Antifriction coating formulation compositions
A technology of anti-friction coating and composition, which is applied in the field of anti-friction coating preparation composition, and can solve problems such as mixed metal sulfide anti-friction coating solid lubricants, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
example
[0035] Examples of Series I: abrasion resistance test
[0036] Example compositions are prepared using the raw materials shown in Table 1.
[0037] Table 1
[0038]
[0039]
[0040] CO x Mo (1-x) S 2 Preparation
[0041] The stoichiometric amount of ammonium sulfide [(NH2 4 ) 2 S] and ammonium heptamolybdate [(NH2 4 ) 2 Mo 7 O 24 -4H 2 O] were combined and stirred in an aqueous solution at 60 ℃ 1 hours (during which the solid was completely dissolved). At 60 deg.] C and the resulting aqueous solution with a stoichiometric quantity of cobalt acetate [Co (C 2 Hide 3 O 2 ) 2 ] Aqueous solution was added dropwise from the addition funnel to the common solution of acetic acid and allowed to stir for one hour. The resulting solid material {(NH 4 ) 4 [Co (MoS 4 ) 3 ]} Was filtered and dried at 80 ℃. The dried material was then placed in a nitrogen purged oven, ramped up to 500 ℃, and maintained for about one hour and the solid product was restored sulfide into the final. After heati...