Purple blue glaze for manufacturing Jun pottery and preparation method of purple blue glaze

A purple-blue and formula technology, applied in the field of ceramic materials, can solve the problems of single color, influence of soil viscosity, different color and luster, etc., and achieve the effect of scientific formula, high glaze water stability and low raw material cost.

Pending Publication Date: 2021-01-05
WUXI TAIHU UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the color of traditional Jun pottery is relatively simple, mostly yellow and blue. The viscosity will be affected, and if the color mud is piled on the green body and then colored, it will cause different colors after firing, so the existing pigments are not suitable for uniform pottery.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Get the feldspar of 40 parts by weight, the kaolin of 5 parts, the quartz of 1 part, the limestone of 10 parts, the talcum of 1 part, the iron oxide of 0.1 part and the magnesium carbonate of 0.1 part stand-by; The feldspar, kaolin, Quartz, limestone, and talc are mixed, and the mixed material is ball-milled for 8 hours by dry ball milling; the material after dry ball milling is mixed with iron oxide and magnesium carbonate in a formula amount for 5 minutes; the resulting mixed material is mixed with water according to Mix at a weight ratio of 1:1 and stir for 30 minutes.

Embodiment 2

[0014] Get the feldspar of 60 parts by weight, the kaolin of 10 parts, the quartz of 10 parts, the limestone of 20 parts, the talcum of 5 parts, the iron oxide of 2 parts and the magnesium carbonate of 1 part stand-by; The feldspar, kaolin, Quartz, limestone, and talc are mixed, and the mixed material is ball-milled for 12 hours by dry ball milling; the dry-milled material is mixed with iron oxide and magnesium carbonate in a formula amount for 10 minutes; the resulting mixed material is mixed with water according to Mix at a weight ratio of 1: 3 and stir for 40 minutes.

Embodiment 3

[0016] Get the feldspar of 50 parts by weight, the kaolin of 8 parts, the quartz of 7 parts, the limestone of 15 parts, the talcum of 3 parts, the iron oxide of 1 part and the magnesium carbonate of 0.5 part stand-by; The feldspar, kaolin, Quartz, limestone, and talc are mixed, and the mixed material is ball-milled for 10 hours by dry ball milling; the dry ball-milled material is mixed with iron oxide and magnesium carbonate in the formula for 8 minutes; the resulting mixed material is mixed with water according to Mix at a weight ratio of 1:2 and stir for 30-40 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses purple-blue glaze for manufacturing Jun pottery. The purple-blue glaze is prepared from the following components in parts by weight: 40-60 parts of feldspar, 5-10 parts of kaolin, 1-10 parts of quartz, 10-20 parts of limestone, 1-5 parts of talc, 0.1-2 part of ferric oxide and 0.1-1 part of magnesium carbonate. Meanwhile, the invention further discloses a preparation methodof the purple-blue glaze for manufacturing the Jun pottery. Compared with the prior art, the invention has the advantages of scientific formula, low raw material cost and high glaze water stability,and can display purple blue which is different from the traditional uniform glaze in blue and yellow.

Description

technical field [0001] The invention belongs to the field of ceramic materials, and in particular relates to a purple-blue glaze used for uniform pottery production and a preparation method thereof. Background technique [0002] The most representative traditional decoration technique in the production process of Jun pottery is "stacking flowers". It depends on the skill of the artist's thumb to pile up the color mud on the body to present different pictures such as flowers and birds, landscapes, etc., which has a strong national style and folk style. Artistic features. However, the color of traditional Jun pottery is relatively simple, mostly yellow and blue. The viscosity of the pottery will be affected, and if the color mud is piled on the green body and then colored, it will cause different colors after firing, so the existing pigments are not suitable for uniform pottery. Contents of the invention [0003] Purpose of the invention: The purpose of the present inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/86C04B41/5022
Inventor 方薛斐张丽方卫明
Owner WUXI TAIHU UNIV