Moisture-permeable cotton-padded clothes

A cotton-padded garment and moisture-permeable technology, which is applied in the field of clothing, can solve the problems of poor moisture-permeability of the lining, and achieve the effects of improved moisture-permeable performance, high coating rate, and good washability

Inactive Publication Date: 2020-10-20
温州厚德服饰有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problem of poor moisture permeability of the cotton lining in the prior art, the purpose of the present invention is to provide a moisture permeable cotton garment, which has the advantage of good moisture permeability of the inner lining

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisture-permeable cotton-padded clothes
  • Moisture-permeable cotton-padded clothes
  • Moisture-permeable cotton-padded clothes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A moisture-permeable cotton coat, such as figure 1 As shown, it includes an outer layer 1, a filling layer 2 and an inner lining layer 3, the outer layer 1 is made of PU coated polyester, the filling layer 2 is cotton, and the inner lining layer 3 is made of treated polyester fabric.

[0035] The processing process of polyester fabric is as follows:

[0036] The first step is to immerse the polyester fabric in the alkali treatment solution with a bath ratio of 1:20, heat up to 50°C, take it out after 10 minutes, wash it with water, and dry it for later use. The alkali treatment solution includes 15g / L sodium hydroxide and 6g / L 30wt% hydrogen peroxide , 3g / LOP-10, the balance is water;

[0037] In the second step, immerse the polyester fabric treated in the first step in the amine treatment solution, the bath ratio is 1:20, heat up to 70°C, take it out after 20 minutes, wash it with water, and dry it for later use. The amine treatment solution includes 20g / L ethanolamin...

Embodiment 2

[0041] A moisture-permeable cotton coat, such as figure 1 As shown, it includes an outer layer 1, a filling layer 2 and an inner lining layer 3, the outer layer 1 is made of PU coated polyester, the filling layer 2 is cotton, and the inner lining layer 3 is made of treated polyester fabric.

[0042] The processing process of polyester fabric is as follows:

[0043] The first step is to immerse the polyester fabric in an alkali treatment solution with a bath ratio of 1:20, heat up to 60°C, take it out after 15 minutes, wash it with water, and dry it for later use. The alkali treatment solution includes 20g / L sodium hydroxide and 8g / L 30wt% hydrogen peroxide , 5g / LOP-10, the balance is water;

[0044] In the second step, immerse the polyester fabric treated in the first step in the amine treatment solution, the bath ratio is 1:20, heat up to 80°C, take it out after 30 minutes, wash it with water, and dry it for later use. The amine treatment solution includes 25g / L ethanolamine...

Embodiment 3

[0048] A moisture-permeable cotton coat, such as figure 1 As shown, it includes an outer layer 1, a filling layer 2 and an inner lining layer 3, the outer layer 1 is made of PU coated polyester, the filling layer 2 is cotton, and the inner lining layer 3 is made of treated polyester fabric.

[0049] The processing process of polyester fabric is as follows:

[0050]The first step is to immerse the polyester fabric in the alkali treatment solution with a bath ratio of 1:20, heat up to 55°C, take it out after 12 minutes, wash it with water, and dry it for later use. The alkali treatment solution includes 18g / L sodium hydroxide and 7g / L 30wt% hydrogen peroxide , 4g / LOP-10, the balance is water;

[0051] In the second step, immerse the polyester fabric treated in the first step in the amine treatment solution, the bath ratio is 1:20, heat up to 75°C, take it out after 25 minutes, wash it with water, and dry it for later use. The amine treatment solution includes 23g / L ethanolamine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of clothes, and particularly discloses moisture-permeable cotton-padded clothes. The cotton-padded clothes comprise an outer surface layer, a filling layer and a lining layer, the lining layer is made of treated polyester fabric, and the treatment process of the polyester fabric comprises the following steps of 1, immersing the polyester fabric in an alkali treatment solution, heating to 50-60 DEG C, keeping the temperature for 10-15 minutes, taking out, washing with water, and drying for later use; 2, immersing the polyester fabric treated in the step 1 in the amine treatment solution, heating to 70-80 DEG C, keeping the temperature for 20-30 minutes, taking out, washing with water, and drying for later use; 3, immersing the polyester fabric treated in the step 2 in a reaction solution, heating to 100-110 DEG C for 1-2 hours, taking out the polyester fabric, then immersing the polyester fabric in hot water at 60-70 DEG C for 8-15 minutes, and finallywashing and drying the polyester fabric; and 4, immersing the polyester fabric treated in the step 3 in a fibroin finishing solution, carrying out two-time immersion and two-time rolling, carrying out pre-drying at 70-80 DEG C for 3-5 minutes, carrying out baking at 130-140 DEG C for 30-50 seconds, washing with water, and drying. The cotton-padded clothes have the advantages that the lining layeris good in moisture absorption and moisture permeability, and the cotton-padded clothes are comfortable to wear.

Description

technical field [0001] The invention relates to the field of clothing, more specifically, it relates to a moisture-permeable cotton coat. Background technique [0002] Cotton clothes refer to clothing filled with cotton, down and other materials as fillings to keep out the cold. Cotton can absorb a lot of air, and air is a poor conductor of heat, which is not easy to produce heat exchange, so cotton clothes have excellent warmth retention effect. The inner lining of the cotton jacket is made of polyester fabric, and the outer layer of the cotton jacket is often a waterproof coated fabric. [0003] The cotton-padded lining made of polyester fabric has the following advantages: 1. It is smooth and free of static electricity, and it is quick and convenient for people to put on and take off the cotton-padded clothes; 2. It is wear-resistant and has high strength and long service life. But polyester is a typical hydrophobic fiber, with only one hydroxyl group at each end of its...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M14/14D06M15/15D06M13/123D06M11/155D06M13/207D06M13/148D06M11/38D06M11/50D06M13/368D06M11/76D06M11/65A41D3/00A41D31/02A41D31/12A41D31/04A41D27/02B32B9/02B32B9/04B32B27/36D06M101/32
CPCD06M14/14D06M15/15D06M13/123D06M11/155D06M13/207D06M13/148D06M11/38D06M11/50D06M13/368D06M11/76D06M11/65A41D3/00A41D31/02A41D31/125A41D31/04A41D27/02B32B9/02B32B9/04B32B27/36D06M2101/32D06M2200/11
Inventor 林巧黄丽娜
Owner 温州厚德服饰有限公司