Manufacturing process of fully-glazed Jianzhan

A technology for making crafts and building cups, which is applied in the field of making all-inclusive glaze pots. It can solve the problems of non-display of partridge crystal patterns, low yield rate, and dim patterns, etc., and achieve high artistic value, appreciation value, and yield rate. High, clear streak effect

Pending Publication Date: 2020-12-11
福建省鼎吉建盏陶瓷有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In addition, the existing partridge spot Jianzhan is often prone to defects such as non-display or unclear crystal pattern of partridge spot, dim pattern, etc., and the yield is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process of fully-glazed Jianzhan
  • Manufacturing process of fully-glazed Jianzhan
  • Manufacturing process of fully-glazed Jianzhan

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The manufacturing process of all-inclusive glaze Jianzhan includes the following steps:

[0041] (1) preparing green body and glaze slurry;

[0042] The green body is prepared by the following method: mix red clay and pear puree by equal weight, add water to wash, pass through an 80-mesh sieve, press filter, stale for 5 years, smelt, and pull the green body to form a green body, dry it, and then repair the green body Molded, dried again and bisque fired to obtain the green body;

[0043] The biscuit firing is that the temperature of the kiln rises to 850° C. after 8 hours, and the furnace is stopped for cooling.

[0044] Wherein, the laterite and pear mud are all taken from Dali Village, Shuiji Town, Jianyang District, Nanping City, Fujian Province; the Dali Mud is the mud on the mountain of Dali Village;

[0045] The glaze slurry is prepared by the following method: mix 75 parts by weight of glaze ore, 15 parts by weight of plant ash, 1.8 parts by weight of iron red,...

Embodiment 2

[0059] The manufacturing process of all-inclusive glaze Jianzhan includes the following steps:

[0060] (1) preparing green body and glaze slurry;

[0061] The green body is prepared by the following method: mix red clay and pear puree by equal weight, add water to wash, pass through a 90-mesh sieve, press filter, stale for 5.5 years, smelt, pull the green body into a green body, dry it, and then repair the green body Molded, dried again and bisque fired to obtain the green body;

[0062] The biscuit firing is that the temperature of the kiln rises to 800° C. after 6 hours, and the furnace is stopped for cooling.

[0063] Wherein, the laterite and pear mud are all taken from Dali Village, Shuiji Town, Jianyang District, Nanping City, Fujian Province; the Dali Mud is the mud on the mountain of Dali Village;

[0064] The glaze slurry is prepared by the following method: take 75 parts by weight of glaze ore, 15 parts by weight of plant ash, 2 parts by weight of iron red, and 8....

Embodiment 3

[0076] The manufacturing process of all-inclusive glaze Jianzhan includes the following steps:

[0077] (1) preparing green body and glaze slurry;

[0078] The green body is prepared by the following method: mix red clay and pear puree by equal weight, add water to wash, pass through an 80-mesh sieve, press filter, stale for 4.5 years, smelt, pull the green body into a green body, dry it, and then repair the green body Molded, dried again and bisque fired to obtain the green body;

[0079] The biscuit firing is that the temperature of the kiln rises to 800° C. after 7 hours, and the furnace is stopped for cooling.

[0080] Wherein, the laterite and pear mud are all taken from Dali Village, Shuiji Town, Jianyang District, Nanping City, Fujian Province; the Dali Mud is the mud on the mountain of Dali Village;

[0081] The glaze slurry is prepared by the following method: take 75 parts by weight of glaze ore, 14 parts by weight of plant ash, 2 parts by weight of iron red, and 9...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing process of a full-glazed Jianzhan. The process comprises the following steps: preparing a green body and glaze slip, glazing, putting the glazed green body intoan electric kiln, roasting, cooling, and discharging. According to the prepared full-glaze-coated Jianzhan, glaze does not flow to adhere to the bottom, the full-glaze-coated Jianzhan is fleshy, plump and right in coverage, the green and black glaze bottom color is provided with yellowish-brown partridge spot oil drops, the partridge spot oil drops are in oval water drop shapes and have feather-shaped grains, the stripes are clear and well-arranged, the mouth edge is golden and glossy, and the prepared full-glaze-coated Jianzhan has extremely high artistic value and appreciation value.

Description

technical field [0001] The invention relates to the technical field of porcelain, and in particular relates to a manufacturing process of all-inclusive glazed Jianzhan. Background technique [0002] Black-glazed porcelain is a strange flower in the history of Chinese ceramics, well-known at home and abroad. Jianzhan is a typical representative of black-glazed porcelain. The colorful light phenomenon of Jianzhan is natural, mysterious and refined, and the markings of Jianzhan have obvious three-dimensional and layered feelings. What Jianzhan pursues is the artistic effect formed naturally. Its glaze pattern is not artificially painted, but formed under strict formula technology, special firing atmosphere and firing temperature curve. The three are indispensable. The artistic effect formed by Jianzhan has no sense of artificial carving at all, and it is completely a display of the essential beauty of its products. [0003] Jianzhan has a special process, which belongs to iro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C04B33/04C04B33/34C03C8/00C04B41/86
CPCC03C8/00C04B33/04C04B33/13C04B33/34C04B41/5022C04B41/86C04B2235/6567C04B2235/661
Inventor 杨敏
Owner 福建省鼎吉建盏陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com