Jute (red jute) and wool blended dress face fabric and preparation process

A wool blending and wool technology, applied in textiles, textiles, papermaking, fabrics, etc., can solve the problems of not finding clothing fabrics, failing to meet the technical requirements of fabrics, and achieving the effect of rich hand feeling, good elasticity and guaranteed shrinkage rate

Inactive Publication Date: 2005-10-26
高占奎
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the domestic existing technology modifies jute and kenaf to improve its textile value. Although the spinning count has been improved, it still cannot meet the technical requirements for making fabrics, so it has not been found to use jute and kenaf with wool and chemical fiber , silk blended clothing fabrics and the corresponding preparation technology disclosure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0093] Embodiment 1: hemp wool fabric

[0094] 1. Raw material preparation

[0095] Bleaching and dyeing process of jute and kenaf:

[0096] Reactive dyes and dyeing processes are used for light colors, and sulfur dyes and dyeing processes are used for dark colors.

[0097] Jute and kenaf need to be modified before dyeing.

[0098] Wool bleaching and dyeing process: use weak acid dyes and dyeing process.

[0099] Chemical fiber dyeing process: nylon, raw white

[0100] 2. Spinning process

[0101] 1. Spinning specifications

[0102] Warp 14 counts 42(twist) / Z(twist) 15% hemp content Original white

[0103] Weft 12 counts 38 / Z 20% mixed colors

[0104] 2. Spinning materials

[0105] Warp Jute Kenaf 15% Raw White

[0106] 64 count carbonized wool 80% virgin white

[0107] Nylon 5% virgin white

[0108] Weft Jute Kenaf 20% Brown Coffee + Raw White

[0109] 64 counts of carbonized wool + hair grains 76% brown coffee + original white + various color gr...

Embodiment 2

[0167] Embodiment 2: hemp wool silk fabric

[0168] 1. Spinning process

[0169] 1. Spinning specification:

[0170] Warp 18 counts twist 50 / twist Z 25% hemp content shallow rice

[0171] Weft yarn 18 counts 50 / Z 25% hemp content light rice

[0172] 2. Spinning materials:

[0173] Warp and weft jute kenaf 25% light rice + original white

[0174]64 wool 60% light rice + original white

[0175] Silk 15% virgin white

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a jute (red jute) and wool blended apparel shell fabric and its preparation process. The shell fabric is made up by using modified jute (red jute), wool, chemical fibre and natural fibre of silk as raw material through the process of blended spinning. The product has the advantages of comfortable handling and loftiness, good elasticity, crispy permeability and micro-organism resistance, etc.

Description

technical field [0001] The invention relates to the field of textiles, in particular to a blended apparel fabric made of jute and kenaf as the main textile raw material, blended with wool and other fibers and a preparation process for the fabric. Background technique [0002] Hemp fiber is the earliest textile raw material used by humans. It is due to its excellent properties of moisture absorption, breathability, coolness, antibacterial and insect resistance, but it also has certain weaknesses: such as stiff and rough hand feeling, difficult to spin, difficult to dye, poor elasticity recovery, Easy to wrinkle, shrink, etc. The weakness of jute and kenaf fiber in this aspect is even more prominent. Because it has the highest lignin content, the fiber is short and thick, the hand feels rough, and the textile value is extremely low. It can only be used to make packaging materials, such as sacks, burlap, and hemp rope. Wait. At present, the domesti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/04D03D15/00
Inventor 才树真高占奎陈谦丛培生
Owner 高占奎
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com