Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Lightweight plastering mortar and preparation method thereof

A plastering mortar, lightweight technology, applied in the field of construction engineering materials, can solve the problems of heavy weight, shedding, low bonding strength, etc., and achieve the effect of reducing wall load-bearing, improving water retention, and high bonding strength

Pending Publication Date: 2022-01-04
安徽亿捷环保科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing traditional cement mortar has disadvantages such as low bonding strength, high linear shrinkage, too much weight, and poor water retention. When used for leveling the base surface of walls and floors, hollowing, cracking, and falling off will occur. and other phenomena, which affect the construction quality and construction efficiency, and there are also potential safety hazards.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lightweight plastering mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with specific embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0033] In the description of the present invention, the terms "comprising", "having" and any variations thereof are intended to cover a non-exclusive inclusion, for example, a process, method, system, product or device comprising a series of steps or units is not necessarily limited to Those steps or units that have been explicitly listed, but may also include other steps or units that are not explicitly listed but inherent to these processes, methods, products or equipment, or are added based on the further optimization scheme of the present invention. steps or units.

[0034] Examples 1-3 all provide a light-weight ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Flexural strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses lightweight plastering mortar and a preparation method thereof. The lightweight plastering mortar is prepared from the following components in parts by mass: 68 to 72 parts of anhydrite, 10 to 15 parts of cement, 8 to 10 parts of stone powder, 8 to 12 parts of vitrified micro bubbles of 70 to 90 meshes, 0.5 to 1.5 parts of an accelerator, 0.17 to 0.25 part of a water-retaining agent and 0.03 to 0.08 part of a lubricant. The preparation method of the lightweight plastering mortar comprises the steps of S1, weighing the raw materials in parts by mass; and S2, sieving the anhydrite weighed in the step S1 with a 200-mesh sieve to obtain sieved anhydrite, crushing the stone powder, sieving with a 0.2 mm-sieve to obtain sieved stone powder, uniformly mixing the sieved anhydrite, the sieved stone powder and the other raw materials weighed in the step S1, stirring and mixing for 4-6 minutes, and then sub-packaging to obtain the lightweight plastering mortar. Compared with the traditional cement mortar, the lightweight plastering mortar disclosed by the invention has the advantages of higher strength, higher bonding strength, lower linear shrinkage rate, stronger water-retaining property and the like.

Description

technical field [0001] The invention relates to the field of building engineering materials, in particular to a lightweight plastering mortar and a preparation method thereof. Background technique [0002] With the rapid development of my country's construction industry and building materials industry, the demand for gypsum is increasing. At present, almost all plaster cementitious materials and products except chemical gypsum in my country are made of natural dihydrate gypsum, which has formed the basic system of my country's construction gypsum industry and has become an important part of my country's new building materials. The gypsum reserves in my country are very large, and the ore reserves of anhydrite deposits account for about 60%. [0003] Natural anhydrite is harder than natural dihydrate gypsum, but its hydration rate is slower, the setting time is longer, the chemical activity is poor, and the strength is low. For a long time, the research on anhydrite has pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/16C04B111/28C04B111/40
CPCC04B28/16C04B2111/40C04B2111/28C04B7/02C04B14/02C04B14/24C04B2103/46C04B2103/0068
Inventor 任开峰高禹博秦虎司腾飞
Owner 安徽亿捷环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products