Novel OLED screen protective film and preparation method and application thereof
A technology of screen protection film and protective film, which is applied in the direction of adhesive type, film/sheet release liner, film/sheet adhesive, etc., which can solve the strict requirements of static electricity, lack of OLED display protective film, etc. Problems, to achieve the effect of low static voltage of tear film, excellent exhaust, and prolong service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0032]Example 1
[0033]The hardness of S1, TPU is set to 45-50HD, which is used to adopt ultraviolet antistatic TPU film;
[0034]S2, the production process of the thermosetting TPU layer is a slit coating method, a speed of 20 m / min, and the coating machine baking is set to 55-105 ° C, and 6 baking is sequentially set during drying. Section 55 ° C, 75 ° C, 95 ° C, 105 ° C, 95 ° C, 75 ° C;
[0035]S3, remove the release membrane of TPU, coating a hardening liquid;
[0036]S4, the production process of the hardened layer is a coating method, the speed of 25 m / min, the front oven drying temperature is set to 60-110 ° C, the drying process is provided in 4 baking sections 65 ° C, 80 ° C, 95 ° C, 105 ° C , Backend UV curing energy is set to 480MJ / cm2The hardening layer has a thickness of 2 to 5 μm, and the hardness of the hardening layer is greater than 3h;
[0037]S5, remove the other side of the TPU to the plate, and apply the PU glue as the TPU.
[0038]S6, PU glue production process is a coati...
Example Embodiment
[0041]Example 2
[0042]The hardness of S1, TPU is set to 45-50HD, which is used to adopt ultraviolet antistatic TPU film;
[0043]S2, the production process of the thermosetting TPU layer is a slit coating method, a speed of 20 m / min, and the coating machine baking is set to 55-105 ° C, and 6 baking is sequentially set during drying. Section 55 ° C, 75 ° C, 95 ° C, 105 ° C, 95 ° C, 75 ° C;
[0044]S3, remove the TPU-side release film, use the TPU to coating the substrate, coating the PU glue;
[0045]The production process of S4, PU glue is a coating method, a speed of 21 m / min, and the drying temperature of the coating machine is set to 85-135 ° C, and the 6 baking sections 85 ° C, 105 during drying process. ° C, 125 ° C, 135 ° C, 125 ° C, 105 ° C;
[0046]S5, PU rubber, the release film is an antistatic release film;
[0047]S6, after the sample is completed, you need to be matured at 80 ° C for 24 h.
Example Embodiment
[0048]Example 3
[0049]S1, adjust the hardness of the TPU layer to 90HD, using an anti-UV resistant electrostatic TPU film;
[0050]S2, the production process of the thermosetting TPU layer is a slit coating method, a speed of 20 m / min, and the coating machine baking is set to 55-105 ° C, and 6 baking is sequentially set during drying. Section 55 ° C, 75 ° C, 95 ° C, 105 ° C, 95 ° C, 75 ° C;
[0051]S3, remove the release membrane of TPU, coating a hardening liquid;
[0052]S4, the production process of the hardened layer is a coating method, the speed of 25 m / min, the front oven drying temperature is set to 60-110 ° C, the drying process is provided in 4 baking sections 65 ° C, 80 ° C, 95 ° C, 105 ° C , Backend UV curing energy is set to 480MJ / cm2The hardening layer has a thickness of 2 to 5 μm, and the hardness of the hardening layer is greater than 3h;
[0053]S5, remove the other side of the TPU to the plate, and apply the PU glue as the TPU.
[0054]S6, PU glue production process is a coa...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap