A production device and process of high -temperature magnesium carbon brick

A production device and a technology for magnesia-carbon bricks, which are applied in the field of refractory material production, can solve the problems of poor adhesion between the refractory layer and the magnesia-carbon brick matrix, numerous production equipment, and influence on production efficiency, etc. The effect of convenient feeding and improving efficiency

Active Publication Date: 2021-09-24
CHANGXING HONGFENG CHARGING
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the high temperature working environment, the fire-facing surface of magnesia-carbon bricks is most affected. At present, the most convenient measure to improve this situation is to coat the fire-facing surface of magnesia-carbon bricks with a refractory layer, but the existing production processes are all The material is coated after the magnesia-carbon brick is fired, and the bonding performance between the refractory layer and the magnesia-carbon brick matrix is ​​not very good. In addition, the existing production equipment is various and the process is complicated, which affects production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A production device and process of high -temperature magnesium carbon brick
  • A production device and process of high -temperature magnesium carbon brick
  • A production device and process of high -temperature magnesium carbon brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0044] The technical solutions in the embodiments of the present invention will be clearly and completely described below. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0045] A high-temperature-resistant magnesia-carbon brick, which is prepared by processing the following raw materials in parts by weight: 8-15 parts of flake graphite powder, 65-80 parts of fused magnesia grain material, 2-4 parts of additives, and 6-10 parts of mullite powder parts, 1-3 parts of binder, 5-12 parts of water;

[0046] The particle size of the flake graphite powder is less than or equal to 0.088mm, and the magnesium oxide content in the fused magnesia powder is greater than 98%;

[0047] The fused magnesia granular mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature-resistant magnesia-carbon brick production device and its process. In the invention, the magnesia-carbon brick raw material is put into a pressing mold box, and the magnesia-carbon brick embryo is obtained by machine pressing, and the refractory coating is applied on the On the fire-facing surface of the magnesia-carbon brick embryo, specifically, the pressing mold box is rotated 90 degrees and aligned with the vertical discharge box, and the cylinder is driven to simultaneously push the mold box bottom plate and the coating roller out, and the mold box bottom plate pushes the magnesia-carbon brick embryo into the vertical discharge box, and the coating roller just smears the refractory coating on the fire-facing surface of the magnesia-carbon brick embryo during the process of moving and resetting the pressing mold box; The whole process of roasting avoids manual or machine contact with the surface of the magnesia-carbon brick embryo, which improves the quality of the magnesia-carbon brick embryo.

Description

technical field [0001] The invention belongs to the technical field of refractory material production, and specifically relates to a production device and process for high-temperature resistant magnesia-carbon bricks. Background technique [0002] Magnesia carbon brick, commonly known as refractory brick, is a refractory material made of refractory clay or other refractory raw materials. It is mainly used for building smelting furnaces. It can withstand high temperatures of 1580°C-1770°C. It is a refractory material with a certain shape and size. It can be used as high-temperature building materials and structural materials for building kilns and various thermal equipment, and can withstand various physical and chemical changes and mechanical actions at high temperatures. Magnesia-carbon bricks contain graphite that is easily oxidized at high temperatures and binder phenolic resin After baking at 800-1100°C, carbon oxidation will inevitably occur and an obvious decarburizati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/043
CPCC04B35/043C04B2235/3463C04B2235/425C04B2235/9607
Inventor 刘伦易卫方王玉兵周永莫桂花刘健杨敏
Owner CHANGXING HONGFENG CHARGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products