A steelmaking process for controlling porosity defects in continuous casting slabs

A slab and porosity technology, which is applied in the field of steelmaking process to control the porosity defects of continuous casting slabs, can solve problems such as bubble defects, and achieve the effect of reducing bubble defects

Active Publication Date: 2022-02-15
福建三宝钢铁有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For this reason, the present invention provides a steelmaking process for controlling the porosity defects of continuous casting slabs, so as to overcome the problem in the prior art that bubble defects still often occur due to manual adjustment of the amount of argon gas injected.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0081] In order to make the objects and advantages of the present invention clearer, the present invention will be further described below in conjunction with the examples; it should be understood that the specific examples described here are only for explaining the present invention, and are not intended to limit the present invention.

[0082] Preferred embodiments of the present invention are described below. Those skilled in the art should understand that these embodiments are only used to explain the technical principle of the present invention, and are not intended to limit the protection scope of the present invention.

[0083] It should be noted that, in the description of the present invention, terms such as "upper", "lower", "left", "right", "inner", "outer" and other indicated directions or positional relationships are only for the purpose of It is for convenience of description, but does not indicate or imply that the device or element must have a specific orientat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a steelmaking process for controlling the pore defects of continuous casting slabs, which is characterized in that it includes: step 1, transporting the ladle containing the molten steel for refining to the turntable, and turning the turntable to the casting position, and turning the steel The liquid is injected into the tundish; step 2, detect the height of the molten steel liquid level in the tundish, adjust the opening of the nozzle of the tundish according to the height of the liquid steel level, and the tundish distributes the molten steel to several crystallizers through the nozzle. The crystallizer is provided with a submerged nozzle, and argon gas is passed into the submerged nozzle to seal the nozzle; step 3, the molten steel is preliminarily formed into a billet in the crystallizer, and the mold lowers the billet to In the pipeline, the steel billet is subjected to secondary water cooling in the pipeline; step 4, pulling and straightening rollers pull the steel billet after secondary water cooling out of the pipeline; step 5, the cutting device cuts the steel billet according to the required length of the casting billet. The invention intelligently adjusts the amount of argon blowing through the control module, thereby reducing bubble defects in the continuous casting slab.

Description

technical field [0001] The invention relates to the technical field of steelmaking, in particular to a steelmaking process for controlling the pore defects of continuous casting slabs. Background technique [0002] The quality of the continuous casting slab is an important factor affecting the qualified rate of the final product and the production cost. Ensuring good quality of the continuous casting slab is a prerequisite for hot delivery, hot charging and direct rolling. Bubble defects are one of the common defects in casting slabs, which often cause the casting slabs to be unqualified in flaw detection. [0003] During the casting process of molten steel, due to the rapid flow of molten steel, negative pressure will be formed near the bowl of the nozzle, and air will be sucked in, causing secondary oxidation of molten steel, which is a common cause of bubble defects. In order to avoid the inhalation of air, a seal is usually set on the bowl of the nozzle, and argon gas i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/16B22D11/20B22D11/22B22D2/00B22D11/115B22D11/117
CPCB22D11/16B22D11/117B22D2/00B22D11/225B22D11/208B22D11/115
Inventor 王光文李维华吴长锡
Owner 福建三宝钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products