湖北碱克新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the common beautifying agents on the market have the following problems: 1. The adhesion strength of the cured adhesive film is not high enough, and it is prone to fall off; 2. The cured adhesive film is soft, and it is prone to scratches and abrasions; 3. The surface is rough, and the gap is easy to turn black after curing, and it is not suitable for the gap on the wall, and it is prone to sag

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A two-component flame-retardant ceramic tile beautifying agent and preparation method thereof
  • A two-component flame-retardant ceramic tile beautifying agent and preparation method thereof
  • A two-component flame-retardant ceramic tile beautifying agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A two-component flame-retardant tile beautifying agent, including A component and B component,

[0024] In parts by weight, the raw material composition of the A component includes:

[0025] Flame-retardant epoxy resin 90 parts,

[0026] Thickener 4 parts;

[0027] In parts by weight, the raw material composition of the B component includes:

[0028]

[0029] Wherein, the flame-retardant epoxy resin is phosphazene tripolymer epoxy resin, the curing agent is maleic anhydride, the leveling agent is polyamide, and the flow-stopping agent is diacetone alcohol , the thickener and thixotropic agent are fumed silica.

[0030] A method for preparing the above-mentioned beautifying agent, comprising the steps of:

[0031] (1) Mix the flame-retardant epoxy resin and the thickener in parts by weight, and stir evenly to obtain the A component;

[0032] (2) Mix the curing agent, leveling agent, stop-flow agent, thixotropic agent, and rutile titanium dioxide in parts by weigh...

Embodiment 2

[0035] A two-component flame-retardant tile beautifying agent, including A component and B component,

[0036] In parts by weight, the raw material composition of the A component includes:

[0037] Flame-retardant epoxy resin 95 parts,

[0038] 5 parts of thickener;

[0039] In parts by weight, the raw material composition of the B component includes:

[0040]

[0041] Wherein, the flame-retardant epoxy resin is phosphazene tripolymer epoxy resin, the curing agent is maleic anhydride, the leveling agent is polyamide, and the flow-stopping agent is diacetone alcohol , the thickener and thixotropic agent are fumed silica.

[0042] A method for preparing the above-mentioned beautifying agent, comprising the steps of:

[0043] (1) Mix the flame-retardant epoxy resin and the thickener in parts by weight, and stir evenly to obtain the A component;

[0044] (2) Mix the curing agent, leveling agent, stop-flow agent, thixotropic agent, and rutile titanium dioxide in parts by we...

Embodiment 3

[0047] A two-component flame-retardant tile beautifying agent, including A component and B component,

[0048] In parts by weight, the raw material composition of the A component includes:

[0049] 100 parts of flame retardant epoxy resin,

[0050] 6 parts of thickener;

[0051] In parts by weight, the raw material composition of the B component includes:

[0052]

[0053] Wherein, the flame-retardant epoxy resin is phosphazene tripolymer epoxy resin, the curing agent is maleic anhydride, the leveling agent is polyamide, and the flow-stopping agent is diacetone alcohol , the thickener and thixotropic agent are fumed silica.

[0054] A method for preparing the above-mentioned beautifying agent, comprising the steps of:

[0055] (1) Mix the flame-retardant epoxy resin and the thickener in parts by weight, and stir evenly to obtain the A component;

[0056] (2) Mix the curing agent, leveling agent, stop-flow agent, thixotropic agent, and rutile titanium dioxide in parts b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a two-component flame-retardant ceramic tile beautifying agent, which includes component A and component B, and the raw material composition of component A includes: flame-retardant epoxy resin 90~ 100 parts, 4-6 parts of thickener; the raw material composition of the B component includes: 20-30 parts of curing agent, 3-5 parts of leveling agent, 5-7 parts of flow-stopping agent, 30-50 parts of thixotropic agent share. The present invention also provides a method for preparing the above-mentioned beauty joint agent, which includes the following steps: (1) uniformly mixing the raw materials of the component A to obtain the component A; (2) mixing the component B (3) Mix the components A and B at a weight ratio of 1:0.5 to 1.5, and stir evenly to obtain the beautifying agent. The cured product prepared by the invention has a flat and smooth surface of the adhesive film, good wear resistance, high adhesion strength, is not easy to scratch, has flame retardancy, and can be applied to gaps on walls at the same time.

Description

technical field [0001] The invention relates to the technical field of beautifying agents, in particular to a two-component flame-retardant ceramic tile beautifying agent and a preparation method thereof. Background technique [0002] The beauty joint agent is a new type of adhesive for gap decoration that has emerged in recent years. It is characterized by various colors, bright colors, safety and environmental protection, no mold, easy to clean, etc., and has a good development prospect. At present, the common beautifying agents on the market have the following problems: 1. The adhesion strength of the cured adhesive film is not high enough, and it is prone to fall off; 2. The cured adhesive film is soft, and it is prone to scratches and abrasions; 3. The surface is rough, and the gaps are easy to turn black after curing, and it is not suitable for the gaps on the wall, and it is prone to sagging. Contents of the invention [0003] The present invention aims to solve at...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J163/00C09J11/08C09J11/04C09J11/06C08G59/42
CPCC09J163/00C09J11/08C09J11/04C09J11/06C08G59/4207C08L2201/02C08K2003/2241C08L77/00C08K7/26C08K3/22C08K5/07
Inventor 陈乐舟陈雯琪
Owner 湖北碱克新材料有限公司