A kind of high-gloss anti-skid material and preparation method thereof

A high-gloss, anti-slip technology, applied in the coating and other directions, can solve the problems of poor control, obvious surface roughness, inability to achieve anti-slip properties, etc., and achieve the effect of high gloss.

Active Publication Date: 2022-07-22
FOSHAN DONGPENG CERAMIC +3
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The second is to make the surface of the tiles rough from the microscopic level. The roughness that is invisible to the naked eye does not affect the decorative effect. However, the materials processed from the microscopic level are all acidic or alkaline materials, and they are generally placed in the penultimate place. However, for the above-mentioned non-slip tiles, due to the obvious surface roughness or insufficient microscopic surface, the performance of both anti-slip and high gloss cannot be achieved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-gloss anti-skid material and preparation method thereof
  • A kind of high-gloss anti-skid material and preparation method thereof
  • A kind of high-gloss anti-skid material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] A preparation method of a high-gloss anti-skid material, comprising the following steps:

[0041] (1) Mix the oxidized modified polyethylene wax emulsion, polypropylene wax emulsion and alkaline silica sol solution to obtain the main anti-skid material a; then add silicon fluoride and polyurethane inside and outside the main anti-slip material a for stirring and mixing, fully After mixing, anti-slip liquid a is obtained;

[0042] (2) stirring and mixing styrene and acrylate to obtain the main anti-slip material b; then adding polyacrylic resin and vinyl resin inside and outside the main anti-slip material b, stirring and mixing, and fully mixing to obtain anti-slip liquid b;

[0043] (3) Mix the anti-slip liquid a and the anti-slip liquid b in proportion, add maleic anhydride, stir and mix, and after fully mixing, the anti-slip material is obtained.

[0044] To further illustrate, in the step (1), the reaction conditions are that the reaction temperature is 180-195° C....

Embodiment A

[0054] A preparation method of a high-gloss anti-skid material, comprising the following steps:

[0055](1) Add silicon fluoride accounting for 7% of the total mass and polyurethane accounting for 2% of the total mass inside and outside the main anti-skid material a, and stir and mix at a stirring speed of 150-160 r / min for 48 hours. After fully mixing, The anti-skid liquid a is obtained; the raw material composition of the main anti-skid material a is shown in Table 1;

[0056] (2) Stir and mix 20% of styrene and 80% of acrylate at a stirring speed of 100-120 r / min for at least 8 hours to obtain the main anti-skid material b; then add inside and outside the main anti-slip material b to account for the total mass 25% of polyacrylic resin and 8% of vinyl resin by total mass are mixed with stirring, the stirring speed is 120-150r / min, and the stirring is carried out for 24 hours. After fully mixing, anti-slip liquid b is obtained;

[0057] (3) Mix the anti-slip liquid a and the...

Embodiment B

[0066] A preparation method of a high-gloss anti-skid material, comprising the following steps:

[0067] (1) Mix 70% of oxidatively modified polyethylene wax emulsion, 20% of polypropylene wax emulsion and 10% of alkaline silica sol solution to obtain main anti-skid material a; then add inside and outside the main anti-slip material a to account for the total mass 7% of silicon fluoride and 2% of polyurethane by total mass are stirred and mixed, the stirring speed is 150-160r / min, and the stirring is carried out for 48 hours. After fully mixing, anti-slip liquid a is obtained;

[0068] (2) Stir and mix styrene and acrylate at a stirring speed of 100-120 r / min, and stir for 8 hours to obtain the main anti-skid material b; then add 25% of the total mass of polyacrylic resin and Vinyl resin accounting for 8% of the total mass, stirring and mixing at a stirring speed of 120-150 r / min, stirring for 24 hours, and fully mixing, to obtain anti-slip liquid b; among them, the mixing sit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

A high-gloss anti-skid material and a preparation method thereof, the raw materials of the anti-skid material include: anti-slip liquid a and anti-slip liquid b; the anti-slip liquid a includes: main anti-slip material a, silicon fluoride and polyurethane; , the main anti-skid material a includes: 60-80% oxidatively modified polyethylene wax emulsion, 15-25% polypropylene wax emulsion and 5-15% alkaline silica sol liquid; the anti-skid liquid b includes: Main body anti-skid material b, polyacrylic resin and vinyl resin; according to mass percentage, the main body anti-skid material b comprises: 20-40% of styrene and 60-80% of acrylate; the preparation method is prepared to the anti-skid liquid a and Anti-slip liquid b, and mix the two to obtain a high-gloss anti-slip material; the anti-slip material uses anti-slip liquid a and anti-slip liquid b, and under the combined action of the two, a kind of anti-slip effect and high gloss is obtained. The anti-skid material solves the problem that the roughness and gloss cannot be improved at the same time in the prior art.

Description

technical field [0001] The invention relates to the technical field of anti-skid materials, in particular to a high-gloss anti-skid material and a preparation method thereof. Background technique [0002] There are two types of existing anti-slip tiles. The first is to roughen the surface of the tile from a macro perspective, so as to improve anti-skid, such as dry grain and uneven effect. The second is to roughen the surface of the tile from the microscopic level, and the roughness that cannot be seen by the naked eye will not affect the decorative effect. However, for the above-mentioned anti-skid tiles, due to the obvious surface roughness or insufficient microscopic surface, the performance of both anti-skid and high gloss cannot be achieved. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to provide a high-gloss anti-slip material, which includes anti-slip liquid a and anti-slip liquid b, which are mixed to obtain a high-gloss anti-slip mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/65C09D7/61C09D7/63
CPCC09D4/06C09D7/65C09D7/61C09D7/63
Inventor 祁明钟保民徐瑜
Owner FOSHAN DONGPENG CERAMIC