Dyeing and finishing process of superfine fiber fabric capable of quickly wicking sweat
A microfiber and fabric technology, applied in the field of elastic fabrics, can solve the problems of weakened water absorption and quick-drying effects, and achieve the effects of making up for poor color fastness, reducing floor space, and maintaining slack
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022]Example 1
[0023]A dyeing and finishing process for superfine fiber fabrics includes the following steps:
[0024]S1 weaving process: weaving the superfine fiber fabric into a single-sided weft-knitted plain weave structure through a weaving machine;
[0025]S2 Pre-shape: Pre-shape the superfine fiber fabric after washing, the setting temperature is 150℃, and the setting cloth speed is 12m / min;
[0026]S3 pre-treatment: immerse the pre-shaped microfiber fabric in 30℃ hot water, add the refined degreasing agent Dyamul SORnew and penetrant JFC, heat it up to 80℃ and keep it for 10 minutes, then wash it and cool it down to 20℃, and wait for dyeing ;
[0027]S4 dyeing: Place the superfine fiber fabric in a relaxed state for 5 hours, and send it to the overflow dyeing machine with 2g / L dye and 0.4g / L acid leveling agent for dyeing, and increase the dyeing machine’s temperature at 2℃ / min Keep the temperature at 85℃ for 3min, then heat up at 1℃ / min to 90℃ for 5min, then at 1.5℃ / min to 110℃ for 30m...
Example Embodiment
[0031]Example 2
[0032]S1 weaving process: weaving the superfine fiber fabric into a single-sided weft-knitted plain weave structure through a weaving machine;
[0033]S2 Pre-shape: Pre-shape the washed superfine fiber fabric, the setting temperature is 155℃, and the setting cloth speed is 12-15m / min;
[0034]S3 pre-treatment: immerse the pre-shaped microfiber fabric in hot water at 32°C, add refined degreasing agent Dyamul SORnew and penetrant JFC, heat it up to 80°C and keep it warm for 13 minutes, then wash with water and cool it down to 22°C before dyeing ;
[0035]S4 dyeing: put the superfine fiber fabric in a relaxed state for 6 hours, and send it to the overflow dyeing machine, adding 2g / L dye and 0.5g / L acid leveling agent for dyeing, and raise the dyeing machine at 2℃ / min Keep the temperature at 85℃ for 3min, then heat up at 1℃ / min to 90℃ for 5min, then at 1.5℃ / min to 110℃ for 30min, finally at 1.5℃ / min to 50℃ for reduction cleaning, and then wash again Among them, 98% glacial acetic ...
Example Embodiment
[0039]Example 3
[0040]S1 weaving process: weaving the superfine fiber fabric into a single-sided weft-knitted plain weave structure through a weaving machine;
[0041]S2 Pre-shape: pre-shape the washed superfine fiber fabric, the setting temperature is 165℃, and the setting cloth speed is 13m / min;
[0042]S3 pretreatment: immerse the pre-shaped microfiber fabric in 30-40℃ hot water, add the refined degreasing agent Dyamul SORnew and penetrant JFC, heat it up to 80℃, keep it warm for 15min, then wash with water and cool it down to 22.5℃. To be dyed
[0043]S4 dyeing: place the superfine fiber fabric in a relaxed state for 6.5h, and send it to the overflow dyeing machine, add 2.5g / L dye and 0.6g / L acid leveling agent for dyeing, and raise the dyeing machine at 2℃ / min Incubate the medium temperature to 85°C for 3 minutes, then heat up at 1°C / min to 90°C for 5 minutes, then heat up at 1.5°C / min to 110°C for 30 minutes, and finally reduce the temperature to 50°C at 1.5°C / min for reduction cleaning...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap