Wear-resistant anti-skid metal floor material

Abstract

The invention discloses a wear-resistant anti-skid metal floor material which comprises the following components in percentage by weight: 35-45% of slag, 30-40% of epoxy resin, 15-25% of nitrile rubber, 5-10% of magnesium fluosilicate solution, 3-6% of silicon dioxide sol and 1-2% of coupling agent, and is prepared by the following steps: firstly, putting 35-45% of slag, 30-40% of epoxy resin and 15-25% of nitrile rubber into a reaction kettle and uniformly stirring; raising the temperature of the reaction kettle to 80 DEG C, adding 5-10% of a magnesium fluosilicate solution, 3-6% of silicon dioxide sol and 1-2% of a coupling agent, stirring for 1 hour, and cooling to room temperature to obtain the wear-resistant and anti-slip metal floor material. The material has the advantages that the slag and the silicon dioxide sol have high skid resistance, wear resistance and strength, and the epoxy resin and the nitrile rubber are used, so that the material has the advantages of tensile strength, skid resistance, attractive appearance, chemical corrosion resistance and the like.

Description

technical field [0001] The invention relates to a wear-resistant and anti-slip metal floor material. Background technique [0002] Floor materials are widely used in workshops, stadiums and other places. At present, corundum floor materials use emery in the floor, which cannot strengthen the strength of the floor well, and the wear resistance and tensile properties are not enough to meet the requirements Various collisions affect the stability and appearance of the floor. At the same time, silica fume is used as an impurity in the emery wear-resistant floor. The shrinkage and water absorption of the floor are large, and the durability of the floor has problems. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a wear-resistant and non-slip metal floor material. [0004] In order to solve the above technical problems, the technical solution of the present invention is: a wear-resistant and non-slip metal floor mate...

AI Technical Summary

Problems solved by technology

[0002] Floor materials are widely used in workshops, stadiums and other places. At present, corundum floor materials use emery in the floor, which cannot strengthen the strength of the floor well, and the wear resistance and tensile properties are not enough to meet the requirements Various collisions affect the stability and appearance of the floor. At the same time, silica fume is used as an impurity in the emery wear-resistant floor. The shrinkage and water absorption of the floor are large, and the durability of the floor is problematic.