Liquid water-blocking permeable material for buildings and preparation method thereof

A technology for permeable materials and construction, applied in the field of building materials, can solve problems such as unfavorable processing links, liquid infiltration, water leakage, etc., and achieve excellent water blocking effect.

Inactive Publication Date: 2021-03-16
重庆市能容建筑科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many materials for waterproofing on the market, such as water-repellent agents, waterproof coatings, etc. Although these materials can play a certain role in waterproofing, when there are cracks or gaps in the building layer, and after a long service life, it will cause liquid It will slowly seep through the crack, causing water leakage
[0003] In addition, the current environmental protection requirements are very strict, and there are processing links that are not conducive to the environment or emissions that are not conducive to the environment in the existing processing technology of some materials, which also makes the existing products unacceptable by the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid water-blocking permeable material for buildings and preparation method thereof
  • Liquid water-blocking permeable material for buildings and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] In this embodiment, the liquid water-repelling and permeable material for construction provided by the present invention has the following components by weight ratio: silicon dioxide 15-30%; muscovite 15-35%; magnesium oxide 4-10% ; Aluminum oxide 4-10%; Zinc sulfide 5-15%; Calcium chloride 5-15%; Potassium hydroxide 10-20%; Water 10-35%; The sum of the percentages equals 100%.

Embodiment 2

[0012] In this embodiment, the liquid water-blocking and permeable material for construction provided by the present invention has the following components by weight: 18-25% of silicon dioxide; 17-26% of muscovite; 5-10% of magnesium oxide %; aluminum oxide 5-10%; zinc sulfide 7-12%; calcium chloride 7-12%; potassium hydroxide 13-15%; water 15-25%; The sum of the percentages of content is equal to 100%.

Embodiment 3

[0014] In this embodiment, the liquid water-repelling and permeable material for construction provided by the present invention has the following components by weight: 15% silicon dioxide; 25% muscovite; 5% magnesium oxide; 5% aluminum oxide ; Zinc Sulfide 10%; Calcium Chloride 10%; Potassium Hydroxide 15%; Water 15%.

[0015] Wherein, the liquid water-blocking and permeable material for construction is liquid at normal temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of building materials, and particularly discloses a liquid water-blocking permeable material for buildings and a preparation method thereof. Theliquid water-blocking permeable material includes the following components, by weight: 15-30% of silicon dioxide; 15-35% of muscovite; 4-10% of magnesium oxide; 4-10% of alumina; 5-15% of zinc sulfide; 5-15% ofcalcium chloride; 10-20% of potassium hydroxide; 10-35% of water. During proportioning, the sum of the percentages of the components in the composition is equal to 100%, and the composition is in theform of solid powder. The liquid water-blocking permeation material for the building, prepared by the invention, has a very good waterproof effect.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a liquid water-repelling and permeable material for building. Background technique [0002] In the prior art, building waterproofing is a very important process, and the waterproofing effect is often closely related to the waterproofing materials used. At present, there are many materials for waterproofing on the market, such as water-repellent agents, waterproof coatings, etc. Although these materials can play a certain role in waterproofing, when there are cracks or gaps in the building layer, and after a long service life, it will cause liquid It will slowly seep through the crack, causing water leakage. [0003] In addition, the current environmental protection requirements are very strict, and there are processing links that are unfavorable to the environment or emissions that are unfavorable to the environment in the processing technology of some existing materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/10C04B111/27
CPCC04B28/105C04B2111/00293C04B2111/27
Inventor 熊智刚
Owner 重庆市能容建筑科技有限公司