Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A color tile paint and raw material technology, applied in the direction of coating, anti-corrosion coating, etc., can solve the problems of product surface foaming, peeling, rust, etc., achieve good film-forming, high self-lubrication, good heat resistance and dispersive effect
Pending Publication Date: 2022-04-29
蔚湃建筑科技(上海)有限公司
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] However, users found that since the tiles are mostly used in the open air and are often used in hot and humid environments, after a period of time, the surface of the product will appear blistering, rust, peeling or discoloration
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0036] Caiwa paint includes the following raw materials: 15kg of titanium dioxide, 0.3kg of dioctyl sodium sulfosuccinate, 10kg of precipitated barium sulfate, 0.2kg of nonylphenol polyoxyethylene ether, 0.15kg of silane coupling agent KH560, multifunctional auxiliary Agent 0.1kg, silicone defoamer 0.1kg, fumed silica 0.8kg, butyl ether 0.3kg, leveling agent 0.2kg, ferrocene 2kg, performance modifier including alcohol ester twelve 2.5kg, acrylic emulsion 50kg, 0.5kg of polytetrafluoroethylene micropowder and 3kg of zinc phosphate, the thickener includes 1.5kg of pyrophyllite powder, 0.2kg of calcium chloride and 0.5kg of sodium silicate.
Embodiment 2
[0038] Caiwa paint includes the following raw materials: 23kg of titanium dioxide, 0.6kg of sodium dioctyl sulfosuccinate, 6kg of precipitated barium sulfate, 0.3kg of nonylphenol polyoxyethylene ether, 0.35kg of silane coupling agent KH560, multifunctional auxiliary Agent 0.2kg, silicone defoamer 0.3kg, fumed silica 0.4kg, butyl ether 0.7kg, leveling agent 0.2kg, ferrocene 4kg, performance modifier including alcohol ester twelve 2.5kg, acrylic emulsion 50kg, 0.5kg of polytetrafluoroethylene micropowder and 3kg of zinc phosphate, the thickener includes 1.5kg of pyrophyllite powder, 0.2kg of calcium chloride and 0.5kg of sodium silicate.
Embodiment 3
[0040] Caiwa paint includes the following raw materials: 17.5kg of titanium dioxide, 0.4kg of dioctyl sodium sulfosuccinate, 7.5kg of precipitated barium sulfate, 0.5kg of nonylphenol polyoxyethylene ether, 0.3kg of silane coupling agent KH560, and more Functional additive 0.2kg, organosilicon defoamer 0.2kg, fumed silica 0.5kg, butyl ether 0.4kg, leveling agent 0.3kg, ferrocene 2.8kg, performance modifier including alcohol ester twelve 2.5kg, acrylic acid Emulsion 50kg, polytetrafluoroethylene micropowder 0.5kg and zinc phosphate 3kg, thickener includes pyrophyllite powder 1.5kg, calcium chloride 0.2kg and sodium silicate 0.5kg.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the field of encaustic tile paint, and particularly discloses encaustic tile paint which is prepared from the following raw materials: titanium dioxide, sodium dioctyl sulfosuccinate, precipitated barium sulfate, a wetting agent, a silane coupling agent, a multifunctional additive, a defoaming agent, fumed silica, a thickening agent, butyl ether, a flatting agent and a performance regulator. The performance regulator comprises texanol, acrylic emulsion, polytetrafluoroethylene micro powder and zinc phosphate, and the thickening agent comprises pyrophyllite powder, calcium chloride and sodium silicate. The construction method of the encaustic tile paint comprises the following steps: step 1, cleaning impurities such as floating rust, foreign matters, oil stains and dust on the surface of a base material, and preheating the base material to 45-55 DEG C for later use; and step 2, diluting the prepared encaustic tile paint with water, adjusting the viscosity to 20-30s, filtering with 80-150-mesh filter gauze, and then carrying out construction. The encaustic tile paint prepared by the invention has excellent heat and humidity resistance and good product quality.
Description
technical field [0001] The application relates to the field of colored tile paint, more specifically, it relates to a kind of colored tile paint and a construction method. Background technique [0002] Color tile paint is a single-component quick-drying material composed of high-grade acrylic resin, silicone resin, pigments, additives and solvents, which is used for concrete products such as cement color tiles and cement asbestos tiles. [0003] For example, the Chinese patent with the publication number CN104231809A discloses a color tile paint and a preparation method thereof. The color tile paint includes acrylic resin: 20-30 parts; a mixture of toluene and butyl ester: 40-50 parts; lauryl alcohol ester: 25 parts -30 parts; preservative: 1-2 parts; wetting agent: 1-2 parts; thickener: 2-4 parts; methylcellulose: 1-3 parts; dispersant: 3-5 parts; talcum powder : 25-30 servings. Through the good compatibility of each component, the color tile paint and the tile have good ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).