Novel acid-resistant salt-resistant swelling shrinking agent and preparation method thereof
A shrinkage-swelling and salt-tolerant technology, which is applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve problems affecting oil and gas development effects, formation permeability decline, etc., to achieve good compatibility, inhibit water swelling, prevent damage effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0030] Example 1
[0031] A novel temperature-resistant salt-resistant reduduulation agent is added to the reaction kettle first to add 22.425 g of acrylamide, 0.1 g of double acrylamide and 7.475 g of methacryloxyethyltrimethyl ammonium chloride, and 100 ml is added under stirring. Hide 2 O, warmed to 30 ° C, reactive for 30 minutes, so that the system becomes a clear transparent solution, the temperature is adjusted to 80 ° C, and the equal temperature is raised to 80 ° C, mixed with ammonium sulfate 0.1 g and 50 ml of water mixed, uniform In the mixed liquid in the reactor, it was added dropwise to about 30 minutes, and the white transparent liquid was obtained, and the reaction was further reacted for 2.5 h, resulting in a pale yellow transparent gel;
[0032] 3 g of polyether amine and 1 g of dimethyl carbonate were mixed with 50 mL of water, and the temperature was adjusted to 85 ° C, stirred for 2 h, and the synthetic polymer was added to the above solution, stir mixed and ...
Example Embodiment
[0035] Example 2
[0036] A novel temperature-resistant salt-resistant reduduant, 12.425 g of acrylamide, 0.2 g of double acrylamide and 7.475 g of methacryloxyethyltrimethyl ammonium chloride, and 100 ml of stirring Hide 2 O, warmed to 30 ° C, reactive 30 minutes, so that the system becomes a clear transparent solution, the temperature is adjusted to 85 ° C, and the equal temperature is raised to 85 ° C, mixed with ammonium sulfate 0.2 g and 50 ml of water mixed, uniform In the mixed liquid in the reactor, it was added dropwise to about 30 minutes, and the white transparent liquid was obtained, and the reaction was continued for 2 h, resulting in a light yellow transparent gel;
[0037] 3 g of polyether amine and 1 g of dimethyl carbonate were mixed with 50 mL of water, and the temperature was adjusted to 85 ° C, stirred for 2 h, and the synthetic polymer was added to the above solution, stir mixed and uniform, to obtain a pale yellow transparent liquid, that is, the target Reduc...
Example Embodiment
[0039] Example 3
[0040] A novel temperature-resistant salt-resistant reduduulation, 33.6 g of acrylamide, 0.2 g of double acrylamide and 11.2 g of methacryloxyethyltrimethyl ammonium chloride, add 100 ml in agitation. Hide 2 O, the temperature is warmed to 30 ° C, the reaction is 30 minutes, so that the system becomes a clear transparent solution, the temperature is adjusted to 80 ° C, the like temperature is raised to 80 ° C, mix the ammonium sulfate 0.2 g and 50 ml of water mixed, uniform drop In the mixed liquid in the reactor, after about 30 minutes, it was added to give a white transparent liquid, and the reaction was continued for 3 h, resulting in a pale yellow transparent gel;
[0041] 9 g of polyether amine and 3 g of dimethyl carbonate were mixed with 50 ml of water, and the temperature was adjusted to 80 ° C, stirred for 2.5 h, and the synthesized polymer was added to the above solution, stir mixed and uniform, to give a light yellow transparent liquid, ie Target deco...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap