High-wear-resistance cold roll and preparation method thereof

A cold roll, high wear-resistant technology, applied in the direction of roll, metal rolling, metal rolling, etc., can solve the problems of high-strength steel rolling deformation resistance, reduce unit production efficiency, roll wear and other problems, and achieve excellent wear resistance , The formula is scientific and rigorous, and the effect of increasing wear resistance

Inactive Publication Date: 2020-12-18
YIXING YONGCHANG ROLL
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

High-strength steel has high resistance to rolling deformation, and the corresponding wear on the rolls is also serious. If the rolls are replaced frequently, the production efficiency of the unit will be greatly reduced and the output will be affected.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The mass percentage is 1.00% C, 0.01% N, 3.00% Cr, 2.00% Mo, 1.00% V, 0.10% Ti, 0.50% Si and 0.50% Mn, and the rest is Fe. Through traditional methods, sequentially (1) electric furnace smelting; (2) casting electrode rod; (3) electroslag remelting; (4) forging; (5) preliminary heat treatment; (6) final heat treatment; (7) machining to finished product .

Embodiment 2

[0017] The mass percentage is 2.00% C, 0.20% N, 6.00% Cr, 4.00% Mo, 3.00% V, 1.00% Ti, 2.00% Si and 1.50% Mn, and the rest is Fe. Through traditional methods, sequentially (1) electric furnace smelting; (2) casting electrode rod; (3) electroslag remelting; (4) forging; (5) preliminary heat treatment; (6) final heat treatment; (7) machining to finished product .

Embodiment 3

[0019] The mass percentage is 1.20% C, 0.01% N, 3.50% Cr, 3.00% Mo, 2.00% V, 0.20% Ti, 1.00% Si and 1.00% Mn, and the rest is Fe. Through traditional methods, sequentially (1) electric furnace smelting; (2) casting electrode rod; (3) electroslag remelting; (4) forging; (5) preliminary heat treatment; (6) final heat treatment; (7) machining to finished product .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-wear-resistance cold roll. The high-wear-resistance cold roll comprises the following components of, in percentage by mass, 1.00%-2.00% of C, 0.01%-0.20% of N, 3.00%-6.00% of Cr, 2.00%-4.00% of Mo, 1.00%-3.00% of V, 0.10%-1.00% of Ti, 0.50%-2.00% of Si, 0.50%-1.50% of Mn and the balance of Fe and inevitable impurities. Meanwhile, the invention further discloses a preparation method of the high-wear-resistance cold roll. Compared with the prior art, the formula is more scientific and rigorous, and the impurity content is low; the preparation method is scientific,simple, low in energy consumption and less in pollution; and the high-wear-resistance cold roll prepared by the preparation method forms a large amount of uniformly distributed nitrides and carbides of Ti, V and Mo, and the nitrides and carbides are used as wear-resistant particles to increase the wear resistance of the material.

Description

technical field [0001] The invention belongs to the field of roll cold treatment, and in particular relates to a high wear-resistant cold roll and a preparation method thereof. Background technique [0002] The roll is an important part in metal rolling, how to improve the service life of the roll and the surface quality of the rolled product is an important subject in the field of metal rolling. During the rolling process of metal, rolling deformation heat, friction heat, heat of the rolled piece itself will cause the surface temperature of the roll to rise, which will cause surface thermal cracks, oxidation, and roll breakage of the roll. Therefore, in order to improve the service life of the roll and the roll is properly cooled, it is one of the important measures in the field of metal rolling. [0003] The cooling technology of the roll surface can usually be divided into two types: internal cooling technology and external cooling technology. Both of these cooling metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/36C22C38/22C22C38/24C22C38/28C22C38/34C22C38/04C22C38/02B21B27/02
CPCB21B27/02C22C38/001C22C38/02C22C38/04C22C38/22C22C38/24C22C38/28C22C38/34C22C38/36
Inventor 陈彬陈刚石跃军
Owner YIXING YONGCHANG ROLL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com