A kind of ultra-fine grain size thin gauge high manganese high aluminum steel and production method

A technology of ultra-fine grain and production method, which is applied in the field of ultra-fine grain size and thin specification high-manganese and high-aluminum steel and production, can solve the problems of lack of large-scale production, complex production process, and long annealing time.

Active Publication Date: 2021-11-05
WUHAN UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

From the above description, it can be found that it still needs to be annealed for 4~13 hours after forging, resulting in long annealing time, complicated production process, and further improvement in production process
In addition, from the description of the patent, it can be seen that the steel is also a related experiment carried out under laboratory conditions, and does not have the conditions for large-scale production, and the strength and strength and plasticity of the steel are relatively low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-fine grain size thin gauge high manganese high aluminum steel and production method
  • A kind of ultra-fine grain size thin gauge high manganese high aluminum steel and production method
  • A kind of ultra-fine grain size thin gauge high manganese high aluminum steel and production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0045] The present invention is described in detail below:

[0046] Table 1 is the composition value list of each embodiment of the present invention and comparative example;

[0047] Table 2 is the list of main process parameters of each embodiment of the present invention and comparative examples;

[0048] Table 3 is the main performance list of each embodiment of the present invention and comparative examples;

[0049] Table 4 is a list of special mold powder parameters for each embodiment and comparative example of the present invention.

[0050] Each embodiment of the present invention is produced according to the following preparation methods:

[0051] 1) Smelting and continuous casting into slabs. During the casting process, the casting speed is controlled at 3.5~5.1m / min, and the thickness of the slabs is controlled at 52~70mm;

[0052] 2) Heating the billet in the tunnel furnace, controlling the heating temperature at 1183~1257°C, and the heating time at 25~41min; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

A high-manganese and high-aluminum steel with ultra-fine grain size and thin gauge, its composition and wt% are: C: 0.91~1.35%, Si: 0.21~0.53%, Mn: 8.5~16.2%, Al: 13.7~22.4% , Nb: 0.11~0.23%, V: 0.15~0.32%, P: ≤0.018%, S: ≤0.008%, N: ≤0.008%; production method: smelting and continuous casting into slab; heating the slab, descaling ; Finish rolling; Laminar cooling; Coiling; Natural cooling to room temperature; Cold rolling; Continuous annealing. The present invention fully refines the microstructure of the high-manganese and high-aluminum steel through reasonable composition and process control combined with Nb microalloying technology, and at the same time, under the joint action of strengthening methods such as precipitation strengthening of Nb and V microalloys , so that the yield strength of the high manganese and high aluminum steel is 1653~1721MPa, the tensile strength is 2035~2119MPa, the elongation is 52~62%, and the thickness is thinner; the annealing process is simpler and the annealing time is shorter.

Description

technical field [0001] The invention belongs to high-strength steel for automobiles and a production method thereof, in particular to a thin-gauge high-manganese and high-aluminum steel with an ultrafine grain size and a production method thereof. Background technique [0002] In recent years, with the sustained and rapid development of my country's automobile industry, the production and ownership of automobiles have continued to rise, which has played a positive role in promoting the development of the national economy. However, the energy consumption of automobiles also has a huge impact and pressure on the increasingly scarce energy conditions and deteriorating environmental conditions. At a time when energy saving and emission reduction are being paid more attention than ever, the automobile industry, which is a large energy consumer, undoubtedly attracts more attention. How to reduce vehicle energy consumption, in addition to measures such as small displacement and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/06C22C38/02C22C38/12C21D8/02C21D1/26
CPCC21D1/26C21D8/0226C21D8/0236C21D2211/001C21D2211/008C22C38/001C22C38/002C22C38/02C22C38/04C22C38/06C22C38/12
Inventor 甘晓龙万响亮徐光赵刚杨庚蔚刘升肖欢许耀文
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products