Method for preventing rare earth steel continuous casting nozzle from being blocked

A continuous casting nozzle and rare earth technology, which is applied in casting equipment, casting melt containers, manufacturing tools, etc., to reduce labor pressure and cost, ensure high purity, and solve the effect of nozzle blockage

Active Publication Date: 2020-11-17
SHANDONG IRON & STEEL CO LTD
View PDF11 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the problem that nozzle nodules and clogging are prone to occur in continuous casting when producing rare earth-containing steel grades, the present invention provides a method for preventing the clogging of the rare earth steel continuous casting nozzle, and better solves the problem of the continuous casting nozzle clogging of the rare earth steel. Improve production efficiency and ensure smooth production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preventing rare earth steel continuous casting nozzle from being blocked
  • Method for preventing rare earth steel continuous casting nozzle from being blocked
  • Method for preventing rare earth steel continuous casting nozzle from being blocked

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Such as Figure 1-3 As shown, the device used in the embodiment of the present invention to prevent the clogging of the rare earth steel continuous casting nozzle includes a heating rod 10 and a heating cylinder 11; the heating rod 10 is placed at the center of the stopper rod 4, and the stopper rod 4 is placed in the tundish 3, the tundish 3 is connected to the crystallizer 6 through the submerged nozzle 5, and the outside of the submerged nozzle 5 is covered by the heating cylinder 11, which is composed of two semicircular heating cylinders spliced ​​together. The diameter of the heating rod 10 is 30-60 mm, and both the heating rod 10 and the heating cylinder 11 are electric heating elements of molybdenum disilicide.

[0031] A method for preventing the clogging of the rare earth steel continuous casting nozzle described in the embodiment of the present invention is smelted in a 50 t electric furnace to produce the rare earth bearing steel GCr15Re as an example. The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of continuous casting equipment, and particularly relates to a method for preventing a rare earth steel continuous casting nozzle from being blocked. The method comprises the following steps that 1, a stopper rod is heated at the beginning of continuous casting, and the heating temperature is kept higher than the temperature of tundish molten steel; meanwhile, a submersed nozzle is heated, and the heating temperature is kept higher than the temperature of tundish molten steel; 2, when the position of the stopper rod rises, namely, the nozzle is nodulated or blocked, the heating temperature of the stopper rod and the submersed nozzle is increased, and if the stopper rod continues rising, the heating temperature of the stopper rod and the submersed nozzle continues to be increased; and 3, after the stopper rod returns, the stopper rod and the submersed nozzle are cooled and adjusted back to the initial set temperature. According to the method,the easily-blocked parts of the nozzle and the stopper rod can be heated, the temperature of the parts is increased, the viscosity of rare earth inclusions is reduced, the fluidity of the rare earthinclusions is improved, and a good effect of improving nozzle nodulation and blockage is achieved.

Description

technical field [0001] The invention belongs to the technical field of continuous casting equipment, and in particular relates to a method for preventing the clogging of a rare earth steel continuous casting nozzle. Background technique [0002] In the process of steel smelting, rare earth can play the role of microalloying, interaction with harmful elements, desulfurization and deoxidation, hydrogen capture, dispersion hardening and deformation inclusions. At the same time, rare earth has an important impact on the properties of steel. However, in the smelting process of rare earth-containing steel, rare earth can modify oxygen and sulfide inclusions, that is, generate rare earth oxysulfide, such as rare earth Ce in bearing steel will generate CeAlO 3 、Ce 2 o 2 S. Ce 2 o 3 、Ce 3 o 4 , the MnS inclusions in the steel will transform into rare earth sulfide composite inclusions, and the overall inclusions are spherical in shape and smaller in size. These rare earth oxid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D41/60B22D11/14
CPCB22D41/60B22D11/14
Inventor 许荣昌韩杰何毅陈良刘成宝王毅孙宗辉刘志刚邵正伟
Owner SHANDONG IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products