A kind of preparation method and its product of juxtaposed 8-shaped multi-dimensional crimp pa6/pa66 bicomponent fiber

A bicomponent fiber, PA66 technology, applied in fiber processing, melt spinning, stretch spinning, etc., can solve the problems of unfavorable long-term preservation of fabrics, low addition of natural fibers, and limitation of natural fiber output, etc. Stabilized production, high hygroscopic properties, the effect of ensuring shape stability

Active Publication Date: 2021-11-26
ZHEJIANG YINYU NEW MATERIAL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The diversified design and comfort of fabrics have always been a persistent problem faced by chemical fiber fabrics. At present, there are some solutions such as blending or blending chemical fibers and natural fibers to prepare yarns or fabrics with natural fiber feel. To a certain extent, both comfort and product stability are taken into account, so there are more blended products on the market at present, but this kind of product has certain disadvantages. First, the amount of natural fiber added should not be too low. If it is too low, it cannot be achieved. The feel of natural fibers, but if the amount is too high, there may still be mildew and other possibilities, which is not conducive to the long-term preservation of fabrics; second, with the development of urbanization, the area of ​​cultivated land will decrease, and the output of natural fibers will be limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method and its product of juxtaposed 8-shaped multi-dimensional crimp pa6/pa66 bicomponent fiber
  • A kind of preparation method and its product of juxtaposed 8-shaped multi-dimensional crimp pa6/pa66 bicomponent fiber
  • A kind of preparation method and its product of juxtaposed 8-shaped multi-dimensional crimp pa6/pa66 bicomponent fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Two-component selection: According to the spinning characteristics of the fiber, choose the same melt spinning method, and at the same time, the fiber spinning temperature should reflect a certain difference and the difference should not be too large, and the fibers should have better compatibility After screening, PA66 and PA6 were selected as raw materials for spinning;

[0028] Confirmation of the proportion of spinning raw materials: the proportion range of PA6 and PA66 is 2:1 according to the mass ratio;

[0029] PA6 / PA66 two-component composite fiber spinning condition setting: two-component spinning is carried out through two screws, the screw temperature for PA66 is set to 285°C, the screw temperature for PA6 is set to 255°C, and the spinning speed is 2000r / min;

[0030] Preparation of PA6 / PA66 two-component composite DTY fiber: the prepared double-component fiber of composite structure is texturized through a texturing machine. The magnification is 30%, the ...

Embodiment 2

[0033] Two-component selection: According to the spinning characteristics of the fiber, choose the same melt spinning method, and at the same time, the fiber spinning temperature should reflect a certain difference and the difference should not be too large. After screening, PA66 and PA6 were selected as raw materials for spinning. Silk;

[0034] Confirmation of the proportion of spinning raw materials: the proportion range of PA6 and PA66 is 1:1 according to the mass ratio;

[0035] PA6 / PA66 two-component composite fiber spinning condition setting: two-component spinning is carried out through two screws, the screw temperature for PA66 is set to 285°C, the screw temperature for PA6 is set to 255°C, and the spinning speed is 2000r / min;

[0036] Preparation of PA6 / PA66 two-component composite DTY fiber: the prepared double-component fiber of composite structure is texturized through a texturing machine. The magnification is 30%, the loading speed is 750m / min, and the light m...

Embodiment 3

[0039]Two-component selection: According to the spinning characteristics of the fiber, choose the same melt spinning method, and at the same time, the fiber spinning temperature should reflect a certain difference and the difference should not be too large. After screening, PA66 and PA6 were selected as raw materials for spinning. Silk;

[0040] Confirmation of the proportion of spinning raw materials: the proportion range of PA6 and PA66 is 1:2 according to the mass ratio;

[0041] PA6 / PA66 two-component composite fiber spinning condition setting: two-component spinning is carried out through two screws, the screw temperature for PA66 is set to 285°C, the screw temperature for PA6 is set to 255°C, and the spinning speed is 2000r / min;

[0042] Preparation of PA6 / PA66 two-component composite DTY fiber: the prepared double-component fiber of composite structure is texturized through a texturing machine. The magnification is 30%, the loading speed is 750m / min, and the light me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hygroscopicityaaaaaaaaaa
hygroscopicityaaaaaaaaaa
hygroscopicityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of parallel 8-shaped multi-dimensional crimped PA6 / PA66 bicomponent fiber and its products, comprising: selecting PA6 slices as a raw material, and selecting PA66 as another raw material; the ratio range between PA6 and PA66 According to the mass ratio of 1:2~2:1; the two-component spinning is carried out through two screws, wherein the screw temperature of PA66 is set at 270~300°C, and the screw temperature of PA6 is set at 240~270°C to obtain POY Pre-drawn yarn; PA6 / PA66 two-component composite DTY fiber preparation: the prepared PA6 / PA66 two-component composite pre-drawn POY fiber is stretched through a texturing machine to obtain PA6 / PA66 two-component composite DTY fiber. The composite fiber of the present invention has a juxtaposed 8-shaped multi-dimensional crimped structure, and the prepared yarn has a cotton and wool feel, and the spun fabric has the style and comfort of a natural fabric, and at the same time has the aging resistance and non-mildew properties of chemical fibers. characteristic.

Description

technical field [0001] The invention belongs to the technical field of differential fiber preparation, and in particular relates to a method for preparing parallel 8-shaped multi-dimensional crimped PA6 / PA66 bicomponent fibers and a product thereof. Background technique [0002] The diversified design and comfort of fabrics have always been a persistent problem faced by chemical fiber fabrics. At present, there are some solutions such as blending or blending chemical fibers and natural fibers to prepare yarns or fabrics with natural fiber feel. To a certain extent, both comfort and product stability are taken into account, so there are more blended products on the market at present, but this kind of product has certain disadvantages. First, the amount of natural fiber added should not be too low. If it is too low, it cannot be achieved. The hand feeling of natural fibers, but if the addition amount is too high, there may still be mildew and other possibilities, which is not ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/12D01D5/22D01D5/32D01D5/08D01D10/02D01D5/12
CPCD01D5/08D01D5/12D01D5/22D01D5/32D01D10/02D01F8/12
Inventor 李刚余媛童勇宫楹戴思铭陈强张海云
Owner ZHEJIANG YINYU NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products