Wood crack repairing material for repairing wooden structure of ancient building big wood

A technology for repairing cracks and ancient buildings, applied in the direction of grafted polymer adhesives, adhesive types, adhesive additives, etc., can solve the problems of large logs losing their load-bearing function, prolonging the service life of large logs, and long construction duration, etc., to achieve Avoid re-expansion, reduce impact, excellent viscous effect

Inactive Publication Date: 2020-10-13
QINGHAI UNIV FOR NATITIES
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The principle in the restoration and protection of large trees in ancient buildings is not to destroy the main body of the large wood, as well as the reversibility and recognizability of the construction, to minimize the interference with the main body of the large wood, and to protect the original appearance and raw materials of the large wood as much as possible; Aging, wind and rain erosion, and building load-bearing can easily lead to cracks in the big wood. If it is not repaired in time, the big wood will lose its load-bearing function
Timely repair requires a repair material and process to better protect the large wooden components of ancient buildings, prolong the service life of the large wood, and avoid greater damage caused by cracks and irreparable losses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A wood crack repairing material for repairing large logs in ancient buildings is prepared from the following raw materials in parts by weight:

[0024] 40 parts of ASA resin; 16 parts of octyl phenolic tackifying resin; 8 parts of shell powder; 3 parts of perfluoroalkyl acrylic additives; 10 parts of trinonylphenyl phosphite; parts; 5 parts of additives.

[0025] In this embodiment, the additives are composed of leveling agent, drier, dispersant, film-forming aid PPH, flame retardant, and defoamer in a mass ratio of 0.3:0.4:0.3:0.3:0.4:0.3 Mix the proceeds.

Embodiment 2

[0027] A wood crack repairing material for repairing large logs in ancient buildings is prepared from the following raw materials in parts by weight:

[0028] 50 parts of ASA resin; 20 parts of octyl phenolic tackifying resin; 10 parts of shell powder; 5 parts of perfluoroalkyl acrylic additives; 12 parts of trinonylphenyl phosphite; parts; 7 parts of additives; 3 parts of pigments.

[0029] In this embodiment, the additives are composed of leveling agent, drier, dispersant, film-forming aid PPH, flame retardant, and defoamer in a mass ratio of 0.6:1:0.6:0.6:0.7:0.5 Mix the proceeds.

Embodiment 3

[0031] A wood crack repairing material for repairing large logs in ancient buildings is prepared from the following raw materials in parts by weight:

[0032] 45 parts of ASA resin; 18 parts of octyl phenolic tackifying resin; 9 parts of shell powder; 4 parts of perfluoroalkyl acrylic additives; 11 parts of trinonylphenyl phosphite; 4.5 parts of elastic silicone acrylic emulsion; 3 parts of bamboo fiber parts; 6 parts of additives; 1.5 parts of pigments.

[0033] In this embodiment, the additives are composed of leveling agent, drier, dispersant, film-forming aid PPH, flame retardant, and defoamer in a mass ratio of 0.45:0.7:0.45:0.45:0.55:0.4 Mix the proceeds.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of ancient building repairing, in particular to a wood crack repairing material for repairing a wooden structure of an ancient building. The wood crack repairing material is prepared from the following raw materials in parts by weight: 40-50 parts of ASA resin, 16-20 parts of octyl phenolic tackifying resin, 8-10 parts of shell powder, 3-5 parts of a perfluoroalkyl acrylic additive, 10-12 parts of trinonyl phenyl phosphite, 3-6 parts of an elastic silicone acrylic emulsion, 2-4 parts of bamboo fibers, 5-7 parts of an additive and 0-3 parts of pigment. The wood crack repairing material for repairing the wooden structure of the ancient building has excellent viscosity, weather resistance, corrosion resistance and strength, realizes repairing of wood cracks,well prevents re-expansion of the wood cracks, enables the repaired ancient building to be good in overall attractiveness, and reduces the influence on the original appearance of the ancient buildingas much as possible.

Description

technical field [0001] The invention relates to the field of ancient building restoration, in particular to a wood crack repairing material for repairing large logs of ancient buildings. Background technique [0002] The principle in the restoration and protection of large trees in ancient buildings is not to destroy the main body of the large wood, as well as the reversibility and recognizability of the construction, to minimize the interference with the main body of the large wood, and to protect the original appearance and raw materials of the large wood as much as possible; Aging, wind and rain erosion, and building load-bearing can easily lead to cracks in the big wood. If it is not repaired in time, the big wood will lose its load-bearing function. Timely repair requires a repair material and technology to better protect the large wooden components of ancient buildings, prolong the service life of the large wood, and avoid greater damage caused by cracks and irreparabl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J151/04C09J11/08C09J11/04C09J11/06
CPCC08K2003/265C08L2205/035C08L2205/16C09J11/04C09J11/06C09J11/08C09J151/04C08L61/06C08L43/04C08L97/02C08K3/26C08K5/526
Inventor 李双营
Owner QINGHAI UNIV FOR NATITIES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com