Flame-retardant and antistatic wool blended fabric

A flame retardant, antistatic, wool blending technology, which is applied in the field of textiles, can solve the problems of poor coloring rate and antistatic ability of fabrics, and achieve the effects of short reaction time, improved wettability, and less dosage

Inactive Publication Date: 2021-06-11
张永齐
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the fabric still has the problems of poor coloring rate and antistatic ability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant and antistatic wool blended fabric
  • Flame-retardant and antistatic wool blended fabric
  • Flame-retardant and antistatic wool blended fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A flame-retardant and antistatic wool blended fabric, the blended fabric is made of 34% wool fiber, 13% bamboo charcoal fiber, 12% flame-retardant viscose fiber, 14% conductive microporous polyester fiber, 9% polyester fiber, and 18% acrylic fiber % is raw material, which is made through the process steps of strip dyeing, combing, spinning, weaving and dyeing and finishing;

[0035] In the sliver dyeing and combing process, the wool fiber, bamboo charcoal fiber, flame-retardant viscose fiber, microporous polyester fiber, polyester fiber, and acrylic fiber are respectively dyed, wherein: wool fiber, Bamboo charcoal fiber, flame retardant viscose fiber, microporous polyester fiber, polyester fiber, acrylic fiber, heat up to 100°C at a speed of 1°C / min, keep it for 30min, and then heat up at a speed of 2°C / min Cool down to 60°C, take out the fibers;

[0036] The dye liquor comprises the following raw materials: cationic dye, refining enzyme, acetic acid, penetrant, hydrog...

Embodiment 2

[0041] A flame-retardant antistatic wool blended fabric, the blended fabric is made of 35% wool fiber, 13% bamboo charcoal fiber, 15% flame-retardant viscose fiber, 10% conductive microporous polyester fiber, 10% polyester fiber, and 17% acrylic fiber % is raw material, which is made through the process steps of strip dyeing, combing, spinning, weaving and dyeing and finishing;

[0042] In the sliver dyeing and combing process, the wool fiber, bamboo charcoal fiber, flame-retardant viscose fiber, microporous polyester fiber, polyester fiber, and acrylic fiber are respectively dyed, wherein: wool fiber, Bamboo charcoal fiber, flame retardant viscose fiber, microporous polyester fiber, polyester fiber, acrylic fiber, heat up to 98°C at a speed of 1°C / min, keep it for 35min, and then heat up at a speed of 2°C / min Cool down to 65°C, take out the fibers;

[0043] The dye liquor comprises the following raw materials: cationic dye, refining enzyme, acetic acid, penetrant, hydrogen p...

Embodiment 3

[0048] A flame-retardant antistatic wool blended fabric, the blended fabric is made of 33% wool fiber, 15% bamboo charcoal fiber, 11% flame-retardant viscose fiber, 12% conductive microporous polyester fiber, 9% polyester fiber, and 20% acrylic fiber % is raw material, which is made through the process steps of strip dyeing, combing, spinning, weaving and dyeing and finishing;

[0049] In the sliver dyeing and combing process, the wool fiber, bamboo charcoal fiber, flame-retardant viscose fiber, microporous polyester fiber, polyester fiber, and acrylic fiber are respectively dyed, wherein: wool fiber, Bamboo charcoal fiber, flame retardant viscose fiber, microporous polyester fiber, polyester fiber, acrylic fiber, heat up to 100°C at a speed of 2°C / min, keep it for 20min, and then heat up at a speed of 2°C / min Cool down to 65°C, take out the fibers;

[0050] The dye liquor comprises the following raw materials: cationic dye, refining enzyme, acetic acid, penetrant, hydrogen p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant and antistatic wool blended fabric, and belongs to the technical field of textiles. The blended fabric is prepared from wool fibers, bamboo charcoal fibers, flame-retardant viscose fibers, conductive microporous polyester fibers, polyester fibers and acrylic fibers as raw materials through the process steps of top dyeing and recombing, spinning, weaving and dyeing and finishing. The blended fabric comprises the following fibers in percentage by weight of 30%-35% of the wool fibers, 10%-15% of the bamboo charcoal fibers, 5%-15% of the flame-retardant viscose fibers, 10%-15% of the conductive microporous polyester fibers, 6%-10% of the polyester fibers, 5%-15% of conductive fibers and 10%-20% of the acrylic fibers. The blended fabric has the characteristics of being high in dye uptake, low in average color difference value, good in antistatic effect and the like.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a flame-retardant and antistatic wool blended fabric and a preparation method thereof. Background technique [0002] Blended or blended chemical fiber fabrics are textile products made of chemical fibers mixed with other cotton wool, silk, hemp and other natural fibers. It has both the style of polyester and the advantages of cotton fabrics, such as polyester cotton cloth and polyester wool gabardine. Blending is divided into wool-viscose blending, sheep and rabbit wool spinning, TR fabrics, high-density NC fabrics, 3M waterproof mousse fabrics, TENCEL fabrics, Rousai silk, TNC fabrics, composite fabrics, etc. [0003] Most of the fibers used in conventional high-end suit fabrics are mainly wool and polyester. Among them, wool is warm and water-repellent, and polyester has high strength but poor air permeability, so it is not suitable for summer wear. Now people hav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06P1/41D06P1/46D06P1/653D06P1/673D06P3/18D06P3/52D06P3/60D06P3/76D06P3/80D01F1/07D01F2/10D01F8/02D01F8/18D06M11/00D06M13/00D06M13/02D06M15/00D03D15/513D03D15/533D03D15/47D03D15/283D03D15/275D03D15/233D03D15/225D03D15/37D04B1/14D04B21/00D02G3/44D02G3/04D06M101/32
CPCD01F1/07D01F2/10D01F8/02D01F8/18D02G3/04D02G3/441D02G3/443D04B1/14D04B21/00D06M11/00D06M13/00D06M13/02D06M15/00D06M2101/32D06P1/41D06P1/46D06P1/6533D06P1/6735D06P3/18D06P3/522D06P3/6016D06P3/76D06P3/80D10B2101/12D10B2201/24D10B2211/02D10B2321/10D10B2331/04D10B2401/16
Inventor 张永齐关怡
Owner 张永齐
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com