PBT/PP composite material as well as preparation method and application thereof

A composite material and melt-blown technology, applied in the field of polymer materials, can solve the problems of melt-blown PP materials such as low temperature resistance, poor fluidity, and poor water absorption, and achieve improved toughening effect, improved compatibility, and high fluidity. Effect

Active Publication Date: 2021-02-09
TIANJIN KINGFA NEW MATERIAL
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the present invention aims to propose a PBT / PP composite material and its preparation method and application. Disadvantages such as poor sex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PBT/PP composite material as well as preparation method and application thereof
  • PBT/PP composite material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0047] A kind of ultra-high fluidity, high temperature resistance, high tenacity PBT / PP composite material, its raw material formula is as shown in table 1, and its preparation method comprises the following steps:

[0048] Mix PP SZ30S and di-tert-butyl peroxide well, then feed it from the main feeding port of the extruder, melt, extrude, and granulate in the extruder to obtain melt-blown grade PP. The melt-blown grade PP is tested by the instrument, and the melt flow rate is above 1500g / 10min (230°C, 2.16kg); the melt-blown grade PP is mixed with the above-mentioned PBT material, acrylic acid, weak alkaline degradation agent, primary antioxidant, secondary antioxidant The agent is mixed evenly in the high mixer according to the above ratio, and then fed from the main feeding port of the extruder, melted, extruded, and granulated in the extruder to obtain ultra-high fluidity, high temperature resistance, and high toughness PBT / PP composite material

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a PBT / PP composite material, and a preparation method and an application thereof. The composite material is prepared from the following raw materials by weight: 75.2-88.2 partsof PBT, 5-10 parts of melt-blown grade PP, 5-10 parts of acrylic acid, 2-4 parts of a weakly alkaline degradation agent, 0.4 part of a main antioxidant and 0.4 part of an accessory antioxidant, wherein the melt-blown grade PP is prepared by processing and granulating a PP material with a melt flow rate of about 30 g / 10 min (230 DEG C, 2.16 kg) and di-tert-butyl peroxide by virtue of a double-screwextruder. The PBT / PP composite material disclosed by the invention has the characteristics of ultrahigh flowability, high temperature resistance and high toughness.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a PBT / PP composite material and a preparation method and application thereof. Background technique [0002] During the refining and processing of fuel oil, impurities such as particulate matter and moisture will inevitably be introduced, and moisture will also be mixed in due to the influence of the air environment during storage and transportation. Traditional metal filter screens and filter screens cannot filter nano-scale impurity particles and moisture. Although the melt-blown cloth made of PP by the melt-blown method has a strong filtering ability to filter nano-scale particles, PP itself is a hydrophobic material and cannot filter moisture. At the same time, fuel filtration requires a very high temperature, and PP has a low melting point and poor temperature resistance. PBT has strong water absorption and can be used as a natural oil-water separation material. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L23/12C08K5/00C08K5/14C08K5/098C08K5/09
CPCC08L67/02C08K2201/014C08L2201/08C08L2201/06C08L23/12C08K5/00C08K5/14C08K5/098C08K5/09
Inventor 崔嵬李聪郝垠龙陆湛泉杨霄云陶四平
Owner TIANJIN KINGFA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com