A kind of cable with high temperature resistance and long service life and its preparation method

A technology with high temperature resistance and long life, which is applied in the direction of cable/conductor manufacturing, power cables with shielding layer/conductive layer, power cables, etc. problems, to achieve simple and environmentally friendly production, reduce external interference, and facilitate preparation

Active Publication Date: 2022-04-12
山东中迈电缆有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a high-temperature-resistant and long-life cable and a preparation method thereof, which can effectively solve the problems in the above-mentioned background technology that the external protective shell of the cable currently used in electric power engineering is relatively soft, has weak protection ability for the cable wire, and is heat-resistant. The capacity is not ideal. When the temperature is high, the cable becomes soft seriously, which affects the service life of the cable and reduces the safety of the cable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cable with high temperature resistance and long service life and its preparation method
  • A kind of cable with high temperature resistance and long service life and its preparation method
  • A kind of cable with high temperature resistance and long service life and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Such as Figure 1-4 As shown, the present invention provides a technical solution, a cable with high temperature resistance and long life, comprising an outer protective shell 1, the inner end surface of the outer protective shell 1 is uniformly bonded with a supporting soft rod 2, and the inner side of the supporting soft rod 2 is provided with a The arc-shaped fixing groove 3 is filled with polyimide filler 4, the supporting soft rod 2 has an arc-shaped structure, and the end faces of both sides of the supporting soft rod 2 are glued to the inner end face of the outer protective shell 1, The middle part of the polyimide filling material 4 is provided with a number of connection holes to facilitate the bending of the flexible rod 2. The two ends of the outer protective shell 1 are symmetrically provided with embedded grooves 5, and a pulling wire 6 is embedded in the embedded groove 5. Each end of the shell 1 is provided with two embedding grooves 5, the length of the ...

Embodiment 2

[0040] Such as Figure 5 As shown, the present invention provides a technical solution, a method for preparing a high-temperature-resistant and high-life cable, comprising the steps of:

[0041] S1, weighing and classifying the raw materials, and then mixing;

[0042] S2, after mixing, put it into an open mill for processing, then take it out and let it stand;

[0043] S3, adding a vulcanizing agent and a vulcanization accelerator, and vulcanizing it;

[0044] S4. After the processing is completed, it is left to be detected and then processed.

[0045] Further, the raw materials in S1 are the following parts by weight: 110 parts of insulating rubber powder, 2 parts of sulfur, 12 parts of transformer oil, 40 parts of talcum powder, 3 parts of wear-resistant carbon black, and 1 part of stearic acid.

[0046] Further, the temperature in S2 is 170 degrees, and the heat treatment time is 12 minutes;

[0047] The vulcanization time in the S3 is 27min, and the pressure is 12Mpa. ...

Embodiment 3

[0050] Such as Figure 5 As shown, the present invention provides a technical solution, a method for preparing a high-temperature-resistant and high-life cable, comprising the steps of:

[0051] S1, weighing and classifying the raw materials, and then mixing;

[0052] S2, after mixing, put it into an open mill for processing, then take it out and let it stand;

[0053] S3, adding a vulcanizing agent and a vulcanization accelerator, and vulcanizing it;

[0054] S4. After the processing is completed, it is left to be detected and then processed.

[0055] Further, the raw materials in S1 are the following parts by weight: 120 parts of insulating rubber powder, 1.5 parts of sulfur, 12 parts of transformer oil, 42 parts of talcum powder, 3 parts of wear-resistant carbon black, and 1 part of stearic acid.

[0056] Further, the temperature in S2 is 180 degrees, and the heat treatment time is 12 minutes;

[0057] The vulcanization time in the S3 is 30min, and the pressure is 12Mpa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-temperature-resistant and long-life cable and a preparation method thereof. The inner end surface of the outer protective shell is uniformly bonded with a support soft rod, and the inner side of the support soft rod is provided with an arc-shaped fixing groove. The inside of the shaped fixing groove is filled with polyimide filler, the two ends of the outer protective shell are symmetrically provided with embedded grooves, the inner of the embedded groove is embedded with a pulling wire, and the inner of the outer protective shell is wrapped with an inner protection shell, the present invention sets an outer protective shell, a supporting soft rod, an arc-shaped fixing groove and polyimide filling materials. The polyimide filling material inside the groove is not easy to deform in high temperature environment, supports the outer protective shell, and can withstand low temperature at the same time, the outer protective shell outside the cable is not easy to become soft and hard and cause rupture, prolonging the service life of the cable, and is safe High performance.

Description

technical field [0001] The invention relates to the technical field of cables, in particular to a high-temperature-resistant and long-life cable and a preparation method thereof. Background technique [0002] A cable is an electrical energy or signal transmission device, usually made of one or more mutually insulated conductors and an outer insulating layer, and a wire that transmits power or information from one place to another, usually consisting of several Or a rope-like cable made of several groups of wires twisted, each group of wires is insulated from each other, and is often twisted around a center, the entire outside is covered with a highly insulating covering, the cable has internal energization, external insulation Features, widely used in power engineering for the transmission of electrical energy; [0003] However, the quality of the outer protective shell of the cables used in power engineering is relatively soft, the protection ability for the cable conducto...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01B7/29H01B7/18H01B7/38H01B7/17H01B9/02H01B13/22H01B13/00
CPCH01B7/292H01B7/18H01B7/1875H01B7/385H01B7/17H01B9/024H01B9/02H01B13/22H01B13/00
Inventor 汤善卿
Owner 山东中迈电缆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products