Mould-proof polyester fiber and manufacturing method thereof

A polyester fiber and anti-mold technology, which is applied in the field of anti-mold polyester fiber and its preparation, can solve the problems of lack of laws and regulations, potential safety hazards, lack of supervision mechanism, etc., and achieve obvious anti-mold effect and good anti-mold effect Effect

Inactive Publication Date: 2020-07-28
王楠
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Relatively speaking, in the development of antibacterial textile products in my country, there is still a lack of corresponding laws and regulations, and there is also a lack of effective supervision mechanism, so that consumers still have certain safety hazards when using antibacterial products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Preparation of aqueous solution of litsea cubeba and cumin extract: 3 parts of litsea cubeba and 4 parts of cumin stems and leaves were sorted, impurity removed, washed with water, dried, crushed, scoured, refined, and spray-dried to obtain extract fine powder grain. Then put the fine powders of the two kinds of extracts into water at 50°C respectively, stir and dissolve to obtain aqueous solution of extracts of litsea cubeba and cumin, both of which have a mass fraction of 20%;

[0023] The preparation of microcapsules of plant Chinese medicine thyme essential oil: first, 2 parts of thyme essential oil in 6 parts of emulsifier solution form a uniform oil-in-water system with water in the form of tiny droplets, and then add 5 parts of melamine resin solution in acidic and heating environment. Medium polycondensation, and coagulation, deposition and solidification around the core material, wrapping the core material to form microcapsules of plant Chinese medicine thyme e...

Embodiment 2

[0029] Preparation of Litsea Cubeba and Cumin extract aqueous solution: 3 parts of Litsea cubeba and 4 parts of Cumin stems and leaves were sorted, impurity removed, washed with water, dried, crushed, scoured, refined, and spray-dried to obtain fine extracts. Powder. Then put the fine powders of the two kinds of extracts into water at 50°C respectively, stir and dissolve to obtain aqueous solution of extracts of litsea cubeba and cumin, both of which have a mass fraction of 20%;

[0030] The preparation of microcapsules of plant Chinese medicine thyme essential oil: first, 3 parts of thyme essential oil in 10 parts of emulsifier solution form a uniform oil-in-water system with water in the form of tiny droplets, and then add 3 parts of melamine resin solution in acidic and heated environment. Medium polycondensation, and coagulation, deposition and solidification around the core material, wrapping the core material to form microcapsules of plant Chinese medicine thyme essentia...

Embodiment 3

[0036] Preparation of Litsea cubeba and Cumin extract aqueous solution: Sorting, removing impurities, washing, drying, crushing, scouring, refining, and spray-drying 5 parts of Litsea Cubeba and 6 parts of Cumin stems and leaves respectively to obtain fine extracts. Powder. Then put the fine powders of the two kinds of extracts into water at 50°C respectively, stir and dissolve to obtain aqueous solution of extracts of litsea cubeba and cumin, both of which have a mass fraction of 20%;

[0037] The preparation of microcapsules of plant Chinese medicine thyme essential oil: first, form a uniform oil-in-water system with 3 parts of thyme essential oil in 7 parts of emulsifier solution in the form of tiny droplets and water, add 3 parts of melamine resin solution in acidic and heating environment Medium polycondensation, and coagulation, deposition and solidification around the core material, wrapping the core material to form microcapsules of plant Chinese medicine thyme essenti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of functional polyester fiber, in particular to mould-proof polyester fiber and a manufacturing method thereof. The mould-proof polyester fiber comprises the components in parts by mass: 5-10 parts of a viscose spinning solution, 3-5 parts of litsea cubeba, 4-6 parts of fennel stems and leaves, 2-5 parts of thyme essential oil, 5-10 parts of an emulgator solution, 2-4 parts of concentrated sulfuric acid, 2-5 parts of sodium sulfate, 1-3 parts of zinc sulfate and 3-6 parts of melamine resin; and the mould-proof polyester fiber is prepared by extracting a watersolution out of the litsea cubeba and fennel, preparing micro capsules from herbal Chinese medicine thyme essential oil and preparing mould-proof polyester fiber. Compared with other polyester fiberson the market, the mould-proof polyester fiber has the advantages of mould-proof effect, safety, non-toxicity and harmlessness.

Description

technical field [0001] The invention relates to the field of functional polyester fibers, in particular to a mildew-resistant polyester fiber and a preparation method thereof. Background technique [0002] Since the 1980s, the development of antibacterial fibers is the fastest in the upsurge of developing functional fibers worldwide. So far, its industrialization degree is also the highest. It is said that in the 1990s, the development speed of antibacterial fibers was five times the average development speed of other functional fibers. The rapid development of antibacterial textiles reflects the changes and development trends of market consumption trends, and is also a concentrated expression of high-tech in the development of functional textile products. [0003] At present, Japan is the leader in the development and industrialization of antibacterial fibers and antibacterial textiles, and they have developed to a fairly mature stage both in terms of quantity and quality...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F2/08B01J13/14
CPCB01J13/14D01F2/08
Inventor 王楠
Owner 王楠
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com