Dry material anti-oxidation coating for continuous casting tundish
An anti-oxidation coating and continuous casting technology, applied in the field of refractory coating, can solve the problems affecting the safety performance of the tundish, reducing the strength of dry materials, loose structure, etc. Strong binding effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0048] Implementation case 1:
[0049] Temperature weighed glass powder 17 parts, 6 parts of sodium silicate solids, 34 parts of light burned magnesium powder, 1.3 parts of terpineol, 2.5 parts of ethyl cellulose, 3.2 parts of the aqueous epoxy resin, 4 parts of sodium metasilicate nonahydrate, 32 parts silicon carbide scrap, MoSi 2 30 parts of a powder, B 2 O 3 Powder 30 parts, SiO 2 Powder 25 parts, 50 parts of isopropanol, 30 parts of chloroplatinic acid powder, 45 parts of ethanol, 15 parts polycarbosilane solution, dilute ammonia solution and 18 parts of deionized water, 57 parts;
[0050] The MgO powder and an aqueous epoxy mix to be added into a planetary ball mill, and then into the reaction 80min vacuum oven and dried by heating in a feed-ball speed ratio 1︰1.5 vibration mill mixing, heating time to 25min, a heating temperature of 95 deg.] C, mixed powder, the mixed powder of particle size of 600 mesh, the medium-temperature glass frit, waste carbide, sodium metasilicate ...
Example Embodiment
[0052] Implementation Case 2:
[0053] Temperature weighed glass powder 18 parts, 5 parts of sodium silicate solids, 33 parts of light burned magnesium powder, 1 parts of terpineol, ethyl cellulose, 2 parts, 3 parts of the aqueous epoxy resin, 3 parts of sodium metasilicate nonahydrate, 35 parts silicon carbide scrap, MoSi 2 30 parts of a powder, B 2 O 3 Powder 30 parts, SiO 2 Powder 25 parts, 50 parts of isopropanol, 30 parts of chloroplatinic acid powder, 45 parts of ethanol, 15 parts polycarbosilane solution, 18 parts of dilute ammonia solution and 56 parts of deionized water;
[0054] The MgO powder and an aqueous epoxy mix to be added into a planetary ball mill, and then into the reaction 80min vacuum oven and dried by heating in a feed-ball speed ratio 1︰1.5 vibration mill mixing, heating time to 25min, a heating temperature of 95 deg.] C, mixed powder, the mixed powder of particle size of 600 mesh, the medium-temperature glass frit, waste carbide, sodium metasilicate nonahy...
Example Embodiment
[0056] Implementation Case 3:
[0057]Temperature weighed glass powder 16 parts, 8 parts of sodium silicate solids, 31 parts of light burned magnesium powder, 1.5 parts of terpineol, 3 parts of ethyl cellulose, 3 parts of the aqueous epoxy resin, 3.5 parts of sodium metasilicate nonahydrate, 34 parts silicon carbide scrap, MoSi 2 30 parts of a powder, B 2 O 3 Powder 30 parts, SiO 2 Powder 25 parts, 50 parts of isopropanol, 30 parts of chloroplatinic acid powder, 45 parts of ethanol, 15 parts polycarbosilane solution, dilute ammonia solution and 18 parts of deionized water, 58 parts;
[0058] The MgO powder and an aqueous epoxy mix to be added into a planetary ball mill, and then into the reaction 80min vacuum oven and dried by heating in a feed-ball speed ratio 1︰1.5 vibration mill mixing, heating time to 25min, a heating temperature of 95 deg.] C, mixed powder, the mixed powder of particle size of 600 mesh, the medium-temperature glass frit, waste carbide, sodium metasilicate non...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap