White tourmaline mineral compounded quick-heating warm-feeling textile and preparation method thereof

A technology of tourmaline and textiles, which is applied in the preparation of industrialized production of fast-heating and warming textiles, and in the field of fast-heating and warming textiles, which can solve problems such as limiting the application scenarios of mineral composite textiles, reducing the flexibility of textiles, and affecting wearing comfort. Enhance the far-infrared performance of minerals, good washing resistance, and reduce energy consumption

Pending Publication Date: 2021-12-21
YUYUE HOME TEXTILE +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, conventional mineral composite textiles, due to the addition of mineral components, will significantly reduce the flexibility of the textiles, affecting the comfort of wearing
Moreover, the firmness and color of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • White tourmaline mineral compounded quick-heating warm-feeling textile and preparation method thereof
  • White tourmaline mineral compounded quick-heating warm-feeling textile and preparation method thereof
  • White tourmaline mineral compounded quick-heating warm-feeling textile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0044] Example 1

[0045] A quick-heat warm-feeling textile composited with white tourmaline minerals, comprising the following steps:

[0046] (1) Preparation of aqueous slurry: Dissolve the auxiliary agent with 20 ml of deionized water, including 0.4 g of water-resistant dispersant CX003 and 0.03 g of AMP-95 conditioner. Then put 20g white tourmaline powder with a particle size of 10μm, 10g black tourmaline powder with a particle size of 10μm, 5g SiO 2 , 5g ZrO 2 Powder with a particle size of 30nm, and then stir evenly;

[0047] (2) Preparation of printing paste: add 60g of SHW adhesive and 100g of thickener to the printing paste in turn, and stir evenly;

[0048] (3) Printing and dyeing: The post-processing parameters of the pure fiber cloth are set as follows: the magnetic force is 5V and the speed is 22m / min. After printing and dyeing, it was dried in an oven at 80°C. After drying, carry out secondary printing and dyeing and then drying, and finally obtain white tou...

Example Embodiment

[0049] Example 2

[0050] A quick-heat warm-feeling textile composited with white tourmaline minerals, comprising the following steps:

[0051] (1) Preparation of aqueous slurry: Dissolve auxiliary agents with 30 ml of deionized water, including 0.4 g of water-resistant dispersant CX003 and 0.03 g of AMP-95 conditioner. Then put 20g white tourmaline powder with a particle size of 10μm, 10g black tourmaline powder with a particle size of 10μm, 5g SiO 2 , 5g ZrO 2 Powder with a particle size of 30nm, and then stir evenly;

[0052] (2) Preparation of printing paste: add 50g of SHW adhesive in the printing paste and 100g of thickener in the printing paste in turn, and stir evenly;

[0053] (3) Printing and dyeing: The post-processing parameters of the pure fiber cloth are set as follows: the magnetic force is 5V and the speed is 10m / min. After printing and dyeing, it was dried in an oven at 80°C. After drying, secondary printing and dyeing is carried out and then drying is pe...

Example Embodiment

[0054] Example 3

[0055] A quick-heat warm-feeling textile composited with white tourmaline minerals, comprising the following steps:

[0056] (1) Preparation of aqueous slurry: Dissolve auxiliary agents with 30 ml of deionized water, including 0.4 g of water-resistant dispersant CX003 and 0.03 g of AMP-95 conditioner. Then put 20g white tourmaline powder with a particle size of 10μm, 5g black tourmaline powder with a particle size of 10μm, 5g SiO 2 , 5g ZrO 2 Powder with a particle size of 30nm, and then stir evenly;

[0057] (2) Preparation of printing paste: add 50g of SHW adhesive and 100g of thickener to the printing paste in turn, and stir evenly;

[0058] (3) Printing and dyeing: The post-processing parameters of the pure fiber cloth are set as follows: the magnetic force is 5V and the speed is 22m / min. After printing and dyeing, it was dried in an oven at 80°C. After drying, secondary printing and dyeing is carried out and then drying is performed to finally obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thermal resistanceaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention generally relates to the technical field of functional textiles, in particular to a white tourmaline mineral compounded quick-heating warm-feeling textile and a preparation method of the industrially produced quick-heating warm-feeling textile. According to the white tourmaline mineral compounded quick-heating warm-feeling textile, white tourmaline and schorlite which can increase the surface temperature after absorbing light energy and have a far infrared ray emission function are used as main components, a metal oxide is used as an auxiliary agent, and a dispersing agent and a conditioning agent are added to prepare water-based slurry; then, an adhesive and a printing thickening agent are added for preparing printing paste; and finally, printing and dyeing are carried out, so that the textile is obtained. The whole preparation method is simple and suitable for large-scale industrial production and preparation, large-scale continuous production can be achieved, and the prepared white tourmaline mineral compounded quick-heating warm-feeling textile is white gray and can be directly converted into an actual commercial product by simply spraying patterns in the later period.

Description

technical field [0001] The present invention generally relates to the technical field of functional textiles, in particular to a quick-heating warm-sensing textile compounded with white tourmaline minerals, and a preparation method for industrially producing the quick-heating warm-sensing textile. Background technique [0002] With the development of society and the continuous improvement of people's quality of life, people's requirements for clothing are no longer shelter from the cold, nor is it just fashionable and beautiful. In addition to basic convenience (easy to wash, quick-drying, no fading, non-ironing, shrink-proof, etc.), comfort (soft fit, moisture absorption, skin-friendly and breathable), people's clothing health care (anti-ultraviolet, antibacterial, etc.) , antistatic, deodorant, insect-proof) also have requirements. [0003] Functional textiles refer to textiles that, in addition to their own basic use value, also have other additional special functions, s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06P1/52D06P1/673
CPCD06P1/67383D06P1/6735D06P1/5257Y02B30/00
Inventor 张以河张国清张磊田娜高路周博文高彩霞陈宇王兰心李兴娜文洪杰路明磊
Owner YUYUE HOME TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap