A kind of low thermal expansion coefficient high strength glass fiber

A low thermal expansion coefficient, glass fiber technology, applied in the field of glass fiber, can solve the problem that the glass fiber cannot meet the higher demand, and achieve the effect of low expansion coefficient and low crystallization rate

Active Publication Date: 2022-03-18
TAISHAN FIBERGLASS INC
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to make up for the deficiencies of the existing technology and solve the problem that the glass fiber in the prior art cannot meet higher requirements, the present invention provides a low thermal expansion coefficient high-strength glass fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low thermal expansion coefficient high strength glass fiber
  • A kind of low thermal expansion coefficient high strength glass fiber
  • A kind of low thermal expansion coefficient high strength glass fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] The technical solutions in the embodiments of the present invention will be clearly and completely described below, and the described embodiments are only part of the embodiments of the present invention, not all of the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0041] The production process of low thermal expansion coefficient high-strength glass fiber comprises the following steps:

[0042] (1) Calculate the quality of each raw material required according to the implementation formula, mix and homogenize each raw material according to the formula requirements, and transport the batch material that meets the requirements of the particle size distribution to the kiln head silo, and then use the feeder to feed the compound at a constant speed. The material is put into the all-electric meltin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
crystallization temperatureaaaaaaaaaa
elastic modulusaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength glass fiber with low thermal expansion coefficient, which belongs to the technical field of glass fiber. The glass fibers of the present invention consist of the following components: SiO 2 59.0~69.0%, Al 2 o 3 13.5~25.0%, MgO 6.0~10.0%, B 2 o 3 1.0~6.0%, CeO 2 0.5~2.0%, ZnO 0.1~4.5%, TiO 2 0.1~4.0%, ZrO 2 0.1~3.0%,H f o 2 0.1~2.0%, Li 2 O 0.1~2.0%; of which TiO 2 , ZrO 2 、H f o 2 The sum of the contents is 1.0-5.0%. The low expansion coefficient high strength glass fiber of the present invention does not add CaO, K 2 O, Na 2 O component, add B 2 o 3 , ZnO, TiO 2 , ZrO 2 、H f o 2 , while increasing the content of silicon and aluminum, reducing the content of boron and magnesium, and adding an appropriate amount of CeO 2 , under the premise of ensuring that the difficulty of production is appropriate, glass fibers with low expansion coefficient and high strength can be obtained.

Description

technical field [0001] The invention relates to the technical field of glass fibers, in particular to a glass fiber with low thermal expansion coefficient and high strength. Background technique [0002] Glass fiber is an excellent inorganic non-metallic material with good insulation, strong heat resistance, good corrosion resistance, and a wide variety. With the development of economy, glass fiber has become an indispensable material in construction, transportation, electronics, electrical, chemical, metallurgy, aviation, national defense and other industries. [0003] However, with the development of science and technology, the performance requirements of glass fiber in printed circuit boards, national defense, aviation, etc. are getting higher and higher. The strength, elastic modulus, and thermal expansion coefficient of existing glass fibers can no longer meet the performance requirements, and the strength, elastic modulus, and thermal expansion coefficient of glass fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C13/02C03B37/025C03B37/027
CPCC03C13/00C03B37/025C03B37/027
Inventor 王加芳杜凤玲孙立国柳丽娜刘晓斌刘莎莎程涛李风香吴钦霞张艳萍徐东芝于雷卜凡宁尚鹏
Owner TAISHAN FIBERGLASS INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com