Mica baby powder and preparation method thereof

A technology of talcum powder and mica, applied in the field of daily necessities, can solve the problem of poor baby powder effect, etc., and achieve the effect of reducing rash and preventing infection

Pending Publication Date: 2021-04-02
湖北研妆实业有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the technical problem of the poor effect of baby talcum powder in the prior art, the present invention proposes a baby mica talcum powder and a preparation method thereof. By optimizing the product formula, the product forms a layer of biofilm on the skin surface, which significantly improves the baby talcum powder. safety and effectiveness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mica baby powder and preparation method thereof
  • Mica baby powder and preparation method thereof
  • Mica baby powder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A baby mica talcum powder, comprising the following components: 60.0g mica, 0.1g corn modified starch, 1.0g hydrolyzed collagen, 0.1g vegetable oil, 0.5g aloe vera leaf extract, 0.1g zinc oxide, 0.02g Xingan alcohol.

[0034] (1) Weigh mica, modified cornstarch, and zinc oxide respectively and add them to a high-speed powder mixer, turn on the homogenization for 0.5-3 minutes, and mix evenly to form a phase A mixed raw material;

[0035] (2) Weigh caprylyl glycol, hydrolyzed collagen, and vegetable oil respectively, dissolve them evenly at 30-40°C, and add them into the oil spray pot to form the raw materials of phase B; turn on the high-speed powder mixer, and slowly spray into phase B while stirring raw material;

[0036] (3) Take the aloe vera leaf extract to form the C-phase raw material in the oil spray pot; turn on the high-speed powder mixer, and slowly spray into the C-phase raw material while stirring;

[0037] (4) Transfer the mixed powder to a vibrating pow...

Embodiment 2

[0039] A baby mica body powder, comprising the following components: 75.0g mica, 15.0g corn modified starch, 3.0g hydrolyzed collagen, 0.5g vegetable oil, 2.0g aloe leaf extract, 5.0g zinc oxide, 0.20g caprylyl glycol .

[0040] The preparation method is the same as in Example 1.

Embodiment 3

[0042] A baby mica body powder, comprising the following components: 99.0g mica, 8.0g corn modified starch, 5.0g hydrolyzed collagen, 0.3g vegetable oil, 0.001 aloe vera leaf extract, 2.5g zinc oxide, 0.50g caprylyl glycol .

[0043] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a mica baby powder and a preparation method thereof. The mica baby powder comprises the following ingredients in parts by weight: (1) 60-99 parts of filling agents, (2) 0.02-0.5 part of humectant and (3) 1.301-27.5 parts of skin conditioners, wherein the filling agent is mica, and the skin conditioner comprises 0.10-15 parts of modified corn starch, 1-5 parts of hydrolyzedcollagen, 0.1-0.5 part of plant oil, 0.001-2 parts of Aloe vera (Haw.) Berg leaf extracts and 0.1-5 parts of zinc oxide. On a premise that the mica and the modified corn starch are taken as the filling agent, the hydrolyzed collagen, the plant oil, the zinc oxide, the Aloe vera (Haw.) Berg leaf extracts and other skin conditioners are assisted to develop the mica baby powder, and the developed mica baby powder has a function of resisting inflammation and moistening the skin, can form a natural biological protection film barrier on the surface of the skin, resists injuries of external bacteriaand sensitinogen, avoids infection, indirectly generates an antisepsis and anti-inflammation function, and obviously reduces rash and red and swollen situations. Meanwhile, injuries to the body function of an infant by asbestos and heavy metal lead in talcum powder can be avoided.

Description

technical field [0001] The invention relates to the technical field of daily necessities, and more specifically, to a baby mica body powder and a preparation method thereof. Background technique [0002] The baby's immune system is not yet perfect, and the resistance is weak. The baby's skin is only one-tenth of the thickness of the adult's skin. The epidermis is a single layer of cells, and the dermis has few collagen fibers, so it lacks elasticity and is easily penetrated by foreign objects and damaged by friction. . At the same time, the stratum corneum is immature, the dermis and fibrous tissue are thin, the skin is delicate and sensitive, and the ability to resist dry environments is relatively weak. The skin's ability to control acidity and alkalinity is poor. Babies only rely on a layer of natural acidic protective film on the skin surface to protect the skin from bacterial infection and keep the skin moisturized and smooth. [0003] The main function of traditional...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/9794A61K8/19A61K8/27A61K8/34A61K8/65A61K8/73A61K8/92A61K8/9789A61Q15/00
CPCA61K8/9794A61K8/9789A61K8/65A61K8/19A61K8/27A61K8/732A61K8/922A61K8/345A61Q15/00
Inventor 陈出新
Owner 湖北研妆实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products