Repair system for cracks in concrete

A concrete and crack technology, applied in the field of concrete crack repair systems, can solve the problems of bottom wall deformation and fission, bottom wall cracks, insufficient freeze-thaw resistance, etc., and achieves better water resistance and freeze-thaw resistance, shearing Stronger effect

Active Publication Date: 2022-03-22
NORTHWEST UNIVERSITY FOR NATIONALITIES
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] In order to solve the above problems, the present invention provides a repair system for concrete cracks, which effectively avoids the lack of shear strength, water resistance, and freeze-thaw resistance in the actual application of concrete crack inhibitors in the prior art , The thermal stress causes the bottom wall in the concrete crack to deform and crack, and the bottom wall in the concrete crack also cracks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Repair system for cracks in concrete
  • Repair system for cracks in concrete
  • Repair system for cracks in concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Such as figure 1 As shown, the repair system for concrete cracks includes an epoxy resin layer 1, a thermoplastic sealing layer 2, and a base encapsulation growth layer 3 that are sequentially arranged from the crack surface along the crack depth direction to the bottom wall in the crack;

[0042] It also includes an auxiliary thermal layer 4 penetrating through the epoxy resin layer 1 , the thermoplastic sealing layer 2 and the base package growth layer 3 .

[0043] The thickness ratio of the epoxy resin layer 1 , the thermoplastic sealing layer 2 and the substrate packaging growth layer 3 is: 1:1:1.

[0044] The material of the base encapsulation growth layer 3 is a concrete crack inhibitor, and the preparation method of the concrete crack inhibitor comprises the following steps:

[0045] (1) Synthesis of β-cyclodextrin powder containing multiple double bonds: first disperse β-cyclodextrin in anhydrous dimethyl sulfoxide, and gradually add dropwise acryloyl chloride ...

Embodiment 2

[0079] A repair system for concrete cracks, including an epoxy resin layer 1, a thermoplastic sealing layer 2, and a substrate encapsulation growth layer 3, which are sequentially arranged from the crack surface along the crack depth direction to the bottom wall of the crack;

[0080] It also includes an auxiliary thermal layer 4 penetrating through the epoxy resin layer 1 , the thermoplastic sealing layer 2 and the base package growth layer 3 .

[0081] The thickness ratio of the epoxy resin layer 1 , the thermoplastic sealing layer 2 and the substrate packaging growth layer 3 is: 1:1:1.

[0082] The material of the base encapsulation growth layer 3 is a concrete crack inhibitor, and the preparation method of the concrete crack inhibitor comprises the following steps:

[0083] (1) Synthesis of β-cyclodextrin powder containing multiple double bonds: first disperse β-cyclodextrin in anhydrous dimethyl sulfoxide, and gradually add dropwise acryloyl chloride containing 10wt% mass...

Embodiment 3

[0116] A repair system for concrete cracks, including an epoxy resin layer 1, a thermoplastic sealing layer 2, and a substrate encapsulation growth layer 3, which are sequentially arranged from the crack surface along the crack depth direction to the bottom wall of the crack;

[0117] It also includes an auxiliary thermal layer 4 penetrating through the epoxy resin layer 1 , the thermoplastic sealing layer 2 and the base package growth layer 3 .

[0118] The thickness ratio of the epoxy resin layer 1 , the thermoplastic sealing layer 2 and the substrate packaging growth layer 3 is: 1:1:1.

[0119] The material of the base encapsulation growth layer 3 is a concrete crack inhibitor, and the preparation method of the concrete crack inhibitor comprises the following steps:

[0120] (1) Synthesis of β-cyclodextrin powder containing multiple double bonds: first disperse β-cyclodextrin in anhydrous dimethyl sulfoxide, and gradually add dropwise acryloyl chloride containing 10wt% mass...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water resistanceaaaaaaaaaa
Login to View More

Abstract

A repairing system for concrete cracks, comprising an epoxy resin layer, a thermoplastic sealing layer and a base encapsulation growth layer arranged sequentially from the crack surface along the depth direction of the crack to the bottom wall in the crack; layer, thermoplastic barrier layer, and auxiliary thermal layer for substrate encapsulation growth layer. The thickness ratio of the epoxy resin layer, the thermoplastic sealing layer and the substrate packaging growth layer is: 1:1:1. Combined with other parts, it effectively avoids the lack of shear strength, water resistance, and freeze-thaw resistance in the actual application of concrete crack inhibitors in the prior art, and thermal stress causes deformation and fission of the bottom wall in the concrete cracks, resulting in concrete cracks. Crack defects also appear on the bottom wall inside the crack.

Description

technical field [0001] The invention relates to the technical field of concrete crack repair, in particular to a repair system for concrete cracks. Background technique [0002] Concrete cracks are physical structural changes caused by internal and external factors of the concrete structure, and cracks are the main reason for the reduction of the bearing capacity, durability and water resistance of concrete structures. Part of the concrete structure plays a water-retaining role in the environment where it is located. When concrete cracks penetrate the backside and frontside, serious water leakage will occur. In some special places, it may cause major engineering accidents. [0003] In order to solve the problem of concrete cracks, what is generally adopted is to fill concrete crack inhibitors in the concrete cracks, and the preparation method of such concrete crack inhibitors comprises the following steps: [0004] (1) Synthesis of β-cyclodextrin powder containing multiple ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04G23/02C04B28/26C04B26/14C08B37/16C08F299/00C04B111/72
CPCE04G23/0203C04B28/26C04B26/14C08B37/0012C08F299/00C04B2111/72C04B2201/50C04B24/42C04B24/383C04B24/08C04B24/06C04B24/026C04B24/16C04B24/023C04B24/34C04B22/148C04B24/129C04B18/021C04B14/106C04B14/08C04B14/06C04B24/02C04B22/14C04B18/08
Inventor 甘季中曹万智杨永恒王洪镇郭启龙庞建利
Owner NORTHWEST UNIVERSITY FOR NATIONALITIES