Organic porous framework material with adsorptive desulfurization performance and preparation method thereof

A porous skeleton, adsorption desulfurization technology, applied in chemical instruments and methods, inorganic chemistry, refined hydrocarbon oil, etc., can solve the problems of difficult regeneration, poor selective adsorption, intolerance to strong acids and alkalis, etc.

Active Publication Date: 2021-10-19
XI AN JIAOTONG UNIV
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Commercial zeolites and activated carbons have the advantages of low cost and easy availability, but the strong acid sites in zeolites have strong interactions with sulfides, making their regeneration difficult
Due to the lack of suitable adsorption sites in activated carbon materials, the selective adsorption of thiophene sulfur is relatively poor.
MOFs materials have also been widely used in adsorption desulfurization research in recent years, and have shown excellent adsorption effects. However, MOFs materials have poor thermal stability and are not resistant to strong acids and alkalis, so they are limited in application range and reusability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic porous framework material with adsorptive desulfurization performance and preparation method thereof
  • Organic porous framework material with adsorptive desulfurization performance and preparation method thereof
  • Organic porous framework material with adsorptive desulfurization performance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Step 1: Add 2mol of 1,3,5-benzenetricarbaldehyde and 3mol of 1,4-benzenediacetonitrile into the reactor, then add 1L of 1,4-dioxane and 1L of 1,3, 5 Trimethylbenzene solvent, after stirring evenly, add 0.2L of 6mol / L DBU (1,8-diazabicyclo[5.4.0]undec-7-ene) solution as a catalyst, and react at 150°C for 72h to obtain a mixed liquid;

[0047] Step 2: Cool the mixture obtained in Step 1 to room temperature, and pour it into the material barrel, during which time the residue in the kettle can be washed with deionized water. The obtained mixture was subjected to suction filtration, and deionized water and methanol were used as washing solvents, each washing three times to obtain a filter cake. Put the filter cake into a beaker filled with DMF solution, rotate and stir on a magnetic stirrer for 1 h, and then carry out suction filtration. The obtained product was subjected to Soxhlet extraction with methanol reagent for 24 hours to further remove impurities, and the Soxhlet...

Embodiment 2

[0053] Step 1: Add 2mol monomer 1,3,5-benzenetricarbaldehyde and 3mol 1,4-benzenediacetonitrile into the reaction kettle, then add 2L of N,N-dimethylformamide solvent, stir well Add 0.2L of 6mol / L sodium hydroxide solution as a catalyst, and react at 100°C for 72h to obtain a mixed solution;

[0054] Step 2: Cool the mixture obtained in Step 1 to room temperature, and pour it into the material barrel, during which time the residue in the kettle can be washed with deionized water. The obtained mixture was subjected to suction filtration, and deionized water and methanol were used as washing solvents, each washing three times to obtain a filter cake. Put the filter cake into a beaker filled with DMF solution, rotate and stir on a magnetic stirrer for 1 h, and then carry out suction filtration. The obtained product was subjected to Soxhlet extraction with methanol reagent for 24 hours to further remove impurities, and the Soxhlet-extracted solid was vacuum-dried at 100° C. for 1...

Embodiment 3

[0064] Step 1: Add 2mol of monomer 1,3,5-benzenetricarbaldehyde and 3mol of 1,4-benzenediacetonitrile into the reaction kettle, then add 2L of dichlorobenzene solvent, stir well and add 0.2L of 6mol / L of potassium carbonate solution was used as a catalyst, and reacted at 120°C for 72 hours to obtain a mixed solution;

[0065] Step 2: Cool the mixture obtained in Step 1 to room temperature, and pour it into the material barrel, during which time the residue in the kettle can be washed with deionized water. The obtained mixture was subjected to suction filtration, and deionized water and methanol were used as washing solvents, each washing three times to obtain a filter cake. Put the filter cake into a beaker filled with DMF solution, rotate and stir on a magnetic stirrer for 1 h, and then carry out suction filtration. The obtained product was subjected to Soxhlet extraction with methanol reagent for 24 hours to further remove impurities, and the Soxhlet-extracted solid was va...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses an organic porous framework material with adsorptive desulfurization performance and a preparation method thereof. According to the principles of the Knoevenagel reaction, an aldehyde compound and a cyano compound with active alpha-hydrogen atoms are subjected to a condensation reaction under a weakly alkaline condition, so a graphene-like organic porous framework material product in which reaction monomers are connected by carbon-carbon double bonds is finally obtained. The prepared material has a large-area conjugated structure unit, and due to the structural characteristic, the material has a more remarkable adsorption effect on aromatic thiophene sulfur compounds compared with alkane compounds.

Description

technical field [0001] The invention belongs to the field of preparation of organic porous framework materials, and in particular relates to an organic porous framework material with adsorption desulfurization performance and a preparation method thereof. Background technique [0002] Fossil fuels (gasoline, diesel, kerosene, etc.) provide important support for the rapid development of society and people's lives, but also cause inevitable damage to our surrounding environment. Sulfur-containing compounds in fuel oil, such as thiophene sulfur, sulfide, etc., are burned to produce sulfur dioxide, which will cause serious pollution to the environment. Therefore, the laws and regulations of various countries in the world have strict restrictions on the sulfur content in fuel oil. With the improvement of environmental protection requirements, it is imminent to produce high-clean hydrocarbon fuels with ultra-low sulfur content. At present, most of the desulfurization of fuel oil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/22B01J20/28B01J20/30C10G25/00
CPCB01J20/22B01J20/28011B01J20/2808B01J20/28061B01J20/3085B01J20/3071C10G25/003C10G2300/202
Inventor 马和平陈姝晖张文祥
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com