Production process of special glass fiber cloth for thermoplastic glass fiber reinforced PP composite material

A glass fiber cloth and glass fiber technology, applied in the field of fiber cloth, can solve the problems of low production efficiency, low strength and high cost, and achieve the effects of improving production efficiency, simplifying molding process and reducing production cost

Inactive Publication Date: 2020-11-17
CHANGZHOU TIANMA GROUP CO LTD
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the thermoplastic glass fiber reinforced PP composite material produced by the above process has a wide range of uses, it has the defects of low strength, low production efficiency and high cost, which will adversely affect the popularization and application of the product, especially In the context of the increasingly large-scale and complex structures of the products, higher requirements are placed on the strength of the products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] 1. Preparation of blended fiber yarn: Add a PP yarn unwinding device on the special hearth of the alkali-free glass fiber pool kiln drawing production line. During the process of drawing glass fiber roving, according to glass fiber: PP fiber = 6:4 ( Fluctuate up and down ± 10%) ratio design yarn number, wind PP yarn and non-alkali glass fiber thermoplastic roving together to form, then dry and shape under the condition of 180±2℃, 60±1min, to get the required no-twisted roving Alkali glass fiber and PP yarn blended fiber yarn, the specifications of the alkali-free glass fiber and PP yarn blended fiber yarn are as follows: the total yarn number is 800±40tex, the winding ratio is 7.2, the package is 17±1.0kg, the oil content ( Glass fiber) is 0.55±0.15%;

[0015] 2. Preparation of glass fiber cloth: put the above-mentioned non-alkali glass fiber and PP yarn blended fiber yarn on the warping creel, after all the yarns are discharged, stick them with adhesive tape, and wind ...

Embodiment 2

[0019] The production process of this embodiment is as follows:

[0020] 1. Preparation of blended fiber yarn: Add a PP yarn unwinding device on the special hearth of the alkali-free glass fiber pool kiln drawing production line. During the process of drawing glass fiber roving, according to glass fiber: PP fiber = 6:4 ( Fluctuate up and down ± 10%) ratio design yarn number, wind PP yarn and non-alkali glass fiber thermoplastic roving together to form, and then set the shape under the condition of 180±2℃, 60±1min, to obtain the required alkali-free glass Fiber and PP yarn blended fiber yarn, the specifications of the alkali-free glass fiber and PP yarn blended fiber yarn are as follows: the total yarn number is 1870±93tex, the winding ratio is 6.4, the package is 17±1.0kg, the oil content (glass fiber ) is 0.55±0.15%;

[0021] 2. Preparation of glass fiber cloth: put the above-mentioned blended fiber yarn on the warp creel, stick all the yarns with adhesive tape after being d...

Embodiment 3

[0024] The production process of this embodiment is as follows:

[0025] 1. Preparation of blended fiber yarn: Add a PP yarn unwinding device on the special hearth of the alkali-free glass fiber pool kiln drawing production line. During the process of drawing glass fiber roving, according to glass fiber: PP fiber = 6:4 ( Fluctuate up and down ± 10%) ratio design yarn number, wind PP yarn and non-alkali glass fiber thermoplastic roving together to form, and then set the shape under the condition of 180±2℃, 60±1min, to obtain the required alkali-free glass Fiber and PP yarn blended fiber yarn, the specifications of the alkali-free glass fiber and PP yarn blended fiber yarn are as follows: the total yarn number is 3650±5%tex, the winding ratio is 4.2, the package is 17±1.0kg, the oil content ( Glass fiber) is 0.55±0.15%;

[0026] 2. Preparation of glass fiber cloth: put the above-mentioned blended fiber yarn on the warp creel, stick all the yarns with adhesive tape after being d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production process of special glass fiber cloth for a thermoplastic glass fiber reinforced PP composite material, and relates to the technical field of fiber cloth. A PP yarnwinding and unwinding device is additionally arranged on a special furnace platform for an alkali-free glass fiber tank furnace wiredrawing production line, during drawing of glass fiber rovings, winding and forming are carried out on PP yarns and the alkali-free glass fiber thermoplastic rovings according to the ratio of 6:4 of glass fibers to PP fibers, and then drying and shaping are carried out to obtain required alkali-free glass fiber and PP yarn blended fiber yarns; the alkali-free glass fibers and PP yarn blended fiber yarns are put on a warping creel, all the yarns are bonded by using an adhesive tape after the yarns are arranged, the yarns are wound on a warp beam with the breadth of 2220+/-10 mm, and drafting, denting, beaming and weaving are sequentially carried out on the warp beam according to the twill weave of 2/2 or 1/3 to prepare fiber cloth; and post-processing is carried out. According to the production process, the production cost is reduced, the production process is simplified, the product strength is improved, and large-scale production is facilitated.

Description

technical field [0001] The invention relates to the technical field of fiber cloth, in particular to a production process of glass fiber cloth special for thermoplastic glass fiber reinforced PP composite materials. Background technique [0002] Thermoplastic materials refer to the characteristics of materials that soften when heated and harden when cooled. Compared with thermosetting materials, they become soft and flow when heated, and harden when cooled. This process is reversible and can be repeated, so it has the effect of repeated use. Among them, thermoplastic glass fiber reinforced PP is a widely used material. [0003] The existing thermoplastic glass fiber reinforced PP composite material is a composite material in which thermoplastic glass fibers are chopped into 0.2-7mm and evenly distributed in the PP matrix. Its production process is divided into two processes: granulation and molding. Pelletization is to heat and mix thermoplastic glass fibers with PP particl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/30D03D15/00D02G3/04D03D13/00D02G3/18B29K23/00
CPCB29C70/30B29K2023/12D02G3/04D02G3/18D03D13/002D10B2321/022
Inventor 宣维栋朱忠裕张从勇李总
Owner CHANGZHOU TIANMA GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap