Preparation process of glass with scratch-resistant crystal diamond flash point effect

A preparation process and anti-scratch technology, which is applied in the field of preparation process of glass with anti-scratch crystal diamond flash point effect, which can solve the problems of easy scratch, short life cycle, easy aging of glass, etc.

Active Publication Date: 2020-10-30
ZHENGZHOU HIHO OPTICAL TECH CO LTD
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]With the substantial improvement of people's living standards, people's demand for furniture decoration, business space partitions, etc. has also been improved. It has a scratch-resistant crystal diamond flash point The demand for effect glass has increased significantly, but in the field of decorative glass production,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of glass with scratch-resistant crystal diamond flash point effect
  • Preparation process of glass with scratch-resistant crystal diamond flash point effect

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1. Prepare crystal diamond flash point effect glass etching solution (wt%) according to the following formula: NH 4 HF 2 22.3%, NaF 15.8%, HCL13.6%, HNO 3 11.8%, K 2 HPO 3 4.5%, NaNO 3 3.5%, (NH 4 ) 2 SiF 6 0.6%, sodium alkylbenzene sulfonate 0.3%, viscosity modifier 4.7%, H 2 O 22.9%; Add the above-mentioned raw materials in sequence according to the etching process requirements, and then fully stir evenly to present a uniform and stable supersaturated solution state, and leave it to mature for 36-72 hours at room temperature to obtain a satisfactory etching solution. You can start the etching treatment of the anti-scratch crystal diamond flash point effect glass of the original glass sheet;

[0018] 2. Use anti-etching ink to protect the side of the original glass that does not need to be etched;

[0019] 3. Clean the side of the original glass sheet that needs to be etched with the pretreatment solution, and put it into the etching solution in a wet state...

Embodiment 2

[0023] 1. Prepare crystal diamond flash point effect glass etching solution (wt%) according to the following formula: NH 4 HF 2 24.1%, NaF 15.3%, HCL13.6%, HNO 3 12.6%, K 2 HPO 3 4.2%, NaNO 3 3.5%, (NH 4 ) 2 SiF 6 0.5%, sodium alkylbenzene sulfonate 0.3%, viscosity modifier 5.1%, H 2 O 20.8%; Add the above-mentioned raw materials in turn according to the etching process requirements, and then fully stir evenly to present a uniform and stable supersaturated solution state, and leave it to mature for 36-72 hours at room temperature to obtain a satisfactory etching solution. You can start the etching treatment of the anti-scratch crystal diamond flash point effect glass of the original glass sheet;

[0024] 2. Use anti-etching ink to protect the side of the original glass that does not need to be etched;

[0025] 3. Clean the side of the original glass sheet that needs to be etched with the pretreatment solution, and put it into the etching solution in a wet state for ...

Embodiment 3

[0029] 1. Prepare crystal diamond flash point effect glass etching solution (wt%) according to the following formula: NH 4 HF 2 23.8%, NaF 15.2%, HCL14.2%, HNO 3 12.7%, K 2 HPO 3 4.5%, NaNO 3 3.2%, (NH 4 ) 2 SiF 6 0.6%, sodium alkylbenzene sulfonate 0.3%, viscosity modifier 4.5%, H 2 O 22.0%; add the above-mentioned raw materials in sequence according to the etching process requirements, and then fully stir evenly to present a uniform and stable supersaturated solution state, and leave it to mature at room temperature for 36-72 hours to obtain a special etching solution that meets the requirements , you can start the etching treatment of the anti-scratch crystal diamond flash point effect glass of the original glass sheet;

[0030] 2. Use anti-etching ink to protect the side of the original glass that does not need to be etched;

[0031] 3. Clean the side of the original glass sheet that needs to be etched with the pretreatment solution, and put it into the etching ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of etched glass, and in particular, relates to a preparation process of glass with a scratch-resistant crystal diamond flash point effect. The process comprises the following steps: preparing etching liquid and carrying out etching treatment on a raw glass sheet; depending on a fact that fluoride has an etching effect on glass, carrying out multi-stagechemical reaction with the surface of the glass in acid liquor with certain concentration and type; and generating a nanoscale diamond-shaped microcrystalline particle adhesion layer, and uniformly distributing on the whole glass surface. Therefore, the visual effect of glittering in the light facing process is achieved; meanwhile, the excellent properties of reflection light resistance, scratch resistance, dust resistance, fingerprint resistance and the like are realized; the process is simple and practical, easy to operate and low in cost, microcrystalline diamond particles on the surface ofthe prepared scratch-resistant crystal diamond flash point effect glass are uniform in distribution and consistent in size, and the technical indexes such as roughness, glossiness, light transmittance and haze meet the specific requirements of the art decorative glass industry.

Description

technical field [0001] The invention belongs to the technical field of chemical etching of anti-scratch crystal diamond flash point effect glass, and in particular relates to a preparation process of glass with anti-scratch crystal diamond flash point effect. Background technique [0002] With the substantial improvement of people's living standards, people's demand for furniture decoration, business space partitions, etc. has also been improved. It is the combination of spraying resin and metal glitter powder to achieve the crystal diamond flash point effect on the glass surface. The crystal diamond flash point effect glass achieved by this physical spraying process has the disadvantages of easy aging, scratching, poor adhesion, Defects such as short life cycle. Contents of the invention [0003] The purpose of the present invention is to provide a preparation process for glass with anti-scratch crystal diamond flash point effect. The developed anti-scratch crystal diamo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C15/00C09K13/08
CPCC03C15/00C09K13/08Y02P40/57
Inventor 熊国祥
Owner ZHENGZHOU HIHO OPTICAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap