Injection type facial filler composition gel for cosmetic and plastic surgery and preparation method of injection type facial filler composition gel

A filler and injection-type technology, applied in the medical field, can solve the problems of short product duration, bad operators, hidden safety hazards, etc., and achieve the effect of improving differentiation and proliferation ability, promoting hematopoietic function, and enhancing use effect.

Inactive Publication Date: 2022-01-18
珠海美如初医疗美容有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing products usually have a short product duration, need several months of re-injection, and are likely to cause postoperative redness and swelling, giving the operator a bad feeling, and there are relatively large safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An injectable facial filler composition gel for cosmetic plastic surgery, comprising the following components in corresponding parts by weight:

[0029] 10 parts of sodium hyaluronate, 90 parts of aqueous solution for injection, 2 parts of collagen powder, 5 parts of modified particles, 0.1 part of extractant, and 0.4 part of multivitamin.

[0030] The aqueous solution for injection is a sodium chloride solution with a mass concentration of 0.9%.

[0031] The preparation method of modified particle comprises the following steps:

[0032] (1) first soak the apatite with citric acid solution, then filter out and rinse with deionized water for 3 times for later use; the mass concentration of the citric acid solution is 0.5%;

[0033] (2) Immerse the apatite treated in step (1) into the silane coupling agent solution, filter out after soaking for 10 minutes for subsequent use; the volume concentration of the silane coupling agent solution is 5%;

[0034] (3) Corona treatm...

Embodiment 2

[0042] An injectable facial filler composition gel for cosmetic plastic surgery, comprising the following components in corresponding parts by weight:

[0043] 15 parts of sodium hyaluronate, 95 parts of aqueous solution for injection, 4 parts of collagen powder, 7 parts of modified particles, 0.15 parts of extractant, and 0.6 parts of multivitamins.

[0044] The aqueous solution for injection is a sodium chloride solution with a mass concentration of 0.9%.

[0045] The preparation method of modified particle comprises the following steps:

[0046] (1) first soak the apatite with citric acid solution, then filter out and rinse with deionized water 4 times for later use; the mass concentration of the citric acid solution is 0.6%;

[0047] (2) Immerse the apatite treated in step (1) into the silane coupling agent solution, filter out after soaking for 13 minutes; the volume concentration of the silane coupling agent solution is 6%;

[0048] (3) Corona treatment is performed on...

Embodiment 3

[0056] An injectable facial filler composition gel for cosmetic plastic surgery, comprising the following components in corresponding parts by weight:

[0057] 20 parts of sodium hyaluronate, 100 parts of aqueous solution for injection, 5 parts of collagen powder, 8 parts of modified microparticles, 0.2 parts of extractant, and 0.7 parts of multivitamins.

[0058] The aqueous solution for injection is a sodium chloride solution with a mass concentration of 0.9%.

[0059] The preparation method of modified particle comprises the following steps:

[0060] (1) Soak the apatite with citric acid solution, then filter out and rinse with deionized water 5 times for later use; the mass concentration of citric acid solution is 0.7%;

[0061] (2) Immerse the apatite treated in step (1) into the silane coupling agent solution, filter out after soaking for 15 minutes for subsequent use; the volume concentration of the silane coupling agent solution is 7%;

[0062] (3) Corona treatment is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an injection type facial filler composition gel for cosmetic and plastic surgery, and belongs to the technical field of medical treatment. The injection type facial filler composition gel is prepared from the following components in parts by weight: 10-20 parts of sodium hyaluronate, 90-100 parts of an aqueous solution for injection, 2-5 parts of collagen powder, 5-8 parts of modified particles, 0.1-0.2 part of an extraction agent, and 0.4-0.7 part of multivitamins. The injection type facial filler composition gel is safe to use, the problems of redness, swelling, vascular embolism and the like are solved, and the treated skin is attractive and natural.

Description

technical field [0001] The invention belongs to the field of medical technology, and in particular relates to an injection-type facial filler composition gel for cosmetic plastic surgery and a preparation method thereof. Background technique [0002] Skin naturally loosens and wrinkles over time, especially facial contour aging, including visible skin lines, deep nasolabial folds, frown lines, marionette lines, buccal seam lines, mouth circumference wrinkles, temporal Collapse etc. Similarly, the collapse of the bridge of the nose due to congenital or trauma, as well as improper browbones and chins, etc. have brought troubles and pains to people. Beauty is an eternal topic and goal pursued by human beings. How to effectively delay skin aging and beautify the appearance is still a problem that people continue to explore and solve. [0003] Injection cosmetology is a kind of non-surgical plastic surgery. Biomaterials or artificially synthesized biocompatible materials are in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/12A61L27/20A61L27/24A61L27/36A61L27/52A61L27/54A61L27/60
CPCA61L27/60A61L27/20A61L27/24A61L27/54A61L27/52A61L27/12A61L27/3604A61L2300/112A61L2400/06A61L2300/30
Inventor 余明张成山
Owner 珠海美如初医疗美容有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com